• Journal of Korean Society of Steel Construction
• /
• v.9 no.2 s.31
• /
• pp.193-204
• /
• 1997

In order to quantify the relationships of the important physical factors relating failure to strong earthquake loading, the plastic fatigue problems for structural components under repeated loading were reviewed first. A new concept of very low cycle fatigue failure for structural components under severe cyclic excitations as in strong earthquakes was represented. Also, an experimental study was made of the very low cycle fatigue failure of structural steel elements. It was attempted to realize the ultimate failure in the course of loading repetitions of the order of several to twenty. The test specimen had a form of rectangular plate, representing a thin-plated element in a steel member as wide-flange cross section. It was subjected to uniaxial loading repeatedly, until complete failure takes place after undergoing inelastic buckling, plastic elongation and/or their combination. It was seen as a result that the state of the ultimate failure is closely related to the maximum strain at the extreme fiber in the cross section.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.12 no.4_1
• /
• pp.23-32
• /
• 1992

The objective of this study is to identify the quantitative relationships among the important physical factors associated with failure of steel members under strong seismic excitations through very low-cycle fatigue tests. Very low-cycle fatigue is meant to be structural fatigue causing cracks and rupture in about 5~30 cycle ranges. The angle specimen was subjected to repeated axial Ioad after undergoing inelastic buckling. The test results reveal that the energy absorption capacities vary heavily with the history of loading and the failure mode. The maximum values of residual local strain at the initiation of a visible crack due to the very low-cycle fatigue were of the order of 25~40%, regardless of loading patterns, deflection modes, and width-to-thickness ratios.

• Journal of Industrial Technology
• /
• v.22 no.A
• /
• pp.3-8
• /
• 2002

In this study, extremely low cycle fatigue tests were carried out under push-pull loading conditions using graphite cast iron (GCD). In order to clarify the fatigue fracture mechanism of GCD in an extremely low cycle fatigue regime successive observations of internal fatigue damage were performed. The results obtained are as follows. (1) The process of extremely low cycle fatigue can be classified into three stages which are composed of the generation, growth and coalescence of microvoids inside materials. (2) In an extremely low cycle fatigue regime, microvoids originate from debonding of graphite-matrix interface.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.30 no.12 s.255
• /
• pp.1573-1580
• /
• 2006

In this study, fatigue tests were carried out under push-pull loading condition using spheroidal graphite cast iron in order to clarify the internal fatigue fracture mechanism in an extremely low cycle fatigue regime. It is found that a successive observation of internal fatigue damage it is found that the fracture processes go through three stages, that is, the generation, growth and coalescence of microvoids originated from debonding of graphite-matrix interface. It is also found that the crack which is initiated from the void propagates by coalescence of neighboring cracks and the fatigue crack growth rate can be expressed in form of the Manson-Coffin rule type. In this paper, quantitative analyses of fatigue properties for realization of simulation about fatigue life evaluation are also presented.