• Korean Chemical Engineering Research
• /
• v.51 no.4
• /
• pp.418-425
• /
• 2013

The catalytic conversion of ethanol to aromatic compounds ETA was studied over ZSM-5 heterogeneous catalysts. The effect of reaction temperature, weight hourly space velocity (WHSV), and addition of water and methanol, which are the potential impurities of bio-ethanol, on the catalytic performance was investigated in a fixed bed reactor. Commercial ZSM-5 catalysts having different Si/$Al_2$ ratios of 23 to 280 and modified ZSM-5 catalysts by addition of metal (Zn, La, Cu, and Ga) were used for the activity and stability tests in ETA reaction. The catalysts were characterized with ammonia temperature programmed desorption ($NH_3$-TPD) and nitrogen adsorption-desorption techniques. The results of catalytic performance revealed that the optimal Si/$Al_2$ ratio of ZSM-5 is about 50~80 and the selectivity to aromatic compounds decreases in the order of Zn/La > Zn > La > Cu > Ga for the modified ZSM-5 catalysts. Among these catalysts from the ETA reaction, Zn-La/ZSM-5 showed the best catalytic performance for the ETA reaction. The selectivity to aromatic compounds was 72% initially and 56% after 30 h over the catalysts at reaction temperature of $437^{\circ}C$ and WHSV of $0.8h^{-1}$.

• Applied Chemistry for Engineering
• /
• v.4 no.2
• /
• pp.365-372
• /
• 1993

$CO_2$ methanation was performed over Ni supported on cation-exchanged Y zeolites under atmospheric pressure at $250{\sim}550^{\circ}C$ and $H_2/CO_2$ mole ratio of 4. Adsorption strength between carbon dioxide and nickel was found to be Influenced by the cation exchanged in the zeolite. TPD(Temperature-programmed desorption) results show that the adsorption strength decreases in the order of Ni/NaY>Ni/MaY>Ni/HY. TPSR(Temperature-programmed surface reaction) results indicate that enhanced methanation activity is obtained when the adsorption strength between carbon dioxide and nickel is stroing. As the reduction temperature increases, the methantion activity of the catalyst increase. From this result the larger size nickel particle seems advantageous for $CO_2$ methanation reaction. The maximum activity is obtained when nickel loading is 3.3wt%. Carbon monoxide is produced as a by-product throughout the reaction temperature range, and as the contact time increases, the selectivity to methane increases and the selectivity to carbon monoxide decreases steadily. Thus methane seems to be produced from $CO_2$ via CO as an intermediate species. In the temperature range of $410{\sim}450^{\circ}C$, the methane production rate is found to be dependent on the orders of 3.3~-0.5 and 1.4~3.6 with respect to $CO_2$ and $H_2$ partial pressures, respectively. This clearly shows that $CO_2$ and $H_2$ are competing for adsorption sites and as the reaction temperature increases, it becomes increasingly difficult for $H_2$ to be adsorbed on the catalyst surface.

• Applied Chemistry for Engineering
• /
• v.10 no.4
• /
• pp.557-562
• /
• 1999

The reaction properties of Pd. Pd-Ce and Pd-La catalysts supported on ${\gamma}-Al_2O_3$ were investigated in the oxidation reaction of methane($CH_4$) exhausted from the compressed natural gas vehicle in a U-tube flow reactor with gas hourly space velocity of $72,000h^{-1}$. The catalysts were characterized by X-ray diffraction(XRD), X-ray photoelectron spectroscopy(XPS), BET surface area and hydrogen chemisorption. Pd catalyst prepared by $Pd(NO_3)_2$ as a palladium precursor and calcined at $600^{\circ}C$ showed the highest activity for a methane oxidation. Catalytic activity of calcined $Pd/{\gamma}-Al_2O_3$ in which most of palladium was converted into palladium oxide species was higher than that of reduced $Pd/{\gamma}-Al_2O_3$ in which most of palladium existed in palladium metal by XRD. As increasing the number of reaction cycles in the wide range of redox, the catalytic activity of $Pd/{\gamma}-Al_2O_3$ was decreased and the highly active window became narrower. Lanthanum oxide promoted Pd catalyst, $Pd/La/{\gamma}-Al_2O_3$ showed enhanced thermal stability compared with $Pd/{\gamma}-Al_2O_3$ even after aging at $1000^{\circ}C$, which was ascribed to the role of La as a promoter to suppress the sintering of palladium metal and ${\gamma}-Al_2O_3$ support. Almost all of methane was removed by the reaction with NO at the redox ratio of 1.2 in case of oxygen excluded steam, but that activity was significantly decreased in the steam containing oxygen.

• Applied Chemistry for Engineering
• /
• v.10 no.2
• /
• pp.237-241
• /
• 1999

Nickel was impregnated on the $SiO_2$ and $Al_2O_3$ supports and applied to the reduction reaction of CFC-113 ($CF_2Cl$-$CFCl_2$) with hydrogen to 3FCl ($CF_2$=CFCl, CFC-1113). The conversion was rapidly declined on the Ni/$SiO_2$(or $Al_2O_3$) and the deactivation accelerated as the increase of Ni content. However, the selectivity of 3FCl was maintained at around 80% level. The simultaneous coprecipitation of copper and lithium on Ni/$Al_2O_3$ improved both the conversion and selectivity to 3FCl, but an excessive amount of lithium reduced the conversion as well as the selectivity of 3FCl. However, in the case of Ni/$SiO_2$, the conversion was greatly reduced possibly due to a loss of silica support with high surface area by the reaction of $SiO_2$ with HF. Such a reduction in conversion also can be ascribed to the decrease in active sites, caused by the addition of alkali metal compound, LiOH.

• Journal of the Korean Chemical Society
• /
• v.42 no.6
• /
• pp.618-628
• /
• 1998

Pure CaO, Mn-doped CaO, Mn/CaO, and K/CaO catalysts were prepared and tested as catalysts for the oxidative coupling of methane in the temperature range of 600 to 800$^{\circ}C$ to investigate the effects of Mn- and K-addition on the catalytic activity of calcium oxide. To characterize the catalysts, X-ray powder diffraction(XRD), XPS, SEM, DSC, and TG analyses were performed. The catalytic reaction was carried out in a single-pass flow reactor using on-line gas chromatography system. Normalized reaction conditions were generally $p(CH_4)/p(O_2)=250$ Torr/50 Torr, total feed flow rate=30 mL/min, and 1 atm of total pressure with He being used as diluent gas. Among the catalysts tested, 6.3 mol% Mn-doped CaO catalyst showed the best $C_2$ yield of 8.0% with a selectivity of 43.2% at 775$^{\circ}C$. The $C_2$ selectivity increased on lightly doped CaO catalysts, while decreased on heavily doped CaO([Mn] > 6.3 mol%) catalysts. 6 wt.% Mn/CaO and 6 wt.% K/CaO catalysts showed the $C_2$ selectivities of 13.2% and 30.9%, respectively, for the reaction. Electrical conductivities of CaO and Mn-doped CaO were measured in the temperature range of 500 to 1000$^{\circ}C$ at Po2's of $10^{-3}\; to\;10^{-1}\;atm.$ The electrical conductivity was decreased with Mn-doping and increased with increasing $P0_2$in the range of $10^{-3}\;to\;10^{-1}\;atm,$ indicating the specimens to be p-type semiconductors. It was suggested that the interstitial oxygen ions formed near the surface can activate methane and the formation of interstitial oxygen ions was discussed on the basis of solid-state chemistry.

• Transactions of the Korean hydrogen and new energy society
• /
• v.24 no.5
• /
• pp.359-366
• /
• 2013

This work is investigated for the catalytic decomposition of hydrogen iodide (HI). Platinum was used as active material by loading on $ZrO_2-SiO_2$ mixed oxide in HI decomposition reaction. To obtain high and stable conversion of hydrogen iodide in severe condition, it was required to improve catalytic activity. For this reason, a method increasing dispersion of platinum was proposed in this study. In order to get high dispersion of platinum, zirconia was incorporated in silica by sol-gel synthesis. Incorporating zirconia influence increasing platinum dispersion and BET surface area as well as decreasing deactivation of catalysts. It should be able to stably product hydrogen for a long time because of inhibitive deactivation. HI decomposition reaction was carried out under the condition of $450^{\circ}C$ and 1 atm in a fixed bed reactor. Catalysts analysis methods such as $N_2$ adsorption/desorption analysis, X-ray diffraction, X-ray fluorescence, ICP-AES and CO gas chemisorption were used to measurement of their physico-chemical properties.

• Transactions of the Korean hydrogen and new energy society
• /
• v.23 no.3
• /
• pp.213-218
• /
• 2012

Steam reforming of methane (SRM) is the primary method to produce hydrogen. Commercial Ni-based catalysts have been optimized for SRM with excess steam ($H_2O/CH_4$ > 2.5) at high temperatures (> $700^{\circ}C$). However, commercial catalysts are not suitable under severe conditions such as stoichiometric steam over methane ratio ($H_2O/CH_4$ = 1.0) and low temperature ($600^{\circ}C$). In this study, 15wt.% Ni catalysts supported on $Ce_{0.8}Zr_{0.2}O_2$ were prepared at various calcination temperatures for SRM at a very high gas hourly space velocity (GHSV) of $621,704h^{-1}$. The calcination temperature was systematically varied to optimize 15wt.% $Ni-Ce_{0.8}Zr_{0.2}O_2$ catalyst at a $H_2O/CH_4$ ratio of 1.0 and at $600^{\circ}C$. 15wt.% $Ni-Ce_{0.8}Zr_{0.2}O_2$ catalyst calcined at $500^{\circ}C$ exhibited the highest $CH_4$ conversion as well as stability with time on stream. Also, 15wt.% $Ni-Ce_{0.8}Zr_{0.2}O_2$ catalyst calcined at $500^{\circ}C$ showed the highest $H_2$ yield (58%) and CO yield (21%) among the catalysts. This is due to complex NiO species, which have relatively strong metal to support interaction (SMSI).

• Korean Journal of Materials Research
• /
• v.24 no.8
• /
• pp.393-400
• /
• 2014

NiO catalysts were successfully coated onto FeCrAl metal alloy foam as a catalyst support via a dip-coating method. To demonstrate the optimum amount of NiO catalyst on the FeCrAl metal alloy foam, the molar concentration of the Ni precursor in a coating solution was controlled, with five different amounts of 0.4 M, 0.6 M, 0.8 M, 1.0 M, and 1.2 M for a dip-coating process. The structural, morphological, and chemical bonding properties of the NiO-catalyst-coated FeCrAl metal alloy foam samples were assessed by means of field-emission scanning electron microscopy(FESEM), scanning electron microscopy-energy dispersive spectroscopy(SEM-EDS), X-ray diffraction(XRD), and X-ray photoelectron spectroscopy(XPS). In particular, when the FeCrAl metal alloy foam samples were coated using a coating solution with a 0.8 M Ni precursor, well-dispersed NiO catalysts on the FeCrAl metal alloy foam compared to the other samples were confirmed. Also, the XPS results exhibited the chemical bonding states of the NiO phases and the FeCrAl metal alloy foam. The results showed that a dip-coating method is one of best ways to coat well-dispersed NiO catalysts onto FeCrAl metal alloy foam.