• Journal of the Korean Ceramic Society
• /
• v.33 no.3
• /
• pp.251-258
• /
• 1996

The reactions between an active metal brazing alloy and interlayers together with the effects of interlayer type on the interfacial microstructure change were investiaged for silicon nitride/stainless steel joint. The bending strengths were measured for joints with Mo, Cu, Ni interlayer type of different thicknesses. It was found that the interlayer with a low yield strength value is effective to improve the bending strength of the Si3N4/stainless steel joint. The maximum joint strength obtained at room temperature for a laminated Cu/Mo interlayer was about 460 MPa. The combined use of Mo and thin Cu layer was found to be effective in enhancing the bending strength for the Si3N4/S.S.316 joint.

• Journal of the Korean Ceramic Society
• /
• v.26 no.4
• /
• pp.583-587
• /
• 1989

Various $\alpha$-silicon carbied and colloidal graphite particles were sintered at 155$0^{\circ}C$ in vacuum atmosphere by reaction bonding sintering method, and the physical properties and microstructural analysis of specimen were investigated. With decreasing particle size, sintered density and 3-point bending strength of materials were increased and 3.2${\mu}{\textrm}{m}$ specimen showed high density and strength, 3.05g/㎤, 40kg/$\textrm{mm}^2$, respectively. The results of X-ray diffractometer and optical micrographs analysis showed that graphite and silicon melt reacted to convert to fine $\beta$-SiC particle and the body was changed to dense material.

• Journal of the Korean Ceramic Society
• /
• v.33 no.2
• /
• pp.127-134
• /
• 1996

The thermal residual stresses were estimated for brazed Si3N4/S.S.316 joints with Cu/Mo multi-interlayers using FEM, and their bending strengths at room temperature were measured for various interlayer configura-tions. The Cu, Mo multi-interlayer decreased the maximum residual stress in Si3N4 and caused the residual stress redistribution rsulting in the high residual stress at Mo interlayer. The stress distribution in the joints as well as the maximum residual stress in silicon nitride were found to be main factors for determining bending strengths and Weibull modulous of the joints. The bending strength of the brazed Si3N4/S.S.316 joints with specific Cu, Mo multi-interlayer system were found to be above 400 MPa.

• Journal of the Korean Ceramic Society
• /
• v.32 no.11
• /
• pp.1227-1232
• /
• 1995

Effect of heating rate on the microstructure of the silicon nitride ceramics has been investigated. The specimens with composition of 92Si3N4-6Y2O3-2Al2O3 (in wt%) were sintered at 176$0^{\circ}C$ under 127 kPa for 3h in N2 atmosphere at various heating rates from 1 to 10$0^{\circ}C$/min. The grain size of larger than 2${\mu}{\textrm}{m}$ and less than 1${\mu}{\textrm}{m}$ were measured and compared for the specimens. Regardless of heating rate, grain size of all the specimens showed bimodal distributions and the fracture toughness remained in the range of 5.53~5.72 MPa.m1/2. However, the aspect ratio of the grains of diameter above 2${\mu}{\textrm}{m}$ increased with the heating rate while their grain size and volume fraction decreased.

• Journal of Korea Foundry Society
• /
• v.11 no.6
• /
• pp.491-497
• /
• 1991

Vanadium은 비중이 6.09로써 비교적 무거운 금속에 속하나 Al을 30wt% 이내로 첨가하여 $Ni_3Al$ 및 TiAl와 유사한 비강도가 크며 내열성을 지니는 V-Al합금을 얻을 가능성을 지니고 있다. 본 연구에서는 V-Al합금에 Si, Y, Ti, B등 제3원소를 첨가함에 따르는 미세 응고조직의 거동과 기계적 성질을 조사하였다. 알곤 분위기에서 제조된 V-30%Al합금은 상온에서 고용체와 취성이 큰 금속간 화합물인 $VAl_3$등 2상으로 존재하므로 용체화 처리 과정이 요구되며 24시간 이상 장시간 열처리에 의하여 단일 고용상을 이룰 수 있었다. 규소의 첨가는 금속간 화합물의 형성과 아울러 합금의 경도를 크게 증가시키는 경향을 나타내며 B을 0.3%정도가지 첨가할 때 경도가 낮아지는 현상이 관찰되었다. �c칭된 V-30%Al 합금은 입계면을 따라 decohesive rupture 현상을 나타내며 입자간 파괴 현상도 일부 관찰되었다.

• 기계와재료
• /
• v.22 no.4
• /
• pp.22-35
• /
• 2010

저에너지 소모를 위한 대책으로 장치설비의 고효율화를 이루어 나가고 있으나, 고온 고압 등의 극한환경 하의 공정이 증가하면서 상기의 조건 하에서도 안정적으로 작동 가능한 다공질 세라믹스를 이용한 촉매기술 또는 포집 분리기술에 대한 필요성이 부각되고 있다. 본 고에서는 다공성 세라믹 소재가 특별히 유효하게 대응 가능한 대기오염과 관련하여 오염원 물질 및 오염의 실태를 살펴보고, 각종 다공성 세라믹스의 제조방법과 이에 따른 소재특성을 소개하고 시장의 현황과 전망을 정리하였다. 또한 다공성 세라믹 소재의 가장 대표적인 활용 형태인 하니컴 구조체의 제조방법 및 특성에 대하여 기술하고, 다공성 세라믹 소재의 실제 활용과 관련해서는 오염물질을 입자상물질과 가스상물질로 대별하여 대표적인 사용처와 소재를 수록하였으며, 차세대 신개념 필터로 연구 중인 반응소결 질화규소에 대해 언급하였다.

• Journal of the Korean Ceramic Society
• /
• v.28 no.8
• /
• pp.577-584
• /
• 1991

Among various forming techniques for ceramics, we have studied the slip casting method for the binary system of SiC and carbon. The stability of the slip of silicon carbide and carbon were investigated by measurements of zeta potential, viscosity, sedimentation height, and also studied as functions of PH and amounts of dispersants. A preform of SiC and C was prepared by slip casting and heat treatment at 400∼600$^{\circ}C$ under N2 gas. The preform was reacted with Si metal at 1550$^{\circ}C$, 10-1 mmHg to give rise a reaction bonded SiC with a density of 3.0g/㎤ and a bending strength of 580 MPa.

• Journal of the Korean Ceramic Society
• /
• v.48 no.5
• /
• pp.348-353
• /
• 2011

By gel-casting, the silicon-polymer green bodies were prepared for silicon nitride ceramics, sintered by microwave gas phase reaction. Considering the viscosity and the idle time of slurries, we decided the operational conditions of related processes, and the optimum concentrations of raw materials powders, organic monomers, cross-linker, dispersant, initiator, and catalyst. So we could get the machinable green bodies, having about 50 MPa of bending strength without cracks by selecting drying conditions carefully.

• Journal of the Korean Ceramic Society
• /
• v.41 no.12 s.271
• /
• pp.893-899
• /
• 2004

The mechanical properties and microstructure and thermal properties of Nitrided Pressureless Sintering(NPS) silicon nitride ceramics, containing three type of $Al_{2}O_3,\;Y_{2}O_3$ sintering additives, were investigated. Also, we have investigated the effect of silicon metal content changing with 0, 5, 10, 15, and $20wt\%$ Si in each composition. In $5wt\%\;Al_{2}O_3,\;5wt\%\;Y_{2}O_3,\;and\;5wt\%$ Si composition, silicon nitride sintered body was successfully densified to a high density. The average 4-point flexural strength and relative density of these specimens were 500 MPa and 98% respectively. Also, Thermal expansion coefficient and thermal conductivity of specimens at room temperature were $2.89{\times}10^{-6}/^{\circ}C\;and\;28W/m^{\circ}C$, respectively. The flexural strength of sintered specimens after thermal shock test of 20,000 cycles was maintained as-received value of 500 MPa.

• Korean Chemical Engineering Research
• /
• v.40 no.6
• /
• pp.752-756
• /
• 2002

Green-emitting $Zn_2SiO_4:Mn$ phosphors for PDP(Plasma Display Panel) application were synthesized by colloidal seed-assisted spray pyrolysis process. The codoping with $Gd^{3+}/Li^+$, which replaces $Si^{4+}$ site in the willemite structure, was performed to improve the luminous properties of the $Zn_2SiO_4:Mn$ phosphors. The particles prepared by spray pyrolysis process using fumed silica colloidal solution had a spherical shape, small particle size, narrow size distribution, and non-aggregation characteristics. The $Gd^{3+}/Li^+$ codoping amount affected the luminous characteristics of $Zn_2SiO_4:Mn$ phosphors. The codoping with proper amounts of $Gd^{3+}/Li^+$ improved both the photoluminescence efficiency and decay time of $Zn_2SiO_4:Mn$ phosphor particles. In spray pyrolysis, the post-treatment temperature is another factor controlling the luminous performance of $Zn_2SiO_4:Mn$ phosphors. The $Zn_{1.9}SiO_4:Mn_{0.1}$ phosphor particles containing 0.1 mol% $Gd^{3+}/Li^+$ co-dopant had a 5% higher PL intensity than the commercial product and 5.7 ms decay time after post-treatment at $1,145^{\circ}C$.