Fluosilicic acid(H2SiF6) is recovered as an aqueous solution which absorbs $SiF_4$ produced from the manufacturing of industrial-graded H3PO4 or HF. Generally, fluosilicates are the salts produced by the reaction of H2SiF6 and metal salts. Addition of fluosilicates to cement endows odd properties through unique chemical reaction with the fresh and hardened cement. This study was performed to know mechanical properties and watertightness using fluosilicates based composite made from fluosilicates and other compounds. Mix proportions for experiments were modulated at 0.45 of water to cement ratio and $0.0-2.0\%$ of adding ratio of fluosilicates based composite. Evaluation for mechanical properties of concrete was conducted to know fresh state of concrete, hardening state of concrete, and watertightness. Evaluation for watertightness of concrete was carried out permeability, absorption test and porosity analysis. In addition. Scanning Electron Microscopy(SEM) and Energy Dispersive X-Ray(EDX) used for investigating micro-structure and atomic component distributed in hardened concrete. It is ascertained that characteristics of mechanical properties and watertightness was more improved than non-added because of packing role of fluosilicates based composite and pozzolanic reaction of soluble $SiO_2$. Also, concrete added fluosilicates based composite had a tendency to delay setting time and only $0.5\%$ addition of fluosilicates based composite delayed 150 minutes compared with non-added.

• Journal of the Korea Concrete Institute
• /
• v.18 no.1 s.91
• /
• pp.57-64
• /
• 2006

The crack presented in concrete structures causes a structural defect, the durability decrease, and external damages etc. Therefore, it is necessary to improve durability through the effort to control the crack. Fluosilicic acid($H_2SiF_6$) is recovered as aqueous solution which absorbs $SiF_4$ produced from the manufacturing of industrial-graded $H_3PO_4$ or HF. Generally, fluosilicates prepared by the reaction between $H_2SiF_6$ and metal salts. Addition of fluosilicates to cement endows odd properties through unique chemical reaction with the fresh and hardened cement. Mix proportions for experiment were modulated at 0.45 of water to cement ratio and $0.0{\sim}2.0%$ of adding ratio of fluosilicate salt based inorganic compound. To evaluate correlation of concrete strength and adding ratio of fluosilicate salt based inorganic compound, the tests were performed about design strength(21, 24, 27 MPa) with 0.5% of adding ratio of fluosilicate salt based inorganic compound. Applications of fluosilicate salt based inorganic compound to reduce cracks resulted from plastic and drying shrinkage, to improve durability are presented in this paper. Durability was evaluated as neutralization, chloride ion penetration depth, freezing thawing resistant tests and weight loss according reinforcement corrosion. It is ascertained that the concrete added fluosilicate salt based inorganic compound showed m ability to reduce the total area and maximum crack width significantly as compared non-added concrete. In addition, the durability of concrete improved because of resistance to crack and watertightness by packing role of fluosilicate salt based inorganic compound obtained and pozzolanic reaction of soluble $SiO_2$ than non-added concrete.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.429-432
• /
• 2008

Large area members such as foundation concrete of underground structures in power plants have an effect on structural stability and durability of the structure due to danger of crack occurrence and shrinkage crack that occur owing to the difference of temperature by heat of hydration between inside and outside of the members at initial age. And a construction for waterproofness is performed additionally to protect marine structures from osmosis of seawater because the structures adjoin below the surface of sea. So, if a rise of the heat of hydration, crack, and corrosion of bars are controled effectively using a composite such as fluosilicate salt in concrete production process of a initial construction, expenses are cut down and construction hours are reduced by securing durability through improvement of watertightness. The property tests of adiabatic temperature by hydration are carried out at initial age about standard concrete and test concrete using a fluosilicate salt composite to evaluate an effect on improvement of watertightness for concrete structures in this study. And the experiments such as a permeability test of hardened concrete, a water absorption test, a compression strength test and a elongation test are carried out and the results from these are described.