• Journal of the Korea institute for structural maintenance and inspection
• /
• v.23 no.1
• /
• pp.45-53
• /
• 2019

Slump flow, compressive strength, flexural strength and drying shrinkage were measured to evaluate workability and mechanical performance of geopolymer. Experimental parameters include the addition of gypsum, blending ratio of blast furnace slag and fly ash and addition of shrinkage reducing agent. Geopolymer using blast furnace slag mixed with gypsum showed larger slump flow than blast furnace slag without gypsum. The slump flow when blending ratio of blast furnace slag and fly ash is 5:5 tended to be larger than the slump flow when blending ratio is 8:2. Geopolymer using blast furnace slag without gypsum showed higher compressive strength and flexural strength than blast furnace slag mixed with gypsum. Compressive strength and flexural strength tended to be higher when blending ratio of blast furnace slag and fly ash was 8:2 than when blending ratio was 5:5. Drying shrinkage decreased with increasing fly ash and blast furnace slag without gypsum, and it was found that shrinkage reducing agent is effective to reduce drying shrinkage of geopolymer.

• Resources Recycling
• /
• v.22 no.6
• /
• pp.12-18
• /
• 2013

In this Study, it was fabricated that shrinkage reducing agent and mortar used $C_{12}A_7$-based slag enhanced the shrinkage reduction and compressive strength. To reduce cement content, setting time, flow and compressive strength of mortar with varying content of fly ash and blast furnace slag were experimented. The flow increased and setting time delayed as the increase of fly ash and blast furnace slag content. And early strength was lower and long age strength was higher than that of mortar with low content of admixture.

• Journal of the Korea Concrete Institute
• /
• v.15 no.6
• /
• pp.785-793
• /
• 2003

This study is intended to analyze the effectiveness of expansive additive, shrinkage reducing agent and combination of the two to reduce the autogenous and drying shrinkage of high performance concrete using mineral admixture such as fly ash, blast furnace slag powder and silica fume. According to results, when expansive additive and shrinkage reducing agent are mixed within an appropriate mixing ratio, fluidity and air content are not influenced, and the enhancement of compressive strength is favorable at the age of 91 and 180days. At the mixing ratio of expansive additive of 5% and 10%, the autogenous and drying shrinkage is reduced by 32∼68% and 25∼49% respectively in comparison with plain concrete. And they are reduced by 18∼34% and 16∼26% respectively at the mixing ratio of shrinkage reducing agent of 0.5% and 1.0%, compared with plain concrete. The mixture of EA-SR combined with expansive additive and shrinkage reducing agent is most effective for reduction of shrinkage. Therefore, it is considered that the using method in combination with expansive additive and shrinkage reducing agent is effective to reduce the shrinkage of high performance concrete using mineral admixture such as fly ash, blast slag powder and silica fume.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.11 no.4
• /
• pp.552-559
• /
• 2023

The purpose of this study is to evaluate the crack reduction performance of blast furnace slag concrete mixed with expansive and swelling admixtures. As a basic performance test, various ingredients such as blast furnace slag fine powder (BFS), calcium sulfoaluminate (CSA), bentonite, and hydroxypropyl methyl cellulose (HPMC) were used, and the results showed that bentonite showed superior performance compared to HPMC. Afterwards, a MOCK-UP test was conducted to evaluate cracking and drying shrinkage according to the mixing ratio. As a result, when bentonite and a small amount of calcium phosphate were added, drying shrinkage was reduced and cracking was reduced. In particular, a cement mixture consisting of 30 % BFS, 1 % bentonite, and 1 % calcium phosphate showed optimal crack-free performance. It is believed that BFS concrete will contribute to compensating for shrinkage through continuous expansion activity and can be used for field applications.

• Journal of the Korea Institute of Building Construction
• /
• v.19 no.2
• /
• pp.123-130
• /
• 2019

As a cold-weather-concrete construction technique for enhancing the sustainability and improving efficiency of cold-weather construction, the cracking timing, the starting point of deterioration for concrete, due to the shrinkage of the blast furnace slag cement concrete including accelerator was evaluated. As a result, by using blast furnace slag and accelerator, the cracking was developed faster with higher cracking potential under the restrained conditions at constant age and free-shrinkage strain. It can be considered that the results of decreased stress relaxation by creep or increased restraint with increased free-shrinkage strain causes the increased cracking development speed. Hence, it should be considered the necessary of cracking due to the shrinkage when blast furnace slag or accelerator was used for cold-weather construction.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2016.10a
• /
• pp.32-33
• /
• 2016

This purpose of this study is to find the properties of pore structure and length change of blast furnace slag cement added alkali powder stimulant on shrinkage reducing agent presence. In length change, the specimen added alkaline stimulant was smaller than normal blast furnace slag concrete. And the specimen added shrinkage reduction agent was confirmed to show smaller rate of length change than the length. In MIP analysis of 1day-age, 0.1㎛ subsequent pore amount of the specimen added alkaline stimulant was significantly smaller value the normal blast furnace slag concrete specimen.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.17 no.6
• /
• pp.693-699
• /
• 2016

In this study, the replacement effects of cementitious materials (fly ash, blast furnace slag, and blended mixtures) were assessed for normal strength concrete with very low shrinkage properties under $350{\mu}{\varepsilon}$ strain using a powder type shrinkage reducing agent. In addition, through mock-up tests of actual size walls restrained with four sides, the shrinkage characteristics using the power type shrinkage reducing agent were measured and the crack reducing ability was assessed. The slump and air contents were measured as the properties of fresh concrete, and the length changes of the prismatic specimens, $100{\times}100{\times}400mm$ in size, were measured for the shrinkage characteristics. To reduce the shrinkage of concrete, the maximum replacing ratio of the fly ash is effective to 20 percent; however, the use of blast furnace slag and ternary mixtures did not reduce the shrinkage.

• Journal of the Korea Concrete Institute
• /
• v.16 no.5 s.83
• /
• pp.621-626
• /
• 2004

The use of blast-furnace slag (BFS) in making not only normal concrete but also high-performance concrete has several advantages with respect to workability, long-term strength and durability. However, slag concrete tends to show more shrinkage than normal concrete, especially autogenous shrinkage. High autogenous shrinkage would result in severe cracking if they are not controlled properly. Therefore, in order to minimize the shrinkage stress and to ensure the service life of concrete structures, the autogenous shrinkage behavior of concrete containing BFS should be understood. In this study, small prisms made of concrete with water-binder (cement+BFS) ratio (W/B) ranging from 0.27 to 0.42 and BFS replacement level of $0\%$, $30\%$, and $50\%$, were prepared to measure the autogenous shrinkage. Based on the test results, thereafter, material constants in autogenous shrinkage prediction model were determined. In particular, an effective autogenous shrinkage defined as the shrinkage that contributes to the stress development was introduced. Moreover, an estimation formula of the 28-day effective autogenous shrinkage was proposed by considering various W/B's. Test results showed that autogenous shrinkage increased with replacement level of BFS at the same W/B. Interestingly, the increase of autogenous shrinkage is dependent on the W/B at the same content of BFS; the lower W/B, the smaller increasing rate. In concluding, it is necessary to use the combination of other mineral admixtures such as shrinkage reducing admixture or to perform sufficient moisture curing on the construction site in order to reduce the autogenous shrinkage of BFS concrete.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.1101-1104
• /
• 2008

Recently, active researches are conducted on high performance concrete(HPC) exhibiting high strength and high fluidity. These researches are resulting in increased applications on real structures. In order to satisfy the required performances, HPC makes use of large quantities of binder and presents low water-cementitious material ratio. Such mixing is increasing significantly the autogenous shrinkage, which subsequently is likely to favor the potential development of cracks. Therefore, we investigated the effect of used materials and mix proportions on the shrinkage properties of HPC, and of the use of expansive additives and shrinkage reducing agents on the HPC. The autogenous shrinkage of HPC using blast furnace slag are tend to be increased, in some case have the potential development of cracks by only the autogenous shrinkage. Also the using method in combination with expansive additive and shrinkage reducing agent is more effective than the separately using method of that.

• Resources Recycling
• /
• v.23 no.4
• /
• pp.37-46
• /
• 2014

Carbon dioxide generated from construction materials and construction material industry among the fields of construction is approximately 67 million tons. It is about 30% of the carbon dioxide generated in the fields of construction. In order to reduce carbon dioxide in the fields of construction, it is necessary to control the use of fossil fuel consumed and decrease carbon emission by reducing the secondary and tertiary curing generating carbon dioxide in construction material industry. Therefore, this study manufactured mortar by having cement as the Plain and substituting three binding materials up to 50% and then adopted different curing methods to analyze congelation and strength characteristics. Test results for strength property by changing binding materials showed that specimens with blast furnace slag, CSA 15% and CAMC 5% resulted in positive effect for strength.