Search | Korea Science

Do, Young-Woong;Ha, Jin-Wook
- Proceedings of the KAIS Fall Conference
- /
- 2010.05b
- /
- pp.957-960
- /
- 2010
본 연구에서는 중금속 크롬($Cr^{+6}$)이 포함된 흑색안료(Copper Chromite Black)를 공침공정을 이용하여 무독성의 Fe 화합물로 대체한 환경친화적인 블랙(흑색)안료를 개발하였다. 안료제조를 위하여 인체에 무해한 화합물($MnCO_3$, Fe(OH)$_3$, CuO)을 원료로 사용하였으며, 가스소성, Ring-Mill에 의한 습식분쇄 그리고 건조과정을 통하여 흑색안료를 제조하였다. 안료의 평가는 제품의 품질을 결정하는 색상과 착색력을 최우선으로 선정하여 색차계로 고찰하였다. 연구결과, 공침공정으로 제조한 원료를 $950^{\circ}C$에서 12시간 동안 가스소성을 한 후 건조와 분쇄공정(습식)을 거쳐 흑색안료를 제조하였을 때, 최적의 색 선명도, 착색력 및 입도($1{\mu}m$ 이하)를 가진 것으로 나타났다.
PDF

김한근;사공건
- Electrical & Electronic Materials
- /
- v.9 no.9
- /
- pp.906-910
- /
- 1996
Ferroxplana N $i_{2}$Y(B $a_{2}$N $i_{2}$F $e_{12}$ $O_{22}$ ) magnetic particles, which is one of the hexagonal ferrite were synthesized by a coprecipitation method. The coprecipitates were prepared by adding aqueous solution of BaC $I_{2}$ - 2 $H_{2}$O, NiC $I_{2}$ - 6 $H_{2}$O and FeC $I_{3}$ - 6 $H_{2}$O(of which the mole ratio is $Ba^{+2}$ : N $i^{+2}$ : F $e^{3+}$= 1 : 1 : 6) to a mixture of NaOH and N $a_{2}$C $O_{3}$. The shape of Ferroxplana N $i_{2}$Y magnetic particles obtained at 1, 100(.deg. C) was hexagonal plate-like, average particle size and aspect ratio were 2(.mu.m) and 7, respectively.y.
PDF

Moon, Young-Hwan;Ihm, Son-Ki
- Applied Chemistry for Engineering
- /
- v.7 no.5
- /
- pp.913-924
- /
- 1996
In this study HDS(hydrodesulfurization) of thiophene was researched over nickel catalysts added with small amounts of neodymium which were prepared by different methods such as unsupported coprepricipitated NdNi catalysts, unsupported intermetallic $NdNi_5$ catalysts, and carbon supported NdNi catalyst. The HDS activity was remarkably increased when a small amounts of neodymium was added to unsupported coprecipitated Ni catalysts. Thus it was known that the role of Nd is important in HDS of thiophene of Ni catalysts. For the case of unsupported intermetallic $NdNi_5$, the intermetallic crystallinity was destroyed to oxide and sulfide after calcination and presulfidation respectively. The HDS activity of thiophene can be explained by surface area of unsupported catalysts. And Nd acts like as structural promoter keeping the high surface area of unsupported catalysts. The HDS activity was increased by each ten times based on 1 gr. of nickel in the order of unsupported intermetallic $NdNi_5$, unsupported coprecipitated NdNi, and carbon supported NdNi catalysts according to different preparation method of catalysts.