• Journal of the Korea Concrete Institute
• /
• v.16 no.6 s.84
• /
• pp.751-757
• /
• 2004

Artificial lightweight aggregates and solids were manufactured with coal ash(fly ash, bottom ash). In order to apply alkali-activated coal ash(fly ash, bottom ash) artificial lightweight aggregate to concrete, several experimental studies were performed. Thus, it can be noticed the optimal mix proportion, basic characteristies, mechanical properties and environmental safety of alkali-activated coal ash(fly ash, bottom ash) solid and alkali-activated coal ash(fly ash, bottom ash) artificial lightweight aggregate. Also, the freezing-thawing test property of concrete using the alkali-activated coal ash(fly ash, bottom ash) artificial lightweight aggregate was investigated. As a result, the optimal mixing proportion of coal ash(fly ash, bottom ash) solid to make alkali-activated artificial lightweight aggregates was cement $10\%$, water glass $15\%$, NaOH $10\%$, $MnO_2\;5\%$. Alkali-activated coal ash(fly ash, bottom ash) solid can achieve compressive strength of 36.4 MPa, at 7-days, after the paste was cured at air curing after moist curing during 24 hours in $50^{\circ}C$. Alkali-activated coal ash(fly ash, bottom ash) artificial lightweight aggregate that do impregnation to polymer was improved $10\%$ crushing strength $150\%$, and was available to concrete.

• Journal of the Korea Concrete Institute
• /
• v.28 no.2
• /
• pp.197-204
• /
• 2016

Concrete walls of neutron generating facilities such as fusion reactors and fission reactors become radioactive by neutron irradiation. Both low-activation and neutron shielding are a critical concern at the dismantling stage after the shutdown of facilities with a requirement of radioactive waste management. To tackle this, two types of additives were investigated in fabricating mortar specimens: synthetic high polymers and boron carbide. It is well known that a hydrogen atom is effective in neutron shielding by an elastic scattering because its mass is almost the same as that of the neutron. And boron is an effective neutron absorber with a big neutron absorption cross section. In this study, the effect of the type, shape, and size of polymers were investigated as well as that of boron carbide. Total 16 mix designs were prepared to reveal the effect of polymers on mechanical properties and neutron shielding performance. The neutron does equivalent of polymers-based mortar for fast neutrons decreased by 36 %, and the count rate of boron carbide-based mortar with regard to thermal neutrons decreased by 90 % compared to conventional mortar. These results showed that a combination of polymers and boron carbide compounds has potential to reduce the thickness of neutron shields as well as radioactive waste from reactors.

• Journal of the Korea Concrete Institute
• /
• v.25 no.6
• /
• pp.657-665
• /
• 2013

The purpose of this study is the basic research of self-compacting concrete using Alkali-Activated Slag (AAS) binder in order to emphasize the durability of structures and facilitate casting the fresh concrete in field. The AAS binder emitted low carbon dioxide ($CO_2$) is eco friendly material of new concept because AAS products not only emit little $CO_2$ during production but also reuse the industrial by-products such as ground granulated blast-furnace slag (GGBS) of the steel mill. Until now, almost of domestic and foreign research are using Ordinary Portland Cement (OPC) for self-compacting concrete, and also, nonexistent research about AAS. The self-compacting concrete must get the performance of flowability, segregation resistance, filling and passing ability. Nine concrete mixes were prepared with the main parameter of unit amount of binder (400, 500, 600 $kg/m^3$) and 3 types of water-binder (W/B) ratio. The results of test were that fresh concretes were satisfied with flowability, segregation resistance, and filling ability of JSCE. But the passing ability was not meet the criteria of EFNARC because of higher viscosity of AAS paste than OPC. This high viscosity of AAS paste enables the manufacturing of self compacting concrete, segregation of which does not occur without the using of viscosity agent. It is necessary that the development of high fluidity AAS binders of higher strength and the study of better passing ability of AAS concrete mixes in order to use self compacting AAS concrete in field.

• Korean Journal of Food Science and Technology
• /
• v.29 no.5
• /
• pp.963-968
• /
• 1997

Cereals and legumes were ground, blended and extruded with a twin-screw extruder to form a reconstituted grain. The basic formula was as follows: brown rice 30%, barley 30%, wheat 20%, millet 5%, sorghum 5%, soybean 7%, and red bean 3%. Extrusion conditions were properly set for feed moisture content of $24{\sim}30%$, barrel temperature of $50{\sim}60^{\circ}C$, and screw speed at 250 rpm. The extruded grain was air-dried and evaluated for quality characteristics, compared with milled rice. Size and shape of the reconstituted grain were similar to short-grain milled rice. Stacking volume of the reconstituted grain was a little higher than that of milled rice, and its water absorption was more rapid. From the texture measurements, hardness of cooked reconstituted grain was slightly lower and adhesiveness was appeared to be higher.

• Korean Journal of Food Science and Technology
• /
• v.41 no.4
• /
• pp.417-422
• /
• 2009

The purpose of this study was to measure the changes in S-adenosyl-L-methionine (SAM) content and to find the best condition for SAM Kimchi during fermentation with the different kinds of raw materials of Kimchi and the diverse ways of making Kimchi. As fermentation was processing, pH of all Kimchi groups dramatically decreases at the beginning stage of experimentation. However, pH value was 4.2-4.3 in the last stage. Titratable acidity tends toward the similar results in pH value. At the first, the SAM content went down time substantially and then increases. Kimchi (A), which was made of the most basic raw materials, resulted in the lowest content of SAM. The most abundant SAM content of Kimchi was the Kimchi made with certain materials. Kimchi (I) had the most has SAM content, overall. The best time of fermentation was when pH was between 4.3 and 5.3, and titratable acidity was 0.5-1.0%. As the results of this study, the highest SAM content in Kimchi could be made when Kimchi was fermented for 9-12 days and titratable acidity showed 0.5-1.0% This study proved that the ratio of raw materials such as red pepper, fermented fished sauces, and other materials improved the levels of SAM in the Kimchi.

• Journal of the Korea Institute of Building Construction
• /
• v.14 no.5
• /
• pp.389-396
• /
• 2014

The set accelerator used for shotcrete at high pH environment often causes the dusting problem in practice. In this research, a slurry-type set accelerator was developed to avoid this problem and its effectiveness was investigated by applying it to shotcrete mortars. Set time, stiffening, compressive strength, and chloride ion penetration resistance were examined with different amounts of slag, used as partial replacement of cement. According to the experimental results, it was found that the earlier responses such as set time, stiffening, and 1-day compressive strength were probably affected by the amount of ettringite, formulated by the hydration between C12A7 and calcium sulfate polymorphs present in blast furnace slag. Whereas, it is believed that the result of compressive strength after 3 days was attributed to the hydration of tricalcium silicates. As for the results of a chloride ion penetration test, the partial replacement of cement with slag significantly reduced the total charge passed through the shotcrete mortar.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.10 no.4
• /
• pp.428-434
• /
• 2022

This study intends to develop an eco-friendly concrete panel mixed with biochars. Experiments about mechanical and thermal properties were conducted on porous biochar concrete, which has insulation and carbon-capture performance. The concrete has a mixing ratio of 0, 5, 10, and 15 % for biochar and a water-binder ratio of 0.35. The unit weight, porosity, and permeability were measured to evaluate the mechanical characteristics. From the results, as the biochar mixing rate increased, the porosity and the permeability increased, but the unit weight decreased. Even though a decreased trend was observed in the compressive strength results, they satisfied the design standard. Since the thermal conductivity was decreased during the increase of contents, biochar could be considered an excellent material for insulation performance. In addition, regression analyses were conducted regarding the relationship of unit weight with porosity, compressive strength with thermal conductivity, and porous with thermal conductivity. From the regression, significant variables for expanding the scope of the application of biochar were presented.

• Food Science and Preservation
• /
• v.30 no.5
• /
• pp.896-904
• /
• 2023

The texturization characteristics of textured vegetable protein (TVP) were investigated based on the extent of soybean decoating during the pretreatment of defatted soybean flour used for TVP. The raw materials for TVP consisted of 50% defatted soybean flour, 30% gluten, and 20% corn starch. The weight ratios of soybean seed coat to soybean flour were 9%, 6%, 3%, and zero. Extrusion was performed using an extruder equipped with a cooling die, maintaining a barrel temperature of 190℃ and screw speed of 250 rpm, Water was injected at a rate of 9 rpm using a metering pump. Regarding the textures of the extruded TVPs produced from defatted soybean flour, an increase in the soybean seed coat content led to a decrease in the apparent fibrous structural layer and an increase in hardness. However, there were no significant changes in elasticity and cohesion. Moreover, as the soybean seed coat content increased, the pH of TVPs decreased. A higher soybean seed coat content also tended to lower the moisture content, increasing water absorption, solids elution, and turbidity. These results suggest that an increased seed coat content reduces the proportion of protein, and the fibers present in the seed coats prevent texturization.

• Journal of Korean Society of Forest Science
• /
• v.74 no.1
• /
• pp.56-60
• /
• 1986

Excised mature embryos of P. koraiensis were plated on a series of G.D. basic media supplemented with growth regulators as follow; $0.1mg/{\ell}$ NAA(M-1); $0.1mg/{\ell}$ NAA and 2,4-D (M-2); $0.1mg/{\ell}$ 2,4-D and BAP (M-3); $0.1mg/{\ell}$ 2,4-D and kinetin (M-4). Cytological study of the callus showed that thercentage of occurrance of diploid cells was observed 52% in M-3 and 36% in M-4, while that was revealed 29% in M-1 and 17% in M-1. The frequency of diploid cells was increased on the M-3 and M-4 media. The stable chromosome state is a crucial factor for organogenesis. Therefore, it can be inferred that the callus tissues cultured on media supplemented with both auxin and cytokinin have the greatest possibility of organogenesis.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.14 no.4
• /
• pp.783-794
• /
• 1994

Recently, several failure cases of concrete structures during construction have been reported. The main reason for these failures is attributed to the poor quality of concrete during construction. It is, therefore. necessary to develop and use high quality concrete. The purpose of the present study is to explore the characteristics of superplasticized concrete, especially the effects of mineral admixtures on the fluidity and strength characteristics of high performance concrete. The mineral admixtures considered in the present study are fly ash, blast furnace slag and silica fume, respectively. The major test variables include the amount of these mineral admixtures, cement contents and water-cement ratios. The compressive strengths for various cases were measured and reported. Optimum contents of mineral admixtures for strength development were derived. The corrosion phenomena of reinforcements embedded in various concrete specimens have been also studied. The present study provides useful basis to apply high-performance concrete to actual structures.