• Journal of the Korea Concrete Institute
• /
• v.17 no.5 s.89
• /
• pp.769-774
• /
• 2005

Fluosilicic acid(H2SiF6) is recovered as an aqueous solution which absorbs $SiF_4$ produced from the manufacturing of industrial-graded H3PO4 or HF. Generally, fluosilicates are the salts produced by the reaction of H2SiF6 and metal salts. Addition of fluosilicates to cement endows odd properties through unique chemical reaction with the fresh and hardened cement. This study was performed to know mechanical properties and watertightness using fluosilicates based composite made from fluosilicates and other compounds. Mix proportions for experiments were modulated at 0.45 of water to cement ratio and $0.0-2.0\%$ of adding ratio of fluosilicates based composite. Evaluation for mechanical properties of concrete was conducted to know fresh state of concrete, hardening state of concrete, and watertightness. Evaluation for watertightness of concrete was carried out permeability, absorption test and porosity analysis. In addition. Scanning Electron Microscopy(SEM) and Energy Dispersive X-Ray(EDX) used for investigating micro-structure and atomic component distributed in hardened concrete. It is ascertained that characteristics of mechanical properties and watertightness was more improved than non-added because of packing role of fluosilicates based composite and pozzolanic reaction of soluble $SiO_2$. Also, concrete added fluosilicates based composite had a tendency to delay setting time and only $0.5\%$ addition of fluosilicates based composite delayed 150 minutes compared with non-added.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• v.y2004m10
• /
• pp.33-38
• /
• 2004

This study was performed to know watertightness and reduction effect and crack occurred by hydration heat, restraint of multiplication of hydration heat, through mechanical test, strength test and crack control test using fluosilicate salt based inorganic compound made from by-product during phosphoric acid manufacturing process. Mix proportions for experiment were modulated at 0.45 of water to cement ratio and $0.5-2.0\%$ of adding ratio of fluosilicate salt based inorganic compound. Evaluation for watertightness of concrete was carried out permeability, absorption test and porosity analysis. Effect of crack reduction was evaluated by length, drying shrinkage as well as stress change of hardened concrete at unrestraint/restraint state and also elucidated crack pattern on the concrete surface. It is ascertained that characteristics of crack resistance and watertightness for concrete was improved by an adequate addition of fluosilicate salt based inorganic compound.

• Journal of the Korea Concrete Institute
• /
• v.18 no.1 s.91
• /
• pp.57-64
• /
• 2006

The crack presented in concrete structures causes a structural defect, the durability decrease, and external damages etc. Therefore, it is necessary to improve durability through the effort to control the crack. Fluosilicic acid($H_2SiF_6$) is recovered as aqueous solution which absorbs $SiF_4$ produced from the manufacturing of industrial-graded $H_3PO_4$ or HF. Generally, fluosilicates prepared by the reaction between $H_2SiF_6$ and metal salts. Addition of fluosilicates to cement endows odd properties through unique chemical reaction with the fresh and hardened cement. Mix proportions for experiment were modulated at 0.45 of water to cement ratio and $0.0{\sim}2.0%$ of adding ratio of fluosilicate salt based inorganic compound. To evaluate correlation of concrete strength and adding ratio of fluosilicate salt based inorganic compound, the tests were performed about design strength(21, 24, 27 MPa) with 0.5% of adding ratio of fluosilicate salt based inorganic compound. Applications of fluosilicate salt based inorganic compound to reduce cracks resulted from plastic and drying shrinkage, to improve durability are presented in this paper. Durability was evaluated as neutralization, chloride ion penetration depth, freezing thawing resistant tests and weight loss according reinforcement corrosion. It is ascertained that the concrete added fluosilicate salt based inorganic compound showed m ability to reduce the total area and maximum crack width significantly as compared non-added concrete. In addition, the durability of concrete improved because of resistance to crack and watertightness by packing role of fluosilicate salt based inorganic compound obtained and pozzolanic reaction of soluble $SiO_2$ than non-added concrete.