• Korean Chemical Engineering Research
• /
• v.49 no.5
• /
• pp.664-668
• /
• 2011

Spherical alumina precursors represented by $AlO_xCl_y(OH)_z$, 30~200 nm in particle diameter, were prepared by partial hydrolysis of $AlCl_3$ vapor in a 500 ml reactor. Investigated on the particle morphology and size were the effects of the reaction time, the stirring speed and the reaction temperature. The particle morphology and size was insensitive to the reaction time in the range 20 to 300 s. The variation of the stirring speed from 0 to 300 and 800 rpm showed that the particle size was the largest at 0 rpm. As the temperature was varied from 180 to 190, 200, $140^{\circ}C$, the particle size showed a maximum at $190^{\circ}C$. By calcination of the as-produced particles at $1,200^{\circ}C$ for 6h with a heating rate of $10^{\circ}C$/min, ${\alpha}$-alumina particles 45 nm in surface area equivalent diameter were obtained. The particle shape after calcination turned wormlike due to sintering between neighboring particles. A rapid calcination at $1400^{\circ}C$ for 0.5 h with a higher heating rate of $50^{\circ}C$/min reduced the sintering considerably. An addition of $SiCl_4$ or TMCTS(2,4,6,8-tetramethylcyclosiloxane) to the $AlCl_3$ reduced the sintering effectively in the calcination step; however, peaks of ${\gamma}$ or mullite phase appeared. An addition of $AlF_3$ to the particles obtained from the hydrolysis resulted in a hexagonal disc shaped alumina particles.

• Korean Chemical Engineering Research
• /
• v.56 no.4
• /
• pp.496-523
• /
• 2018

The objective of this study is to evaluate the economic feasibility of two fast pyrolysis and biooil upgrading (FPBU) plants including feed drying, fast pyrolysis by fluidized-bed, biooil recovery, hydro-processing for biooil upgrading, electricity generation, and wastewater treatment. The two FPBU plants are Case 1 of an FPBU plant with steam methane reforming (SMR) for $H_2$ generation (FPBU-HG, 20% yield), and Case 2 of an FPBU with external $H_2$ supply (FPBUEH, 25% yield). The process flow diagrams (PFDs) for the two plants were constructed, and the mass and energy balances were calculated, using a commercial process simulator (ASPEN Plus). A four-level economic potential approach (4-level EP) was used for techno-economic analysis (TEA) under the assumption of sawdust 100 t//d containing 40% water, 30% equity, capital expenditure equal to the equity, $H_2$ price of $1050/ton, and hydrocarbon yield from dried sawdust equal to 20 and 25 % for Case 1 and 2, respectively. TCI (total capital investment), TPC (total production cost), ASR (annual sales revenue), and MFSP (minimum fuel selling price) of Case 1 were $22.2 million, $3.98 million/yr, $4.64 million/yr, and $1.56/l, respectively. Those of Case 2 were $16.1 million, $5.20 million/yr, $5.55 million/yr, and $1.18/l, respectively. Both ROI (return on investment) and PBP (payback period) of Case 1(FPBU-HG) and Case 2(FPBU-EH) were the almost same. If the plant capacity increases into 1,500 t/d for Case 1 and Case 2, ROI would be improved into 15%/yr.

• Proceedings of the KWS Conference
• /
• 2010.05a
• /
• pp.73-73
• /
• 2010

합금원소가 다량 첨가된 고합금강, 스테인리스강, Ni기 초내열합금 등은 용접시 혹은 후열처리 동안 열영향부 (HAZ: heat-affected-zone)에서 결정립계를 따라서 액화균열이 종종 발생한다. 이러한 액화균열은 급속한 가열시 HAZ의 결정립계가 국부적으로 용융되어 액상필름을 형성하고, 냉각시 수축으로 인한 인장구속응력에 의해 필름을 따라서 균열이 발생하여 생성된다. HAZ 결정립계 액화는 탄화물, 황화물, 인화물, 보론계 화합물 등이 급가열시 기지와의 반응에 의해 표피 액상을 형성하는 조성적 액화 (constitutional liquation)에 의한 액상의 결정립계 침투로 설명되거나, 결정립계 자체의 용융점을 상당량 낮추는 보론(B), 인(P), 황(S)등의 편석에 의한 국부적 입계 용융으로 주로 연관 지어 해석한다. HAZ 액화균열은 고온 입계균열 현상이므로, 결정립계의 특성에 따라 크게 영향을 받으며 결정립계 character 설계에 의해 액화균열 저항성을 개선시킬 수 있음을 유추할 수 있다. 한편, 본 연구자들은 최근 Ni기 초내열합금에 있어 입계 serration 현상을 새롭게 발견하였으며, 이론적 접근법을 통해 serration을 위한 특별한 열처리 방법을 개발하였다. 형성된 파형입계는 결정학적인 관점에서 조밀 {111} 입계면을 갖도록 분해 (dissociation)되어 낮은 계면에너지를 갖게 됨을 확인하였으며, 입계형상 변화뿐만 아니라 탄화물 특성변화까지 유도하여 크리프 수명을 기존대비 약 40% 정도 향상시킴을 확인하였다. 본 연구에서는 이러한 직선형 입계 대비 'special boundary'로 간주되는 파형입계가 도입될 경우, 보론 편석 및 HAZ 액화거동에 미치는 영향을 고찰하고자 하였다. SIMS (secondary ion mass spectrometry)를 이용하여 열처리 직후 결정립계 보론편석 정도를 비교하였다. 파형입계 시편의 경우, 일반직선형 시편에 비해 결정립계에 보론편석 저항성이 우수함을 확인할 수 있었다. 재현 HAZ 열사이클 시험을 통해 미세조직을 정량적으로 분석하였다. 파형입계 시편 및 일반직선형 시편 모두 최고온도 $1060^{\circ}C$이상부터 입계 탄화물이 기지내로 완전 용해되고 입계가 액화되기 시작하였다. 최고온도별로 입계액화비율을 정량적으로 비교한 결과, 파형입계가 직선입계 대비 훨씬 낮음을 확인할 수 있었으며, 때때로 액화된 필름이 입계를 따라 전파되지 않고 부분적으로 단락되어 있음이 관찰되었다. 액화시험 후 투과전자현미경을 이용한 EDS (energy dispersive spectrometry) 분석을 통해 결정립계 액화의 주요원인은 입계 $M_{23}C_6$의 조성적 액화반응 보다는 보론 편석 (원자 및 $M_{23}(CB)_6$)으로 인한 결정립계 국부용융이 더 유력함을 유추할 수 있었다. 따라서 상기 결과로부터 입계구조가 안정되어 계면에너지가 낮은 파형입계가 보론편석에 대한 저항성이 우수하였으며, 이러한 결과는 액화 저항성에 대응되어 영향을 미침을 알 수 있었다. 게다가 파형입계에 액상 필름이 생성되더라도 낮은 계면에너지에 의해 비롯된 상대적으로 낮은 적심성 (wettability)에 의해 필름이 쉽게 전파되지 않음을 'Smith 입계 wetting 이론'을 이용하여 해석할 수 있었다.