• Journal of the Society of Disaster Information
• /
• v.19 no.2
• /
• pp.280-291
• /
• 2023

Purpose: As fire accidents happen at the production and storage sites of superabsorbent polymers for convenience of daily life, an experimental study was conducted to secure basic data to establish practical preventive measures against them. Method: The sample container (20cm width × 20cm length) was made into a rectangular cuboid with the heights of 3cm, 5cm, 7cm, and 14cm, respectively, to allow access to the infinite flat plane. The front and back of the container were covered with a 300-mesh stainless steel mesh for one-dimensional heat transfer. The sample container was placed in the center of the thermostatic bath, which was heated to a predetermined temperature by setting the thermostat program in advance, and it was determined to be 'ignited' when the central temperature of the sample rose by more than 20℃ above the set temperature, and "unignited" when it was maintained at an approximate value of the set temperature. Result: The critical autoignition temperature was calculated to be 217.5℃ when the height of the sample container was 3 cm, 212.5℃ when it was 5 cm, 202.5℃ when it was 7cm, and 187.5℃ when it was 14cm. The ignition induction time to reach the maximum temperature was 34hours for 3cm, 76hours for 5cm, 143hours for 7cm, and 318hours for 14cm. Conclusion: ① As the size of the container increased, the autoignition temperature decreased and the induction time to reach the maximum temperature increased. ② An apparent activation energy was calculated to be 44.92kcal/mol, with a correlation of 96.93%.

• Journal of the Korean Chemical Society
• /
• v.55 no.1
• /
• pp.98-103
• /
• 2011

This study was done for the preparation of macromolecular material with UV-blocking features by adding the benzophenone group that is commonly used as a UV-absorbent and $TiO_2$ which is known to be a very stable material in chemical and physical aspects. Also, we compared the level of UV absorbency of the polymer produced from polymerization with previous materials and measured basic properties such as water content, refractive index and optical transmittance of produced contact lenses. The results of the measurement showed that the refractive index and water content of the contact lens with added UV-absorbent was 1.430~1.440 and 35.0~45.0% respectively, which was similar to that of previous contact lenses. Also, for optical transmittances of each wave length, contact lenses without the UV-absorbent was 89%, 88% and 89% respectively for UV-A, UV-B and visible light, indicating that the UV transmittance is very high though contrary with cases of contact lenses with added 2-hydroxy-4-methoxy-benzophenone and 2,4-dihydroxy-benzophenone which showed transmittances of 0% and 6% respectively for UV-A and UV-B showing a UV-blocking effect. Meanwhile, contact lenses with added $TiO_2$ showed transmittance of 6% and 51% respectively for UV-A and UV-B also showing a UV-blocking effect. The visible transmittance was 77~89% showing that it satisfies the visible transmittance required for ophthalmological materials.