• Proceedings of the KAIS Fall Conference
• /
• 2007.11a
• /
• pp.337-340
• /
• 2007

냉간단조금형(Cold Forging Die)의 다이블록(Dieblock)을 제작하는 방법 중의 하나로, 다이블록 제작용 재료를 면가공 하여 다이블록 상면(上面)을 마스터펀치(Master Punch)인 호브(Hob)로 압입(Indentaion) 시켜 절삭가공((Cutting Work)이 아닌 다이호빙(Die Hobbing) 방법으로 임프레션(Impression)을 성형하여 제작하고 있다. 이 방법에 의하여 다이블록의 재료를 합금공구강(Alloy Tool Steel)인 SKD11을 사용하여 제작하고, 스테인리스판(Stainless Sheet Metal)을 제품 재료로 하여 냉간단조가공(Cold Forging Work)을 하였더니 6,000 스트로크(Stroke)에서 금형수명(Die Life)을 다 하였다. 본 논문에서는 다이블록 재료를 고속도공구강(High Speed Tool Steel)인 SKH51로 교체 제작하고, 탄소강(Carbon Steel)인 S45C를 제품 재료로 하여 냉간단조가공을 수행 하였더니 21,000 스트로크에서 금형수명을 다하고 종료 되어 종래의 방법과 비교 검토 하였을 때 350%의 금형수명 연장 효과를 얻게 되었다.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.9 no.2
• /
• pp.281-285
• /
• 2008

Die hobbing is one of the dieblock manufacturing methods of cold forging die, which makes the upper side of dieblock indented using master punch, hobb to produce impression not using cutting work. SKD11, alloy tool steel was used as the material of dieblock and stainless sheet metal was used as product material in cold forging work. The life span of the die was 6,000 strokes. In this research, the material of dieblock was changed into SKH51, the high speed tool steel and the product material was S45C, the carbon steel in the cold forging work. The life span of the die was 21,000 strokes, which is 350% of the life span of the die using the former method.

• Applied Microscopy
• /
• v.7 no.1
• /
• pp.45-49
• /
• 1977

For obtaining high manganese steel plates, the study has been made on the optimum conditions in melting, forging, rolling and water toughning treatment practices. The optimum water toughning temperature and time was found to be $1030^{\circ}C$ and 30 min. respectively for the plates of 1 mm thickness. The argon atmosphere is very effective for the prevention of decarburization which can be easily occured in open air. There is a close relation between the degree of c 이 d working and the hardess. The greater the cold reduction ratio is, the smaller the grain size is and it results in the increase of hardness. The improvement of tensile and bending properties can be made by the addition of small amount of nickel, chromium and vanadium.