• Journal of the Korean Magnetics Society
• /
• v.3 no.4
• /
• pp.305-309
• /
• 1993

Thermal stability of Co/Cu artificial superlattice (AS) prepared by RF-magnetron sputtering and the effect of low temperature annealing on the magnetoresistance of the AS have been investigated in this work. Dependence of annealing behavior on the Cu spacer thickness, Fe underlayer thickness, and kind of the underlayer was examined and the relationship between the interfacial reaction and magnetoresistance was studied. It turned out that when Co/Cu AS was annealed at low temperature ($<450^{\circ}C$), the magnetoresistance could increase in the case of AS with thick spacer Cu ($20~25\AA$) layer, whereas it decreased in the case of AS with thin spacer Cu ($7\AA$) layer, which of the former is in contrast with previous reports and the latter in consistent with them. The increase of magnetoresistance is due to increase of interfacial atomic sharpness, which is supported by low angle X-ray diffraction analysis. The thermal stability of Co/Cu AS was better in the case of thick Fe underlayered AS. Interfacial reaction (separation of intermixed Co and Cu) could be observed at lower temperature for (200)-textured samples than for (111)-textured samples, which can be interpreted in terms of interdiffusion kinetics depending on the crystallographic orientation.

• Journal of the Korean Magnetics Society
• /
• v.7 no.5
• /
• pp.243-248
• /
• 1997

The effect of $O_2$ partial pressure on microstructure and soft magnetic properties of as-deposited Fe-Hf-O thin film alloys, which are produced by rf magnetron sputtering method in $Ar+O_2$ mixed gas atmosphere, are investigated. Saturation magnetization ($4{\pi}M_s$) of Fe-Hf-O film were decreased with increasing $O_2$ partial pressure, the best soft magnetic properties exhibit at $O_2$ partial pressure of 10%. With further increase of $O_2$ partial pressure, soft magnetic properties decreased continuously. The $Fe_{82}Hf_{3.4}O_{14.6}$ film with $P_{O2}=10%$ exhibits good soft magnetic properties with $4{\pi}M_s=17.7kG$, $H_c=0.7Oe$ and ${\mu}_ {eff}$ (1~100 MHz)=2,500, respectively. The addition of O is effective in grain refinement. In case of $P_{O2}=15%$, it is observed that $Fe_3O_4$ compound is formed and high frequency soft magnetic properties are decrease. The electrical resistvity($\rho$) of Fe-Hf-O film is increased with increasing $O_2$ partial pressure. Electrical resistivity of $Fe_{82}Hf_{3.4}O_{14.6}$ film was 5 times higher than that of the film without oxygen. Thus, it is considered that the good magnetic properties of $Fe_{82}Hf_{3.4}O_{14.6}$ film results from decreasing the $\alpha$-Fe grain size by precipitates (Hf and O), high electrical resistivity.

• Journal of Sensor Science and Technology
• /
• v.2 no.1
• /
• pp.101-108
• /
• 1993

$TiO_{2}$/Se : Te heterojunction for color sensor has been fabricated by RF reactive sputtering and thermal evaporation methods onto glass substrate. The optimum deposition condition of $TiO_{2}$ films was such that RF power was 120 W, substrate temperature was $100^{\circ}C$, oxygen concentration was 50%, working pressure was 50 mTorr for the $TiO_{2}$ film thickness of $1000{\AA}$. In this case, the optical transmittance of $TiO_{2}$ film at 550 nm-wavelength was 85%, resistivity was $2{\times}10^9{\Omega}{\cdot}cm$, refractive index was 2.3, and optical bandgap was 3.58 eV. The composition ratio of 0 to Ti by AES analysis was 1.7. When $TiO_{2}$ films were annealed at $400^{\circ}C$ for 30 min. in $O_{2}$ ambient, the optical transmittance of $TiO_{2}$ films at the wavelength range of $300{\sim}580$ nm was improved from 0 to 25%. When Se : Te films were annealed at $190^{\circ}C$ for 1 min., photosensitivity under illumination of 1000 lux was 0.75. The optical bandgap of Se : Te films was 1.7 eV. The structures of Se : Te films were the hexagonal with (100) and (110) orientation. The spectral response of a-Se was improved by the addition of Te, especially in the long wavelength region. The $TiO_{2}$/Se : Te heterojunction showed wide spectral response, and more improved one than that of a-Si film in the blue light region.