This study is mainly concerned with the friction and wear properties for the specimens of crank shaft which are made of ductile cast iron. The friction and wear tests were carried out for the nor-malized ductile cast iron specimens and their properties were compared with each other at reheat-ing temperatures(550^{\circC,\; 600^{\circ}C,\; 650^{\circ}$) and in dry condition at different friction velocity(0.94 m/s 1.88m/s 2.83m/s) range. After austenized at $910^{\circ}C$ it is observed that the higher the reheating temperature is the hardness becomes decrease which is supposedly attributed to the fact that the amount of pearlite austenite matrix is rduced by reheating after normalizing and that as the reheating temperature goes up the pearlite generated is less and the interval between the pearlites were widened at last to make pearlite globular. At the low velocity the friction coefficient increase in the beginning and gets stabilized as the sliding distance increases. As the friction velocity grows the friction coefficient decreases suppos-edly since the abrasive wear is heavier at low velocity than at the high velocity as the friction tem-perature at low velocity is lower than at high velocity.

• 열처리공학회지
• /
• 제30권2호
• /
• pp.43-52
• /
• 2017

Heat treatment condition for dissolution of the M23C6 carbides in 2.25Cr-1Mo-V-Ti material for thermal power plant tube was investigated using a dilatometer method. 2.25Cr-1Mo-V-Ti material was heat-treated at $900{\sim}1,100^{\circ}C$ for 0, 10, 30 min to find the proper dissolution condition of M23C6 carbides. The phase identification and volume fraction of the carbide were measured by using OM, SEM, EBSD and TEM analysis. Optimal heat treatment condition of M23C6 carbide dissolution was selected by predicting dissolution temperature of carbide using Bs points appeared at dilatometer curve. Experimental results showed that the conditions of carbide dissolution was 900, 1,000, $1,100^{\circ}C$ for 30 min. Eventually, the optimal heat treatment condition for dissolution was 30 min at $1,000^{\circ}C$ considering the minimum coarsening of Austenite grain size.

• Journal of Advanced Marine Engineering and Technology
• /
• 제23권3호
• /
• pp.284-291
• /
• 1999

Recently the ductile cast iron is being used successfully to the parts for processing machinery vessels and gear etc. This study is mainly concerned with the heat treatment for the specimens of crank shaft which are made of ductile cast iron. The results obtained are summarized as follows. Comparing the mechanical properties of the specimens for the normalized ductile cast irons the specimen heat treated at $550^{\circ}C$ was the best for crank shaft of air-compressor. After austenizing at $910^{\circ}C$ it was observed that the higher the reheating temperature is the less tensile strength and the hardness became which was supposedly attributed to the fact that the amount of pearlite. Austenite matrix was reduced by reheating after normalizing and that as the reheating tem-perature went up the pearlite generated was less and the distance between the pearlites were widened at last made pearlite globular. In the comparsison of crank shaft for air compressor made of ductile cast iron with that made by forged steel the crank shaft made of ductile cast iron was superior in economical terms. And ductile cast iron could be practically enough if only the elonga-tion which was inferior mechanical property to forged steel could be reinforced by increasing the diameter of crank pin when designing the crank shaft.

• 대한기계학회논문집
• /
• 제13권2호
• /
• pp.307-315
• /
• 1989

본 연구에서는 단조과정을 거친후 노멀라이징(normalizing) 처리된 SF45A강종과 압연후 자연 냉각시킨 SM41B강종의 두 국산 강종에 대해 저사이클 피로시험을 행하여 저사이클 피로특성을 밝히고, 강재의 가공공정과 부하변형율변화에 따른 피로과정중의 연화 및 경화 거동을 관찰하였다. 그리고 저사이클 피로파면의 미시적 고찰을 통해서 부하변형율 크기에 따른 미시적 파면 양상의 변화를 밝혀 파괴 해석의 기초자료로 제공하였다.