• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.47 no.2
• /
• pp.15-20
• /
• 2010

In this study, AZO (Al: 3 wt%) thin films have been prepared on PES Plastic substrates at various working pressure (5~20 mTorr), $O_2$ gas flow rate(0~3%) and the fixed substrate temperature of 200 f by using the RF magnetron sputtering and their optical and electrical properties have been studied. The XRD measurement shows that AZO thin films exhibit c-axis preferred orientation. From the results of AFM measurements, it is known that the lowest surface roughness (3.49 nm) is obtained for the AZO thin film fabricated at 5 mTorr of working pressure and 3% of $O_2$ gas flow rate. The optical transmittance of AZO thin films is measured as 80% in the visible region. We observe that the energy band gap of AZO thin films increases with decreasing the working pressure and the $O_2$ gas flow rate. This phenomenon is due to the Burstein-Moss effect. Hall measurement shows that the maximum carrier concentration ($2.63\;{\times}\;10^{20}\;cm^{-3}$) and the minimum resistivity ($4.35\;{\times}\;10^{-3}\;{\Omega}cm$) are obtained for the AZO thin film fabricated at 5mTorr of working pressure and 0% of $O_2$ gas flow rate.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.18 no.10
• /
• pp.2497-2502
• /
• 2014

The 5 wt.% Ga-doped zinc oxide (GZO) thin films were fabricated on PES substrates with various RF power 50~80 W by using RF magnetron sputtering in order to investigate the optical and electrical properties of GZO thin films. The XRD measurement showed that GZO thin films exhibit c-axis orientation. At a RF power of 70W, the GZO thin film showed the highest (002) diffraction peak with a Full-Width-Half-Maximum (FWHM) of $0.44^{\circ}$. AFM analysis showed that the lowest surface roughness (0.20 nm) was obtained for the GZO thin film fabricated at 70 W of RF power. The electrical property indicated that the minimum resistivity ($6.93{\times}10^{-4}{\Omega}{\cdot}cm$) and maximum carrier concentration ($7.04{\times}10^{20}cm^{-3}$) and hall mobility ($12.70cm^2/Vs$) were obtained in the GZO thin film fabricated at 70W of RF power. The optical transmittance in the visible region was higher than 80 %, regardless of RF power. The optical band-gap showed the slight blue-shift with increased in carrier concentration which can be explained by the Burstein-Moss effect.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.36 no.4
• /
• pp.351-361
• /
• 2023

The purpose of this paper is to help those who research and develop solar cells in university laboratories and industrial sites understand the most basic and important quantum efficiency measurement and analysis method in analyzing solar cell performance. Starting with the definition of quantum efficiency, we calculate the theoretical current density according to the band gap of the solar cell material from the solar spectrum, along with a detailed introduction to the measurement and analysis methods, and measure and analyze the theoretical current density and quantum efficiency. We discuss in depth how to analyze the performance of solar cells through Quantum efficiency measurement and analysis of solar cells is a very useful method that can give intuition to solar cell performance analysis as it can analyze solar cells according to depth (front emitter, bulk, rear surface). Students and researchers who study solar cells with a deep understanding of theoretical current density and quantum efficiency measurement analysis are expected to use it as a basis for analyzing solar cell performance.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.21 no.3
• /
• pp.99-104
• /
• 2011

A stoichiometric mixture of evaporating materials for $MgGa_2Se_4$ single crystal thin films was prepared from horizontal electric furnace. The crystal structure of these compounds has a rhombohedral structure with lattice constants $a_0=3.953\;{\AA}$, $c_0=38.890\;{\AA}$. To obtain the single crystal thin films, $MgGa_2Se_4$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the Hot Wall Epitaxy (HWE) system. The source and substrate temperatures were $610^{\circ}C$ and $400^{\circ}C$, respectively. The crystalline structure of the single crystal thin films was investigated by the double crystal X-ray rocking curve and X-ray diffraction ${\omega}-2{\theta}$ scans. The carrier density and mobility of $MgGa_2Se_4$ single crystal thin films measured from Hall effect by van der Pauw method were $6.21{\times}10^{18}\;cm^{-3}$ and 248 $cm^2/v{\cdot}s$ at 293 K, respectively. The optical absorption of $MgGa_2Se_4$ single crystal thin films was investigated in the temperature range from 10 K to 293 K. The temperature dependence of the optical energy gap of the $MgGa_2Se_4$ obtained from the absorption spectra was well described by the Varshni's equation, $E_g(T)=E_g(0)-({\alpha}T^2/T+{\beta})$. The constants of Varshni's equation had the values of $E_g(0)=2.34\;eV$, ${\alpha}=8.81{\times}10^{-4}\;eV/K$ and ${\beta}=251\;K$, respectively.