• Journal of the Korean Vacuum Society
• /
• v.19 no.2
• /
• pp.81-90
• /
• 2010

We introduce a novel and versatile approach for preparing self-assembled nanoporous multilayered films with antireflective properties. Protonated polystyrene-block-poly (4-vinylpyrine) (PS-b-P4VP) and anionic polystyrene-block-poly (acrylic acid) (PS-b-PAA) block copolymer micelles (BCM) were used as building blocks for the layer-by-layer assembly of BCM multilayer films. BCM film growth is governed by electrostatic and hydrogen-bonding interactions between the oppositely BCMs. Both film porosity and film thickness are dependent upon the charge density of the micelles, with the porosity of the film controlled by the solution pH and the molecular weight (Mw) of the constituents. PS7K-b-P4VP28K/PS2K-b-PAA8K films prepared at pH 4 (for PS7K-b-P4VP28K) and pH 6 (for PS2K-b-PAA8K) are highly nanoporous and antireflective. In contrast, PS7K-b-P4VP28K/PS2K-b-PAA8K films assembled at pH 4/4 show a relatively dense surface morphology due to the decreased charge density of PS2K-b-PAA8K. Films formed from BCMs with increased PS block and decreased hydrophilic block (P4VP or PAA) size (e.g., PS36K-b-P4VP12K/PS16K-b-PAA4K at pH 4/4) were also nanoporous. Furthermore, we demonstrate that the nanostructured electrochemical sensors based on patterning methods show the electrochemical activities. Anionic poly(styrene sulfonate) (PSS) layers were selectively and uniformly deposited onto the catalase (CAT)-coated surface using the micro-contact printing method. The pH-induced charge reversal of catalase can provide the selective deposition of consecutive PE multilayers onto patterned PSS layers by causing the electrostatic repulsion between next PE layer and catalase. Based on this patterning method, the hybrid patterned multilayers composed of platinum nanoparticles (PtNP) and catalase were prepared and then their electrochemical properties were investigated from sensing $H_2O_2$ and NO gas. This study was based on the papers reported by our group. (J. Am. Chem. Soc. 128, 9935 (2006); Adv. Mater. 19, 4364 (2007); Electro. Mater. Lett. 3, 163 (2007)).

• Journal of Sensor Science and Technology
• /
• v.7 no.4
• /
• pp.254-262
• /
• 1998

Multilayer Langmuir-Blodgett (LB) films coated on quartz crystal microbalance (QCM) of octa-substituted metallophhtalocyanines ($MPc(OEH)_8$, M = Cu, Co, and Sn) and dihydrogen phthalocyanines ($H_2Pc(OEH)_8$) were used to quantify $NO_2$ concentrations. They were exposed to various concentrations of $NO_2$ in dry $N_2$. Among the four phthalocyanines we tested, the metal-free $H_2Pc(OEH)_8$ was observed to be most sensitive to $NO_2$. However, its LB film showed a partially irreversible behavior, that is part of the frequency change due to $NO_2$ adsorption could not be recovered even after purging with pure $N_2$ gas for an extended period. Examining the spectra of NMR and FTIR revealed fact that the irreversible portion of frequency change was due to ether groups in the linkage between side chains and the Pc unit. In order to remove the effect of such initial deactivation, on $NO_2$ quantification experiment, a freshly fabricated LB film was treated at a high concentration of $NO_2$ so that the ether sites were saturated. A pretreated LB film showed a reproducible performance for repeated uses. The $CuPc(OEH)_8$ LB film showed a satisfactory sensing performance down to as low as 4 ppm. For the $H_2Pc(OEH)_8$ LB film, the lower detection limit was found to be 35ppb of $NO_2$. In order to make the experimental condition more realistic, the carrier gas, dry nitrogen, was replaced by air. It was observed that the presence of oxygen, a weak electron acceptor, reduced the sensitivity and thus increased the sensing limit to hundreds of ppb. Results of experiments with moisture added showed that the interference of moisture was quite severe.

• Journal of the Korean Magnetics Society
• /
• v.8 no.6
• /
• pp.374-379
• /
• 1998

$Mn_1-xCr_xPt_3$ alloy films have been prepared by depositing (Mn, Cr)/Pt multilayers using a rf magnetron sputterer followed by heat treatment. Small and wide angle x-ray diffractometry, magnetic hysteresis loops and Kerr rotation angle spectra of the films have been measured and used to investigate structural, magnetic and magneto-optic properties of the films. The films had a crystal structure of ordered AuCu$_3$ type and the strong preferred orientation of a (111)plane parallel to the film surface. The saturation magnetization of the films was decreased with Cr content reaching almost zero near x=0.58 and then increased for further increasement of Cr content up to x=0.77 over that stayed almost constant. This indicated that Cr atoms were antiferromagnetically coupled with Mn atoms. The magnetic easy axis of MnPt$_3$(x=0) film was parallel to the film surface but those of the films with x$\geq$0.58 increased as Cr content increased reaching about 4 kOe at x=1(CrPt$_3$). The dependence of the Kerr rotation angle on the Cr content was similar to that of the saturation magnetization on the Cr content. The films with x=0.77 and x=1 showed the larger Kerr rotation angle at the wavelengths of near infrared compared to the magneto-optic recording medium, TbFeCo, currently being used.

• Archives of design research
• /
• v.17 no.4
• /
• pp.241-250
• /
• 2004

In this research, the copper alloy plates C2200, C5210, C7701, C8113 were selected to make datum and to identify further usage of metal craft experimentation. For its experimentation, the general welding and TIG welding methods were researched; for 2nd experimentation, the Reticulation and Electroforming skill's differences in color and temperature were researched. With these methods 3 different kinds of works are introduced for sample studies. For this research, Dr. Lee, Dong-Woo who works in Poongsan Metal Co, supported 4 kinds of copper alloy metals. Which are Commercial bronze (Cu-Zn), Deoxidiged Copper(Cu-Sn-P), Nickel Silver (Cu-Ni-Zn), and White Bronze (Cu-Ni); they were applied partly and wholly by the method of Laminatin, Reticulation, Fusing, and Electroforming skills. In case of C2200, the brass, the A. C. TIG welding method is better under 2mm slight plate; the D.C. TIG welding is better upper 2mm plate; and 250~300$^{\circ}C$ is recommended for remain heat treatment. In case of C5210, not having Hydrogen in high temperature return period, doesn't need Oxygen in high temperature and hardening in comparative high temperature neither, it is good for welding. It contains Sn 2-9% ad P 0.03-0.4% generally; and in accordance with the growth rate of Sn contain amount, the harden temperature boundary become broad. In case of cold moment after welding, they are recommended that higher speed TIG welding, smaller melting site and less than 200$^{\circ}C$ for pre-heating temperature. In case of C7701, the 10-20% Ni, 15-30% Zn are widely used.. If it is upper 30% Zn, it become (${\alpha}+{\beta}$) system and adhesive power rate become lower, and the productivity become lower in low temperature but the productivity become higher in high temperature. Nickel Silver's resistance of electricity is well; and the heatproof and incorrodibility is good, too. Lastly, in case of C8113, good at persistence in salty and grind; high in strength of high temperature. In case of white brass, contain 10-30% Nickel and hardened in high temperature and become single phrase. For these reason, the crystallization particles easily become large, if the resistance become higher small amount of Pb, P, S separation rate become higher.