This paper reports results of an investigation to determine properties of superplasticizered fly ash concrete. The mixture proportions of fly ash were 0, 10, 20 and 30%, by weight of cement, and superplasticizer was added as a percentage of fly ash, 0, 0.6, 12 and 1.8%. To investigate the effective use of the superplasticized fly ash concrete, the basic data were analyzed. The results obtained were summarized as follows : 1. The unit water content was decreased by 1%, 6% and increased by 2% to the ratio of addition of fly ash 10%, 20%, 30%, respectively, but in case of the superplasticized fly ash concrete, it was decreased by 3~16%, 4~14% and 10~17%, at 0.6, 12, and 1.8% dosage of superplasticizer, respectively. 2. In the properties of the fresh fly ash concrete, the slump loss was reduced with the ratio of replacement of fly ash increased, and with times went by. When using superplasticizer in fly ash substituting concrete, the fludity in the concrete was not decreased. 3. The compressive strength of fly ash concrete at early ages was lower than that of ordinary concrete. At the later age of 28 days, the compressive strength with 20% addition of fly ash was increased than that of ordinary concrete. In cased of 10%, 30% addition of fly ash, the compressive strength were reduced. From this, it was proved that the optimum amount of fly ash appears to be about 20%. The compressive strength at all ages of superplasticized fly ash concrete was significantly higher than that of fly ash concrete, with increasing fly ash content. 4. In case of the tensile strength, the effects of the increasing strength with the ages were similar to those of the compressive strtength, and at the later ages was seen a decreasing tendency of strengths. 5. The correlation between compressive and tensile strength of superplasticized fly ash concrete was highly significant. The multiple regression equations of compressive and tensile strength were obtained on a function of the mixture proportion of fly ash and the addition of superplasticizer. The relation between compressive and tensile strength is higher than for ordinary concrete. The strength ratio is 7~11, and it is higher than that of ordinary concrete, 8~10. 6. Bulk density was decreased by 1~3% compared with ordinary concrete with the mixture proportion of fly ash increased, 10~30%, and decreased by 1~2% with the superplasticizer added 0.6~1.8%.