• Composites Research
• /
• v.16 no.6
• /
• pp.48-55
• /
• 2003

This research makes comparisons of empirical fatigue-lives between AC8A A1 alloy and the metal matrix composites(A1/A12O3, A1/A12O3/A12O3p), and also includes comparisons of fatigue-lives between empirical fatigue-lives and estimated fatigue-lives from regular-periodic load testing, AE method to predict fatigue-crack initiation before visible in sight and SEM(scanning electron microscope) photographs of each material. According to the test results of the notched specimen. the fatigue life of the hybrid metal matrix composites and the metal matrix composites, which are more brittle than the base matrix was shorter than that of the base matrix under both types of loads. In addition, the fatigue-life estimated from the damage summation method and that from experiments at random loads were fairly identical.

• 기계와재료
• /
• v.6 no.2 s.20
• /
• pp.97-108
• /
• 1994

• Composites Research
• /
• v.36 no.2
• /
• pp.101-107
• /
• 2023

In this study, aluminum nitride (AlN) reinforced aluminum (Al) matrix composites are fabricated via plasma arc melting under a nitrogen atmosphere. Within a minute of the chemical reaction between Al and N, dispersed AlN with the shape of transient and lamellar layers is in situ formed in the Al matrix. The composite contains 10 vol.% AlN reinforcements with low thermal resistance and strong bonding at the interfaces, which leads to the unique combination of thermal expansivity and conductivity in the resulting composites. The coefficient of thermal expansion of the composite can be further reduced when Si was alloyed into the Al matrix, which proposes the potential of the in situ Al matrix composites for thermal management applications.

• Journal of the KSME
• /
• v.31 no.3
• /
• pp.293-299
• /
• 1991

단섬유보강 금속복합재료의 2차가공은 금속복합재료의 넓은 범위 응용을 위해 필히 요구된다. 여러 가공방법 중 하나인 열간압출시 보강섬유파괴 및 계면에서의 접합분리 및 균열발생이 없는 제조공정의 최적화를 위해서 가공시 내부조직의 소성변형 기구 규명보다 압출력에 의한 응력분 포와 기지재료와 보강섬유 사이 계면 변화 및 기계적 특성 관계규명이 정량적으로 요구된다. 본 글에서는 유한요소법을 이용하여 계면에서의 접합상태를 임의로 가정하여 압출조건에 따른 압 출후의 보강섬유 방향 및 계면균열 및 접합분리를 거시적으로 예측하고, advanced shear-lag을 이용하여 균열 전, 후의 응력. 변형관계를 미시적으로 규명할 수 있음을 제시하였다. 그러나 향후 현상적 모델인 shear-lag 모델을 수학적 모델인 균질화법에 도입하면 미시적. 거시적 거 동해석이 함께 요구되는 금속복합재료의 열간압출거동 해석을 일체적으로 행할 수 있어 효율적 이고 정확한 예측이 가능하리라고 사료된다.

• Journal of the KSME
• /
• v.28 no.3
• /
• pp.216-225
• /
• 1988

고성능 복합재료는 그 제조 공정이 다양하고 공정의 개념이 기존 금속 재료와는 크게 다르며, 많은 열 공학 및 금속 재료와는 크게 다르며, 많은 열 공학 및 유체공학적인 문제를 수반하고 있다. 특히 최적 공정의 선택이 가장 큰 관심의 대상이므로 공정의 modeling에 대한 연구가 많이 이루어지고 있으며, 이러한 modeling을 통하여 고성능 복합재료 제조 공정에서의 문제점을 보다 잘 이해할 수 있고 제조 공정의 최적화에 이용할 경우 비용이 많이 들고 시간이 오래 걸 리는 실험적인 방법을 많은 부분 대치할 수 있어 새로운 기지재료가 소개되었을 경우의 그 제조 공정의 결정에 있어 시간과 비용을 대폭 절감시킬 수 있다. 앞으로 소재의 기능화, 경량화 추 세에 힘입어 복합재료의 수요는 계속 늘어날 전망이어서 새로운 공업용 소재로서의 복합재료에 대한 공학적인 이해가 필요하며, 특히 기존의 재료 제조 공정과는 비교적 색다른 복합재료 제조 공정에 대한 보다 넓은 이해가 필요할 것이다.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.03a
• /
• pp.222-222
• /
• 2003

나노크기 금속입자가 분산된 세라믹 나노복합재료는 향상된 기계적 특성과 함께 독특한 전기적, 자기적 특성을 보여주어 새로운 기능성 재료로의 응용가능성을 갖고 있다. 그러나 소결 중의 반응이나 입자성장 등으로 형성된 반응상 또는 조대한 입자상이 세라믹 기지의 입계 등에 존재한다면, 나노크기 금속상 분산에 의한 기계적 특성의 향상과 독특한 기능성 부여라는 장점들이 없어지게 된다. 따라서 요구되는 특성을 구현할 수 있는 금속분산 나노복합재료의 제조를 위해서는 미세조직 제어를 위한 최적의 제조공정 확립과 미세조직과 특성 등의 관계에 대한 연구가 요구된다. 본 연구에서는 기지상으로 A1$_2$O$_3$를, 분산상으로는 저융점 금속이며 일반적인 A1$_2$O$_3$의 가압소결시에 (약 140$0^{\circ}C$) 액상으로 존재하는 금속 Cu를 선택하여 조성이 5 vol% Cu가 되도록 복합재료를 제조하였다. $Al_2$O$_3$와 CuO 원료분말들은 습식 및 건식 볼 밀링을 통하여 균일한 분말혼합체로 제조되었다. 혼합분말은 열간가압소결기 내에 장입한 후 35$0^{\circ}C$에서 30분 동안 H$_2$가스를 흘려주며 CuO를 Cu로 환원 처리하였다. 계속해서 H$_2$분위기를 유지하며 승온한 후, 각각 1000-145$0^{\circ}C$에서 분위기를 Ar 으로 치환하였다. 소결은 145$0^{\circ}C$에서 30 ㎫의 압력으로 1시간동안 행하였다 소결한 시편들은 직사각형 형태로 가공하였으며 표면은 0.5$\mu\textrm{m}$의 다이아몬드 입자로 연마하였다. XRD, SEM 및 TEM을 이용하여 상분석 및 미세조직관찰을 행하였다. 파괴강도는 3중점 굽힘 법으로 (3-point bending test) 측정하였다. 이때 시편 하부의 지지 점간의 거리는 30mm, cross-head 속도는 0.5 mm/min으로 하였고 5개의 시편을 측정하여 평균값을 구하였다.

• Composites Research
• /
• v.14 no.5
• /
• pp.1-11
• /
• 2001

The particulates reinforced metal matrix composites(PMMC) have a number of interesting mechanical properties. including high strength and good resistance to wear at high temperature and low thermal expansion. The equipment structure to obtain the homogeneous distribution in composites are proposed for the continuous pouring of reinforcement at the desired temperature. The particulates reinforced metal matrix composites(A357/SiCp) were fabricated by the process of the combined stirring method with the various fabrication process. The combined stirring method to niform distribution of particle is consisted of two stirring force both electro-magnetic stirring generated from induction heating and mechanical stirring with graphite stirrer. PMMC billets were fabricated with the volume fractions ranged from 0% to 20% and particle sizes ranged from 14${\mu}{\textrm}{m}$ to 25${\mu}{\textrm}{m}$. It is important to cont the size of primary $\alpha$-Al solid particles because it could become the cause of the particle pushing or capture phenomena from the fact that secondary dendrite arm spacing size depends on the cooling rate during the solidification in hypoeutectic Al-Si alloy. Therefore, the effect of primary $\alpha$-Al on the reinforcement distribution in matrix alloys has been investigated. The microstructure of PMMC fabracated with various volume fractions(0%, 10%, and 20%) and particle size were observed.

• Korean Journal of Materials Research
• /
• v.6 no.11
• /
• pp.1090-1098
• /
• 1996

개조한 가스 금속 아아크 용접공정을 이용하여 SiC/AI 금속기 복합재료를 제조하고 그 특성을 조사하였다. AI 모재위에 강화입자의 크기와 부피분율을 변화하여 다양한 SiC/AI 복합재료층을 제조하였고, 만들어진 복합재료층의 특성은 미세조직관찰과 미소경도시험을 통하여 이루어졌다. 복합재료층의 두께는 약 7-8mm로 측정되었고 균일한 강화입자의 분포도를 얻을 수 있었다. 분산입자의 부피분률은 Ar가스의 유량에 의하여 조절하였고 분산입자의 부피분률이 증가하고 크기가 작아짐에 따라 기지의 수지상 응고조직은 더욱 미세화되었다. 복합재료의 부피경도는 분산입자의 부피분률이 감소함에 따라 낮아졌으나 입자 크기에는 크게 변화가 없는 것으로 나타났다.

• Composites Research
• /
• v.16 no.3
• /
• pp.1-8
• /
• 2003

Densification occurs by the inelastic flow of the matrix materials during the consolidation processes at high temperature for MMCs, and the results depend on many process conditions such as applied pressure, temperature and volume fraction of fiber and matrix materials. This is particularly important in titanium matrix composites since material failure may occur by either the applied conditions or microstructural parameters through the processes, and thus a generic model based on micro-mechanical approaches enabling the evolution of density over time to be predicted has been developed. The mode developed is then implemented into FEM so that practical process simulation has been carried out. Further the experimental investigation of the consolidation behavior of SiC/Ti-6Al-4V composites using vacuum hot pressing has been performed, and the results obtained are compared with the model predictions.

• Composites Research
• /
• v.34 no.4
• /
• pp.212-225
• /
• 2021

Metal matrix composites (MMCs) were widely used in various industries, due to the excellent properties: high strength, stiffness, wear resistance, hardness, thermal conductivity, electrical conductivity, etc. With additive manufacturing (AM) technology rapidly developed, AM MMCs have been actively investigated thanks to the cost- and time-saving manufacturing. However, several issues still need to be addressed before fabricating AM MMCs. Here, several types of MMCs were introduced and MMCs' design methods to tackle the issues were suggested in a powder bed fusion (PBF) technique. The paper could come up with a guideline for the material and process design of MMCs in the PBF technique.