• Journal of the Korean Magnetics Society
• /
• v.6 no.3
• /
• pp.165-169
• /
• 1996

The relationship between grain size and number of magnetic domain walls for tertiary recrystallized ultra thin 3 % Si-Fe strips was investigated. It was found that the strips with different grain size can be produced by controlling the inserting speed of sample in annealing furnace. Though grain size of the stirip became smaller than 1mm, $B_{8}$ of high value above 1.95T was obtained. But $H_{c}$ increased with decaying the grain size. The magnetic domains and losses of the ultra thin grain oriented silicon steel with smaller grian size were observed. The eddy current losses of the strips were decreased with decreasing the grain size in high frequency range because strips with smaller grain have narrower magnetic domain wall spacings. But Hysteresis losses of the strips with smaller grain have high value in low frequency range. Therefore the iron loss of ultra thin grain oriented silicon steel could be controlled by the grain size. It was clarified that the minumum tatal loses depended on the exciting frequency and grain size.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2014.11a
• /
• pp.132-133
• /
• 2014

구리도금 및 적절한 어닐링 공정을 통해 수nm 크기의 초기 도금 미세조직과 수${\mu}m$정도의 결정립 크기를 갖는 재결정이 진행된 결정립이 병존하는 도금막 샘플을 제작하였다. 전기 비저항 측정과 EBSD를 통해 결정립 성장 분율을 측정하였으며 다양한 사이즈와 결정 방향을 갖는 결정립에 대해 질산용액을 이용하여 화학적 에칭방법을 통해 간접적으로 각 구리원자의 화학적 안정성을 평가할 수 있었다. 결과적으로 결정립이 클수록 에칭속도가 느린 것을 확인하였으며, 주요 원인으로 결정립계면이 우선적으로 에칭되는 것이 관찰되었다. 즉, 결정립의 크기가 작을수록 결정립계면의 비율이 커서 에칭속도가 증가하고 Nanosize의 초기 결정립이 빨리 에칭되는 것이 확인되었다.

• 기계와재료
• /
• v.23 no.3
• /
• pp.82-95
• /
• 2011

다결정압연판재는 열가공공정을 거쳐서 생산되므로 공정의 특성을 반영하는 미세조직/집합조직 특성을 가지게 된다. 결정립들은 특정방향으로 배향하고 결정립의 형상과 크기도 변화한다. 이러한 변화는 거시적으로 다결정판재의 이방성으로 귀결이 되는데, 근본적으로 판재를 구성하는 단결정들의 기계적 물성이 각각의 방향별로 이방성을 띄기 때문이다. 본 자료에서는 압연공정시 다결정판재의 수직/평면이방성의 발생원인을 집합조직과 결정소성학을 이용하여 제시하고자 하였다.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.40 no.7
• /
• pp.653-658
• /
• 2016

High pressure components of a gas turbine engine are generally made of nickel-base superalloys, using precision casting process due to complicated geometries with intricate channels and cooling holes. Turbine components manufactured from directionally solidified and single crystal materials have columnar grains; however, it is found that the crystals do not grow in its preferred direction, although the orientation can be controlled. This anisotropy can lead to the variations of elastic and Hill's parameters in constitutive equations, and they alter stress distributions and the low cycle fatigue life. We aims to evaluate the effects of perturbed crystal orientations on the structural integrity of a directionally solidified nozzle using low cycle fatigue life. We also attempt to show the necessity for the control of allowed manufacturing errors and stochastic analysis. Our approaches included conjugate heat transfer and structural analysis, along with low cycle fatigue life assessment.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.10 no.2
• /
• pp.152-158
• /
• 2000

The crystallographic grain orientation of {{{{ { ZrB}_{2 } }}}}-ZrC composite sintered by pressureless a sintering(PLS) and spark plasma sintering (SPS) was analysed by the SEM-EBSP technique. In the case of PLS, (160) plane of {{{{ { ZrB}_{2 } }}}} was oriented to ND direction, (101) and (111) plane of ZrC were oriented to ND direction. In the case of SPS, (0001) plane of {{{{ { ZrB}_{2 } }}}} was strongly oriented to ND direction. Only (001) plane of ZrC was oriented to ND direction. The PLS specimen had weakly oriented grain structure and interface between {{{{ { ZrB}_{2 } }}}} and ZrC was found to be more stable than that of SPS but the SPS specimen had a preferentially oriented grain structure.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.03a
• /
• pp.144-144
• /
• 2003

니켈계 내열합금의 성형은 수백 $^{\circ}C$에 이르는 고온에서 이루어지기 때문에 열간성형 과정에서 소재 내부의 미세조직 변화에 대한 이해는 부품의 특성 제어 측면에서 매우 중요하다. 특히 열간 동적 재결정에 의해 발생되는 결정립 구조의 변화를 적절히 조절함으로써 부품의 특성을 극대화 할 수 있다. 본 연구에서는 Ni-Fe계 초내열합금에 대한 고온 압축실험과 압축시편에 대한 EBSD 분석을 통해 열간 변형 과정에서 발생하는 소재 내부의 동적인 결정립 구조의 변화를 정량적으로 분석하고자 하였다. 고온 압축시험은 101$0^{\circ}C$, 1066$^{\circ}C$의 온도 조건과 0.5s-1, 0.005s-1의 변형율 속도 조건에서 최대 진변형율 0.7까지 수행하였으며 진변형율에 따른 결정립 조직 변화를 관찰하기 위해 진변형 율에도 변화를 주어 실험을 수행하였다. 이들 고온 압축시편은 응력방향에 평행한 면에 대한 미세조직 관찰을 통해 재결정립 크기, 분율 및 결정립계의 특성 변화에 대한 정량적 연구를 수행하였다.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.1 no.2
• /
• pp.15-22
• /
• 1991

When $YBa_2Cu_3Ox$ is liquid-phase sintered at $925^{\circ}C$ in $O_2$ for 16h, liquid pockets are entrapped within the grains. The liquid pockets show a thin parallelepiped shape with short edge lengths in the c axis, even after reannealing $925^{\circ}C$ in $O_2$ for 16h. All grains in contact with the liquid matrix show the same shape. However, when liquid-phase sintered at 925^{circ}C in $N_2$ for 16h, the grains dispersed in the liquid matrix show a thicker parallelepiped shape than in $O_2$, and their shape remains intact even after reannealing at $925^{\circ}C$ in $N_2$ for 16h. The effect of atmosphere on the grain shape is expected to be due to the variation of oxygen vacancy concentraion in $CuO_2$ plane of tetragonal unit cell.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.08a
• /
• pp.427-427
• /
• 2012

Cu(In,Ga)$Se_2 $ (CIGS) 박막 태양전지는 높은 효율과 낮은 생산 단가로 인해 많은 연구가 이루어지고 있다. 특히, Se flux는 박막의 특성에 가장 중요한 CIGS의 결정성, 결정립 크기, 결정방향을 형성하는데 영향을 주는 것으로 알려져 있다. 일반적인 co-evaporation에 사용되는 Se effusion cell의 경우, 높은 분자가를 가지는 Se 분자들이 공급되기 때문에 낮은 반응성을 보이지만 Se cracker cell을 사용할 경우 Se 분자들이 열적으로 크래킹되어 낮은 분자가를 가지므로 화학적으로 높은 반응성을 가진다. 따라서 적은 양의 Se으로도 양질의 CIGS 박막 제작이 가능하다. 본 연구에서는 Se effusion cell과 cracker cell을 이용하여 CIGS 광흡수층을 제작하였으며, 각각 제작된 CIGS 박막의 특성을 비교하였다. 또한 Se cracker cell의 reservoir zone(R-zone) 온도를 통해 Se flux를 변화시켜 Se flux에 따른 CIGS 박막 태양전지의 특성에 대해 알아보았다. SEM, EDS, XRD 측정을 통해 박막의 특성을 분석하였고, J-V 측정을 통해 태양전지의 특성에 대해 알아보았다. Se cracker를 사용하여 제작된 CIGS 박막의 결정립 크기가 effusion cell로 제작된 박막보다 더 크게 나타났고, Se flux가 증가할수록 결정립의 크기는 증가하였다. Se cracker의 flux가 $0.17{\'{{\AA}}}$/s일 때 반사방지막 없이 13.14%의 효율을 나타내었다.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2002.04b
• /
• pp.45-45
• /
• 2002

나노미터 크기의 결정립을 가지는 나노분말 및 나노복합분말의 제조와 특성에 관한 연구가 매우 활발하다. 나노복합분말의 제조방법에는 기상증발후 응축법, 화학응축법, 기계적합금법 등이 있으나, 고순도 및 균일한 크기분포의 분말과 응집되지 않은 분말의 제조 조건을 가장 잘 만족하는 방법은 화학기상응축법(Chemical Vapor Condensation; CVC)이다. 본 연구그룹 에서는 CVC밤법으로 이용하여 공구/금형재료에 가장 많이 사용되는 WC/Co 합금의 결정립을 n nm크기로 극미세화고자하는 연구을 진행하고 있다. 본 연구에서는 이들 WC/Co합금제조시 가장 중요한 출발분말인 나노크기 WC 분말의 제조와 그 특성에 관하여 연구하고자 하였다. 나노미터 WC분말을 제조하기 의한 전구체는 고상의 금속유기물인Tungstenhexacarbonyl$(W(CO)_6)$ 을 사용하였다. 수평관상로을 반응기로 사용하였으며, 노내의 온도을 500-110$0^{\circ}C$로 변화시 키면서 WC 분말을 합성하였다. 반응기 및 포집기 내부를 대기분위기, 상압의 Ar분위기, 진공 분위기로 변화시켜 압력 및 분위기의 영향을 조사하였다. 포집기는 상온 및 액체질소로 냉각 한 Chiller을 사용하였다. 형성분말의 상분석은 XRD로 조사하였으며, 형태 및 결정립크기는 TEM로 분석하였다. 반응온도 600 -1 OOO$^{\circ}C$의 온도범위에서 검은색의 WC 분말이 제조되었다. XRD 분석의 결과 로 제조된 분말은 상온에서 준안정상인 Hexagonal 구조의 $\gammar-WC_{1-x}$ 상이였으며, TEM 분석결 과 상압하에서는 약 30nm이하의 WC분말이 제조되었으며, 그 형태는 둥근 4각형의 모양을 지녔다. 감압하에서 진행한 경우 결정립의 크기는 8nm이하를 가졌다.곤가스로 산화를 방지하였고, 냉매로는 질소가스를 이용하였다. 제조된 분말을 기ㅖ적 분급법을 이용하여 분급하였고, 냉매로는 질소가스를 이용하였다. 제조된 분말을 기계적 분급ㅂ법을 이용하여 분급하였고, 압출에 이용된 분말은 250$\mu\textrm{m}$이하의 크기를 사용하였다. 또한 분말제조과정 중 형성되는 표면산화층을 제거하기 위하여 36$0^{\circ}C$에서 4시간동안 수소 환원처리를 행하였다. 제조된 분말은 열간 압출을 위하여 Aㅣcan에 넣고 냉간성형체를 만들고, 진공처리를 한 후 밀봉하여 탈가스처리를 하였다. 압출다이는 압출비가 각각 28:1과 16:1인 평다이(9$0^{\circ}C$)를 사용하여 각각 내경이 9, 12cm이고, 길이가 50, 30cm인 압출재를 제조하였다. 열간압출한 후의 미세조직을 광학현미경으로 압출방향에 평행한 방향과 수직방향으로 관찰하였고, 열간 압출재 이방성을 검토하기 위하여 X선 회절분석을 실실하여 결정방위를 확인하였다. 전기 비저항 및 Seebeck 계수 측정을 위하여 각각 2$\times$2$\times$10$mm^3$ 그리고 5$\times$5$\times$10TEX>$mm^3$ 크기의 시편을 준비하였다.준비하였다.전류를 구성하는 주요 입자의 에너지 영역(75~l13keV)에서 가장 높은(0.80) 상관계수를 기록했다. 넷째, 회복기 중에 일어나는 입자들의 유입은 자기폭풍의 지속시간을 연장시키는 경향을 보이며 큰 자기폭풍일수록 현저했다. 주상에서 관측된 이러한 특성은 서브스톰 확장기 활동이 자기폭풍의 발달과 밀접한 관계가 있음을 시사한다.se that were all low in two aspects, named "the Nonsign

• Electrical & Electronic Materials
• /
• v.6 no.5
• /
• pp.446-453
• /
• 1993

초기충진압력이 서로 다른 시편에 가한 가압횟수와 열처리시간의 혼합공정이 임계전류밀도 특성에 미치는 영향을 관찰하기 위하여 power-in-tube방법으로 초전도 선재를 제조하였다. 일정 초기충진압력에서 테이프화를 위한 열처리 및 가압이 혼합공정횟수가 증가할수록 임계전류밀도가 증가하였다. 초기충진압력이 1000kg/$cm^{2}$에서 Bi-2223 고온상 체적비가 가장 높게 나타났고 결정립이 판상으로 성장되었을 뿐만 아니라 C축과 직각방향으로 잘 배양되어 있음을 관찰할 수 있었다. 특히 초기충진압력 1000kg/$cm^{2}$의 시편을 두께를 줄이기 위하여 3회 가압하고 450시간 열처리하였을때 임계전류밀도가 5800A/$cm^{2}$를 나타내었으며 이를 중심으로 500, 2500kg/$cm^{2}$이 양측단으로 가우시안분포를 보였다. 결론적으로 시편의 임계특성은 적정 초기충진압력, Bi-2223 고온상 체적비, 테이프화를 위한 가압횟수, 결정의 일방향배열, 결정립의 성장등에 강하게 의존함을 알 수 있었다.