• Journal of Welding and Joining
• /
• v.29 no.5
• /
• pp.47-53
• /
• 2011

• Journal of Convergence for Information Technology
• /
• v.9 no.7
• /
• pp.94-99
• /
• 2019

Friction stir welding was first reported by TWI(The Welding Institute) in 1991, and this welding method has been rapidly used in various industrial areas such railway, automobile, aerospace and shipbuilding industry. Here, we study core characteristics of friction stir welding (FSW) applied to Al 6005-T6 extruded sheets, which is the typical alloy used for railway car bodies. With the fixed welding speed of 500 mm/min, the rotating tool speed was varied from 600 to 1800 RPM. The results of hardness measurement revealed that the hardness of nugget area is ~70% with respect to the parent material, and for the selected range of rotation speed, no clear dependence was observed and the hardness values close to the parent materials were achieved for the area located 5 mm away from the welding interface. The tension test shows that yield strength and tensile strength were slightly decreased with increasing RPM, with no observed difference for the elongation.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.33 no.7
• /
• pp.693-699
• /
• 2009

This paper shows mechanical properties and behaviors of macro- and micro-structures on friction stir welded specimen with 6061-T6 aluminum alloy plate. It apparently results in defect-free weld zone jointed at welding conditions like the traverse speed of 267mm/min, tool rotation speed of 2500rpm, pin inserted depth of 4.5mm and tilting angle of $2^{\circ}$ with tool dimensions such as tool pin diameter of 5mm, shoulder diameter of 15mm and pin length of 4.5mm. The tensile stress ${\sigma}_T=228MPa$ and the yield point ${\sigma}Y=141MPa$ are obtained at the condition of traverse speed of 267mm/min and tool rotation speed of 2500rpm. With the constant rotation speed, the higher traverse speed become, the higher tensile stress and yielding point become. Vickers hardness for welding zone profile were also presented.

• The KSFM Journal of Fluid Machinery
• /
• v.16 no.1
• /
• pp.47-55
• /
• 2013

In the present study, a numerical simulation to analyze mixing performance inside an industrial mixer was investigated for various geometry of turbine impellers. Various pitching angles and various types of turbine blades were considered in the simulation. In order to model the rotation of impeller, the Multiple Reference Frames (MRF) technique was used. For evaluation of the effect of various shapes on the mixing performance, dimensionless coefficient such as flow coefficient, circulation coefficient, power coefficient, pumping effectiveness and circulation effectiveness were used. From the results, the effect of pitching angle of a pitched turbine impeller was to give best pumping effectiveness around $30^{\circ}$ pitching angle, whereas best circulation effectiveness around $65^{\circ}$ pitching angle. Dual pitched turbine impeller showed best performance in both pumping effectiveness and circulation effectiveness among impeller types considered in the present study.

• Journal of the Korean Society for Railway
• /
• v.12 no.4
• /
• pp.512-517
• /
• 2009

Extruded aluminium panels have been widely used for railway vehicle structures because -of their light specific weight and other merits. In the past, GMAW (Gas Metal Arc Welding) and GTAW (Gas Tungsten Arc Welding) were mainly used to join aluminium panels. But recently friction stir welding (FSW) is widely used due to its lots of advantage. In this study aluminium A6005 which is used for car body structures was chosen. The influences of main parameters on mechanical properties such as: pin (tool) rotating speed, pin transition speed, shoulder, diameter, pin length and tilting angle were examined. Optical microscope and scanning electron microscope (SEM) observation, micro hardness tests, and tensile tests were carried out.

• Korean Journal of Materials Research
• /
• v.3 no.5
• /
• pp.529-537
• /
• 1993

The mecllanical properties of AI/TiCp composite fabrication by liquid mixing was investigat ed. The composites, containing 10 wt% Tic. were producwi using induction furnace with mechanical stirring. The amounts of' 1.5wt% Mg were, added to wetting agents. Thr presence of aluminum in TiC composites showed rnhanced strengrh without loss of ductility at room and clrvated temperatures. Espe cially, wear resistance was found to dramatically irnprovc. I3ul excess stirring d~terrninrd the mect~ani~ cal properties. Approximate values at present work were 500 rpm. There was no inrerfacial reaction of any kind and the interface remains clearly deineated.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.31 no.4
• /
• pp.532-539
• /
• 2007

The 7075-T651 Al alloy was welded by friction stir welding. Microstructure, macro behaviors and fracture type in the nugget, thermo-mechanically affected zone(TMAZ) and heat affected zone(HAZ) of the welded part were compared to base metal. The microsturctures of nugget zone were compared with tool rotation speeds and various tool transition speed. When the rotation speeds were decreased and transition speeds were increased, the hardness of nugget zone were decreased. Also, the optimal microstructure was observed at the low rotation speed of 800rpm and the high transition speed of 124mm/min. The transgranular dimple and quasi-cleavage at fractured part of nugget zone were investigated.

• Journal of the Korea Organic Resources Recycling Association
• /
• v.3 no.2
• /
• pp.47-57
• /
• 1995

The purpose of this study was to investigate the effect of mechanical mixing intensity on composting. The major parameters investigated were the mixing intensity and initial moisture content. Laboratory scale composting reactors with mixing equipment were used in this study. Wastes used for the study were raw nightsoil sludge, nightsoil sludge after vacuum evaporation treatment and pig manure. When moisture contents were 60% and 63%, amount of organic material degraded in the continuous mixing reactors was higher than that in the intermittent mixing reactors. Compost produced from reactors with continuous mixing had better texture than that obtained from reactors with intermittent mixing. When moisture content was 68%, organic waste was kneaded rather than mixed in the continuous mixing reactors. Amount of organic material degraded in the continuous mixing reactors also was lower than that in the intermittent mixing reactors.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.42-42
• /
• 2009

마찰교반접합 (Friction Stir Welding)은 1991년 영국 TWI에서 개발된 접합 법으로서 회전하는 툴이 재료내부에 삽입되면 툴과 재료사이에서 발생하는 마찰열에 의하여 온도가 상승하게 되어 재료는 연화되고, 이러한 재료 내부에서 회전하는 툴이 이동하게 되면 재료 내부는 기계적 교반에 의해 소성변형이 일어남과 동시에 접합이 이루어진다. 마찰교반접합은 동적 재결정에 의한 접합부의 미세한 결정립 형성으로 인하여 기계적 특성이 향상되며 보호 가스가 필요 없어 친환경적임과 동시에 용융 용접 법에 비해 접합 시 에너지 소모가 적으며 또한 접합 후 접합부에서의 변형이 상대적으로 적다는 장점이 있다. 이러한 장점을 가진 마찰교반접합은 알루미늄 합금, 마그네슘 합금 그리고 동 합금과 같은 저 융점 비철재료에 많은 연구와 적용 사례들이 있어왔다. 하지만 최근에는 일반 탄소강, 연강, 오스테나이트계 스테인리스강, 니켈 합금, 티타늄 합금과 같은 고융점 재료에도 연구 및 적용이 진행되고 있는 추세이다. 페라이트계 스테인리스강은 가격이 비싼 Ni을 함유하지 않아 오스테나이트계 스테인리스강에 비하여 강재의 가격은 낮으면서도 고온특성 및 내식성이 우수하여 건축용, 자동차 배기계용으로 널리 사용되고 있다. 하지만 이런 장점을 가진 페라이트계 스테인리스강을 기존의 용융 용접 법으로 접합 시 용접부 및 열영향부에서의 결정립의 조대화로 인한 인성 및 연성이 저하되며, 특히 예민화된 열영향부 입계 내에 Cr 탄화물이 석출되어 입계주변에 Cr 결핍 층을 형성되어 입계부식이 발생되는 문제점이 발생된다. 본 연구에서는 마찰교반접합을 이용하여 두께 3mm의 409 스테인리스강에 대해 맞대기 접합을 실시하였다. 접합 변수를 툴의 재료 (WC-12wt%Co, $Si_3N_4$)로 하여 접합을 실시하였고 접합 후 외관상태 점검, 광학 현미경과 주사 전자 현미경을 통하여 미세조직을 관찰하였으며 황산-황산동 부식 시험을 실시하여 접합부의 부식 특성을 평가하였다.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.37 no.9
• /
• pp.1109-1116
• /
• 2013

This study aims to investigate the spatial randomness of fatigue crack growth rate for the friction stir welded (FSWed) 7075-T651 aluminum alloy joints. Our previous fatigue crack growth test data are adopted in this investigation. To clearly understand the spatial randomness of fatigue crack growth rate, fatigue crack growth tests were conducted under constant stress intensity factor range (SIFR) control testing. The experimental data were analyzed for two different materials-base metal (BM) and weld metal (WM)-to investigate the effects of spatial randomness of fatigue crack growth rate and material properties, the friction stir welded (FSWed) 7075-T651 aluminum alloy joints, namely weld metal (WM) and base metal (BM). The results showed that the variability, as evaluated by Weibull statistical analysis, of the WM is higher than that of the BM.