• Restorative Dentistry and Endodontics
• /
• v.36 no.2
• /
• pp.132-138
• /
• 2011

Objectives: The purpose of this study was to evaluate curing degree of three dual-cure resin cements with the elapsed time in self-cure and dual-cure mode by means of the repeated measure of micro-hardness. Materials and Methods: Two dual-cure self-adhesive resin cements studied were Maxcem Elite (Kerr), Rely-X Unicem (3M ESPE) and one conventional dual-cure resin cement was Rely-X ARC resin cement (3M ESPE). Twenty specimens for each cements were made in Teflon mould and divided equally by self-cure and dual-cure mode and left in dark, $36^{\circ}C$, 100% relative humidity conditional-micro-hardness was measured at 10 min, 30 min, 1 hr, 3 hr, 6 hr, 12 hr and 24 hr after baseline. The results of micro-hardness value were statistically analyzed using independent samples t-test and one-way ANOVA with multiple comparisons using Scheffe's test. Results: The micro-hardness values were increased with time in every test groups. Dual-cure mode obtained higher micro-hardness value than self-cure mode except after one hour of Maxcem. Self-cured Rely-X Unicem showed lowest value and dual-cured Rely-X Unicem showed highest value in every measuring time. Conclusions: Sufficient light curing to dual-cure resin cements should provided for achieve maximum curing.

• Journal of the Korean earth science society
• /
• v.25 no.2
• /
• pp.87-93
• /
• 2004

To study the effect of cloud on the variabilities of turbulent fluxes over the flat terrain, we used the gradient method to analyze the dynamic and thermodynamic data from the meteorological 9-m mast (0.75, 3 and 9 m) in Villafria airport in Spain. The decrease of the surface wind speed is governed by cooling at the surface following the evening transition. The sensible heat flux and the momentum flux are increased with the dynamic factor rather than the thermodynamic factor, and the sensible heat flux was not affected by the thermal condition. The global radiation did not play an important role in the variation of the sensible heat flux in the cloudy day, but the atmospheric surface layer was characterized rather by the wind intensity.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1988.06a
• /
• pp.43-48
• /
• 1988

보호피막을 입히는 방법으로는 화학증착법과 물리증착법이 주로 사용되고 있다. 고온 분위기에서 기체 상태인 반응물의 화학반응을 통하여 원하는 물질을 증착시키는 화학증착법은 물리증착법에 비해 점착성(adhesion)이 우수하고, 보호피막층의 성분조절이 용이하며, 반응물이 기체상태이므로 대량생산이 용이하여 보호피막 증착법으로 많이 사용되고 있다. $Si_3N_4$-TiC ceramic 표면에 TiC, TiN 및 Ti(C, N) coating을 함으로써 얻을 수 잇는 장점들은 표면층의 경도를 증가시키며, steel과의 마찰계수의 감소 및 coating 층 자체가 고온에서 고체 윤활제로 작용하여 마찰열의 상당한 감소를 얻을 수 있으며, 또한 coating층 자체가 비교적 안정한 화합물로 피삭재내의 성분원소들에 대한 diffusion barrier로 작용되며, 내식성을 증가시킬 수 있다. 본 연구에서는 각 증착층의 미소경도, 열충격저항, steel과의 마찰계수를 측정하였으며, 최종적으로 절삭시험을 통하여 증착층들의 내마모성을 조사, 규명하였다.

• Proceedings of the KAIS Fall Conference
• /
• 2011.12b
• /
• pp.646-648
• /
• 2011

본 논문에서는 쌍롤 박판주조(Twin Roll Casting, TRC)법을 이용하여 AA4343 합금을 제작하였다. 주조시 롤 간격을 조절하여 냉각속도를 달리하였으며 인고트 주조(Ingot Casting, IC)법을 이용하여 제조된 합금과의 미세조직학적 차이와 이에 따른 물성 변화를 고찰하였다. TRC 및 IC로 제조된 합금을 냉간압연하였으며 압연 건전성을 평가하였다. 한편, 냉각속도별로 상이한 미세조직을 구현할 수 있는 스텝몰드(Step Mold Casting, SMC)법을 이용하여 제조된 합금의 냉각속도에 따른 미세조직 및 경도 차이를 조사하여 상대 비교하였다. 냉각속도가 빠를수록 주조 셀조직의 크기 및 공정 Si 입자의 크기가 감소하였으며 이로 인하여 경도가 증가되는 효과를 나타내었다. 주조시 생성된 공정 Si 입자의 크기는 압연에 의하여 그 크기의 변화가 거의 없었으며 열분석 결과 액상선 온도의 변화가 일부 발생하나 큰 차이가 없었다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2013.05a
• /
• pp.192-192
• /
• 2013

하이브리드 표면처리는 다른 표면처리법을 동시 또는 연속적으로 행하여 단일표면처리에 비해 더욱 우수한 특성을 부여시키기 위한 표면처리법이다. 본 연구는 붕소와 질소 원소를 이용한 하이브리드 표면처리를 오스테나이트계 스테인리스강인 STS 316L 소재에 적용하여 변화된 특성을 평가하였다. 본 실험에 사용된 하이브리드 표면처리법으로는 붕소분말을 이용한 보로나이징처리와 활성스크린을 이용한 이온질화처리법을 적용하였다. 하이브리드 표면처리된 STS 316L시편은 FE-SEM을 이용하여 표면형상 및 단면조직을 관찰하였으며 GDS와 XRD를 이용하여 깊이에 따른 원소 및 상분석을 실시하였다. 또한 마이크로비커스 경도계와 마모시험기를 이용하여 경도와 마모특성을 측정하였고, 염수분무시험을 통하여 해수환경에서 부식거동을 평가하였다.

• Korean Journal of Optics and Photonics
• /
• v.34 no.5
• /
• pp.185-191
• /
• 2023

We report the results of evaluating the hardness, flexibility, and adhesion between the protective layer and the stealth sheet after applying a protective layer to improve the practicality of the flexible stealth sheet. The result of the ISO 15184 pencil hardness test showed that the hardness increased from HB to 3H by three grades when a protective layer was applied. The flexibility evaluation was conducted by bending the material against cylinders of certain diameters and observing whether cracks occurred according to the ASTM D522 test method. The result showed that the minimum diameter was 0.125 inches. The adhesion was evaluated by using the ASTM D3359 test method, attaching and peeling off an adhesive strip to the protective layer and determining the proportion of the protective layer peeling off. The result was 5B, which is better than the military adhesion limit of 4B.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2001.11a
• /
• pp.28-28
• /
• 2001

$TiCl_44,{\;}AICl_3,{\;}H_2,{\;}Ar,{\;}NH_3$ 기체를 사용하여 플라즈마 화학 증착법으로 $(Ti_{1-x}AI_x)N$ 피막을 증착한 후 진공열처리 실험을 통해 열처리 전후에 나타나는 피막의 가계적 특성 변화 및 상변화 양상에 대해 연구하였다. 기판으로는 M2 고속도강과 알루미나(${\alpha}-Al_2O_3$)를 사용하였으며, 열처리 실험은 진공 열처리로를 이용하여 $800$ ~ $1100^{\circ}C$ 에서 진행하였다. M2 고속도강 위에 증착한 $(Ti_{1-x}AI_x)N$ 피막은 모두 (200) 우선 방위를 갖고 있었으며, AI의 함량이 높아짐에 따라 입자의 크기가 미세해져 $(Ti_{0.2}AI_{0.8})N$ 의 경우 수 nm의 업자들로 이루어져 있었다. 열처리 시간을 일정하게 하고, 그 온도를 증가시킬 경우 비교적 낮은 온도 영역($~900^{\circ}C$)에서는 경도 증가를 나타내지만, 열처리가 더욱 진행됨에 따라 다시 경도가 감소하는 양상을 나타내었으며, 열처리 온도를 일정하게 하고 열처리 시간을 변화 시킬 경우에도 초기에 경도가 증가하다가 열처리가 진행됨에 따라 경도가 다시 감소하는 현상을 관찰 하였다. 이때 경도증가 정도는 Al 함량이 높을 수록 뚜렷하고 오래 지속되었으며, $(Ti_{0.2}AI_{0.8})N$ 피막의 경우 열처리 전 $2000HK_{0.01}$에서 열처리 후 $4500HK_{0.01}$로, 매우 큰 경도 증가를 나타내었다. 이와 같은 열처리 전후의 기계적 특성 변화는 준 안정상의 $(Ti_{1-x}AI_{x})N$ 피막에서, 열처리가 진행됨에 따라 미세한 AlN 업자가 석출되면서 나타나는 현상으로, 고분해능 전자현미경(HRTEM) 분석을 통해 경도가 증가한 시편의 경우 석출상의 크기가 5nm 이하로 매우 작고 대체로 기지와 연속적인 계면을 형성하나, 열처리가 진행될수록 석 출상의 크기가 커지고 임계크기 이상에 이르면 연속적인 계면은 거의 발견되지 않고, 대부 분 불연속적이고 확연한 계면을 형성함을 관찰 할 수 있었다. 알루미나(${\alpha}-Al_2O_3$) 기판 위에 증착한 $(Ti_{1-x}AI_{x})N$ 피막은 마찬가지로 (200) 우선 방위를 나타내었으나, 그 입자의 크기가 수십 nm로 고속도강위에 증착한 피막에 비해 상당히 크게 형성되었다. 또한 열처리 후에 AIN의 석출이 진행됨에도 불구하고 경도 증가는 나타나지 않고, 열처리가 진행됨에 따라 경도가 감소하는 양상만을 나타내었다. 결국 $(Ti_{1-x}AI_{x})N$ 피막이 열처리 전후에 보아는 기계적 특성의 변화 양상은 열역학적으로 안정한 Wurzite-AlN의 석출에 따른 것으로 AlN 석출상의 크기에 의존하며, 또한 이러한 영향은 $(Ti_{1-x}AI_{x})N$ 피막에 존재하는 AI의 함량이 높고, 초기에 증착된 막의 업자 크기가 작을 수록 클 것으로 여겨진다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2013.05a
• /
• pp.125-125
• /
• 2013

기계부품 및 자동차부품 등의 내마모나 내피로성의 향상을 위한 표면처리로서 고주파처리, 침탄처리, 질화처리 등이 사용되고 있다. 최근에는 변형을 최소화 함으로써 후가공을 생략할 수 있는 질화처리가 주목받고 있다. 질화처리종류로는 염욕질화나 가스질화법이 사용되고 있으나, 이들에 비해 환경오염 및 공해가 적고 인체에 무해한 플라즈마 연질화법이 사용되고 있다. 플라즈마 연질화 기술은 IT기기의 제품에 적용되는 표면경화의 공정개발은 미비한 실정이다. 마이크로 구동 요소 부품중의 하나인 Leadscrew는 이송장치를 구성하는 핵심 부품으로 IT기기의 정밀 이송 및 구동제어에 사용되는 핵심 부품으로 사용되고 있으며, 리드스크류의 소재인 SWCH1018A(냉간압조용강선)은 표면 경도가 낮고 변형이 쉽기 때문에 표면 경화를 위한 플라즈마 연질화 기술을 이용하고자 했다. 본 연구는 플라즈마 연질화 공정을 적용한 시편의 표면경도를 높혀주고 변형을 최소화 할 수 있는 공정을 확인하는 것이다. 공정변수를 변화 시키면서 얻어진 시편의 표면미세 구조를 미소경도측정, XRD, SEM분석을 통하여 확인하였으며, 이를 통해 시편 표면경도를 높여주는 공정 조건을 도출하였다.

• Korean Journal of Materials Research
• /
• v.7 no.6
• /
• pp.464-471
• /
• 1997

Melt-overflow 급냉응고장치를 이용하여 두께 약 300$\mu\textrm{m}$, 폭 10mm의 Mg-Zn합급 스트립을 연속적으로 제조하였다. 또한 알루미늄을 첨가하여, 첨가원소에 따른 결정립미세화와 기계적강도에 미치는 영향을 조사하였다. 스트립의 미세응고조직은 전자현미경(TEM, SEM)과 image analyzer를 이용하여 분석하였으며, 경도시험으로 기계적특성을 평가하였다. Mg-5wt%Zn합금 스트립의 경도는 결정립크기의 제곱근에 반비례하여 급냉응고에 의한 결정립미세화 효과로 같은 조성의 일반주조 합금보다 2배 이상의 높은 경도값을 가지며, 알루미늄을 첨가함으로서 2배 정도의 결정립미세화 효과를 얻어 경도가 더욱 증가하였다. 결정입계를 따라 생성된 금속간화합물은 마그네슘화합금의 입계부식을 방지하여 우수한 내식성을 갖는다. 따라서 적절한 합금설계와 급냉응고법을 적용시키면 마그네슘합금의 취약성을 보완하며 경량성의 장점을 최대한 활용할 수 있다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.05a
• /
• pp.187-188
• /
• 2012

본 연구에서는 자동차 연료분사 장치의 내마모성 및 내구성 개선을 목적으로 이온빔 증착법을 이용하여 DLC 코팅을 증착하고 특성을 평가하였다. 특히 $CH_4/C_2H_2$ 분압비에 따라 DLC 박막의 표면조도, 밀착력, 경도등에 미치는 영향을 조사하였으며 DLC 박막의 구조 변화를 관찰하였다. 제조된 박막의 표면조도는 AFM (Atomic Force Microscopy)을 이용하였으며 박막의 밀착력은 스크래치 시험기를 이용하였고 미소 경도는 나노 인덴테이션을 이용하였으며 구조분석은 Raman spectroscopy를 이용하였다. 표면조도 결과 $C_2H_2$ 주입량을 증가함에 따라 표면조도와 경도값은 급격하게 증가하였고 $C_2H_2$만 주입했을 경우 Ra값이 90 nm, 미소 경도값은 2291 Hv로 최대값을 나타내었다.