• Korean Journal of Materials Research
• /
• v.10 no.1
• /
• pp.55-61
• /
• 2000

The sintering characteristics of PVA-Al(III) complex added $UO_2$ pellet and AlOOH added $UO_2$pellet were compared. The major phase of PVA-Al(III) complex and AlOOH decomposed at $1000^{\circ}C$ in $H_2$atmosphere was $\theta-Al_2O_3$. Compared with the apparent density of pure $UO_2$, that of AlOOH added $UO_2$ powder was higher but that of PVA-Al(III) complex was lower. the densification of AlOOH added $UO_2$ pellet was initiated at about $800^{\circ}C$, the densification of PVA-Al(III) complex added $UO_2$ pellet was initiated at about $900^{\circ}C$ respectively. In a view of pore size distribution, the PVA-Al(III) complex added $UO_2$ pellet appeared as monomodal type, whereas the AlOOH added $UO_2$ pellet appeared as bimodal type. The grain size of AlOOH added $UO_2$ pellet was about $13\mu\textrm{m}$ but the grain size of PVA-Al(III) complex added $UO_2$ pellet was increased up to about $36\mu\textrm{m}$.

• Journal of the Microelectronics and Packaging Society
• /
• v.7 no.3
• /
• pp.45-54
• /
• 2000

The effect of electropolishing far stamped leadframe on the removal of the edge burr and residual stress relief was examined. The present study showed that the electropolishing could be used for enhanced surface quality of stamped leadframes. The electropolishing was performed at the condition of 60% phosphoric acid electrolyte, 5 ampere of current and 3 cm electrode gap at $70^{\circ}C$ for 2 minutes for Alloy42 type leadframe, and $50^{\circ}C$ for 1.5 minutes for C-194 type leadframe. The FWHM values from X-ray diffraction showed that residual stress of electropolished leadframe recovered to the level of as-received raw materials and surface roughness measured by using AFM tuned out to be improved by 0.079 $\mu\textrm{m}$ and 0.014 $\mu\textrm{m}$ ($R_{rms}$) far alloy 42 and C-194 type leadframes, respectively. The plated thickness using XRF showed the improved uniformity in thickness variation by 0.4~0.5 $\mu\textrm{m}$ and grain growth, which is favorable for interface adhesion, was also observed from the bake test samples. We could certify dimensional stability of leadframe with inspection by means of 3D-topography and hardness measurements.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1997.10a
• /
• pp.335-341
• /
• 1997

운전중 노심의 출력변화를 감시하는 노외계측기(Excore Detector)는 노내계측기(Incore Detector)를 통하여 측정되어진 축방향 출력편차(Axial Offset)를 이용하여 교정되고 있다. 노외 계측기의 전류와 축방향출력편차의 선형적인 관계를 가정하여 노내계측기로 최소한 4회 노심출력을 측정한후 최소자승법(Least Square Method)으로 비례상수들을 구하는 기존의 방법을 대신하여, 단순 노외계측기 교정법은 노내계측기로 1회 측정되어진 자료들을 이용하여 계측기 반응상수(Detector Response Factor)를 계산한 후 비례상수를 계산한다. 계측기반응상수는 2차원 중성자수송모델로부터 계산된 weighting factor와 3차원 확산이론으로부터 구한 노심출력을 이용하여 계산된다. 중성자수송계산은 (R-Z)와 (R-$ heta$)모델을 합성하여 3차원 weighting factor를 계산하므로 축방향 영향뿐만 아니라 집합체별 영향을 고려하였다. 또한 노심의 복잡한 구조로 인하여 근사적인 weighting (actor와 노심출력분포의 사용은 노외계측기의 전류와 계측기반응율의 불일치를 초래하며, 이를 해결하는 상수를 소개하여 보다 정확한 교정결과를 얻도록하였다. 이와 같은 방법을 고리 3호기 9, 10주기 전주기와 11주기초에 적용하여 노심의 연소분포, 냉각수의 온도분포, 노심의 연소도, 노심출력준위등에 대한 단순 노외계측기 교정법의 오차를 분석하여 최적의 노외계측기 교정모델을 제시하였다. 2차원 중성자수송모델 합성법에 의한 단순노외계측기 교정법은 2차원 (R-Z) 중성자수송모델보다 개선된 결과와 평균오차 0.179% 최대 오차 0.624%를 보여주고 있다.하면 조사 후의 조직안정성에도 크게 기여할 것으로 기대된다.EX>O가 각각 첨가된 경우, Ar-4vol.%H$_2$ 분위기보다 H$_2$분위기에서 소결했을 때 밀도가 더 높았다. 그러나, 결정립은 $UO_2$와 $UO_2$-Li$_2$O의 경우, 수소분위기에서 소결했을 때, (U,Ce)O$_2$와 (U,Ce)O$_2$-Li$_2$O에서는 Ar-4vol.%H$_2$분위기에서 소결했을 때 더욱 성장하였다.설명해 줄 수 있다. 넷째, 불규칙적이며 종잡기 힘들고 단편적인 것으로만 보이던 중간언어도 일정한 체계 속에서 변화한다는 사실을 알 수 있다. 다섯째, 종전의 오류 분석에서는 지나치게 모국어의 영향만 강조하고 다른 요인들에 대해서는 다분히 추상적인 언급으로 끝났지만 이 분석을 통 해서 배경어, 목표어, 특히 중간규칙의 역할이 괄목할 만한 것임을 가시적으로 관찰할 수 있 다. 이와 같은 오류분석 방법은 학습자의 모국어 및 관련 외국어의 음운규칙만 알면 어느 학습대상 외국어에라도 적용할 수 있는 보편성을 지니는 것으로 사료된다.없다. 그렇다면 겹의문사를 [-wh]의리를 지 닌 의문사의 병렬로 분석할 수 없다. 예를 들어 누구누구를 [주구-이-ν가] [누구누구-이- ν가]로부터 생성되었다고 볼 수 없다. 그러므로 [-wh] 겹의문사는 복수 의미를 지닐 수 없 다. 그러면 단수 의미는 어떻게 생성되는가\ulcorner 본 논문에서는 표면적 형태에도 불구하고 [-wh]의미의 겹의문사는 병렬적 관계의 합성어가 아니라 내부구조를 지

• Journal of the Korean Ceramic Society
• /
• v.36 no.1
• /
• pp.43-49
• /
• 1999

Gas pressure sintered silicon nitride based composites with 0~5wt% $\beta$-Si3N4 whiskers were prepared. The whiskers were unidirectionally oriented by a modified tape casting technqiue and green bodies with various microstructure were formed by changing stacking sequences of sheets cut from the tape. Orientations of the large elongated grains of the sample after gas pressure sintering were the same as the those of the whiskers of green body, and the sintering shrinkage and mechanical properties of sintered sample were consistent with the microstructural characteristics. In case of unidirectional samples, the sintering shrinkage normal to whisker alignment direction was larger than that parallel to the direction. The shrinkage difference inceaed as the whiskercontent increaed. As whisker content increaed, the crack length normal to and parallel to tape casting direction became shorter and larger, respectively. Although the grain size increased by th whisker addition, the flexural strength of unidirectional samples was not lower than that of smaple without the whisker. In case of crossplied and 45$^{\circ}$rotated samples, the anisotropy of mechanical preoperties disappeared.

• Korean Journal of Materials Research
• /
• v.11 no.2
• /
• pp.104-114
• /
• 2001

To investigate the effects of the addition of Nb and Sn on the recrystallization of Zr- Sn-Nb alloys, both Vickers micro-hardness test and TEP measurement were carried out on cold-worked specimens annealed at various temperatures from $300^{\circ}C$ to 75$0^{\circ}C$. The microstructures of heat treated specimens were analyzed by optical microscope, SEM, and TEM. The study of microhardness and microstructures showed that both recrystallization process and grain growth were retarded as the activation energy was increased by the addition of Nb and Sn. Especially, the addition of Sn was more effective on retarding recrystallization. Precipitates were formed more easily when Nb was added because the solubility of Nb into Zr is lower than that of Sn. However, the recrystallization process was affected more by Sn than Nb because the strain field formed by substitutional Sn repressed the dislocation movement. TEP was increased due to the decrease of electron scattering as recovery and recrystallization were proceeded and saturated when the recrystallization completed. However, when precipitates formed, TEP was increased because the decrease of solute concentration near the precipitates caused the decrease of electron scattering.

• Korean Journal of Materials Research
• /
• v.29 no.4
• /
• pp.205-210
• /
• 2019

$Pb(Zr,Ti)O_3$ (PZT) is used for the various piezoelectric devices owing to its high piezoelectric properties. However, lead (Pb), which is contained in PZT, causes various environment contaminations. $(K,Na)NbO_3$ (NKN) is the most well-known candidate for a lead-free composition to replace PZT. A single crystal has excellent piezoelectric-properties and its properties can be changed by changing the orientation direction. It is hard to fabricate a NKN single crystal due to the sodium and potassium. Thus, $(Na,K)NbO_3-Ba(Cu,Nb)O_3$ (NKN-BCuN) is chosen to fabricate the single crystal with relative ease. NKN-BCuN pellets consist of two parts, yellow single crystals and gray poly-crystals that contain copper. The area that has a large amount of copper particles may melt at low temperature but not the other areas. The liquid phase may be responsible for the abnormal grain growth in NKN-BCuN ceramics. The dielectric constant and tan ${\delta}$ are measured to be 684 and 0.036 at 1 kHz in NKN-BCuN, respectively. The coercive field and remnant polarization are 14 kV/cm and $20{\mu}C/cm^2$.

• Membrane Journal
• /
• v.25 no.5
• /
• pp.422-430
• /
• 2015

The present study announces that the pH value of seed coating solution makes a significant effect on the microstructure of silicalite-1 zeolite layer formed on ${\alpha}$-alumina support. Seed with an average diameter of 75 nm was dispersed in ethanol to prepare three kinds of seed coating solutions with different pH values, and dip-coated on the support. The pH value was controlled to be 2.2, 7.0, and 9.3, respectively. In the secondary growth process, pH 7 seed solution resulted an uniform, 3 to $4{\mu}m$ thick, completely covered, and 100 nm grained silicalite-1 zeolite separation layer. The uniformity and completeness were explained by a uniform, closely packed, multi-layered, and completely covered seed coating in the pH 7 condition. In the condition, ${\alpha}$-alumina support and seed are oppositely charged: support is positively charged (8.4 mV) and seed, negatively (-1.7 mV). The opposite charging induced a strong electrostatic attraction between seed and support, which made the good seed coating state. On the other hand, pH 2.2 and pH 9.3 seed solutions resulted non-uniform, partially covered, and around $1{\mu}m$ grained zeolite separation layer, since seed and support are the same sign charged in the conditions. The same sign charging induced a strong electrostatic repulsion between seed and support which caused a low coverage of seed. It could be concluded that the pH value of seed coating solution is a key parameter to determine the microstructure of silicalite-1 zeolite separation layer.

• Journal of the Korean Vacuum Society
• /
• v.17 no.6
• /
• pp.538-543
• /
• 2008

Recently a nano-scale diamond is possible to manufacture forms of powder(below 100 nm) by new processing of explosion or deposition method. Using a sintering of nano-scale diamond is possible to manufacture of grinding tools. We have need of a processing development of coated uniformly inorganic to prevent an abnormal grain growth of nano-crystal and bonding obstacle caused by sintering process. This paper, in order to improve the sintering property of nano-scale diamond, we coated ZnO thin films(thickness: $20{\sim}30\;nm$) in a vacuum by ALD(atomic layer deposition) Economically, in order to deposit ZnO all over the surface of nano-scale diamond powder, we used a new modified fluidized bed processing replaced mechanical vibration effect or fluidized bed reactor which utilized diamond floating owing to pressure of pulse(or purge) processing after inserted diamond powders in quartz tube(L: 20 mm) then closed quartz tube by porosity glass filter. We deposited ZnO thin films by ALD in closed both sides of quartz tube by porosity glass filter by ALD(precursor: DEZn($C_4H_{10}Zn$), reaction gas: $H_2O$) at $10^{\circ}C$(in canister). Processing procedure and injection time of reaction materials set up DEZn pulse-0.1 sec, DEZn purge-20 sec, $H_2O$ pulse-0.1 sec, $H_2O$ purge-40 sec and we put in operation repetitive 100 cycles(1 cycle is 4 steps) We confirmed microstructure of diamond powder and diamond powder doped ZnO thin film by TEM(transmission electron microscope) Through TEM analysis, we confirmed that diamond powder diameter was some $70{\sim}120\;nm$ and shape was tetragonal, hexagonal, etc before ALD. We confirmed that diameter of diamond powders doped ZnO thin film was some $70{\sim}120\;nm$ and uniform ZnO(thickness: $20{\sim}30\;nm$) thin film was successfully deposited on diamond powder surface according to brightness difference between diamond powder and ZnO.

• Journal of the Korean Magnetics Society
• /
• v.16 no.5
• /
• pp.255-260
• /
• 2006

The basic composition of Ni-Zn ferrite was $(Ni_{0.35}Cu_{0.2}Zn_{0.45})_{1.02}(Fe_2O_3)_{0.98}$ (group A) and $(Ni_{0.4}Cu_{0.2}Zn_{0.4})_{1.02}(Fe_2O_3)_{0.98}$(group B) with additional 0.1 mol% $CaCO_3$ and 0.03 mol% $V_2O_5$. For high permeability and acceleration of grain growth, $CaCO_3$ and $V_2O_5$ was added. The mixture of the law materials was calcinated at $600^{\circ}C$ for 2 hours and then milled. The compacts of toroidal type were sintered at different temperature ($1,050^{\circ}C,\;1,070^{\circ}C,\;1,100^{\circ}C$) for 2 hours in air followed by an air cooling. Then, effects of various composition and sintering temperatures on the microstructure and physical properties such as density, resistivity, magnetic induction, coercive force, initial permeability, quality factor, and curie temperature of the Ni-Zn ferrite were investigated. The density of the Ni-Zn ferrite was $4.90{\sim}5.10g/cm^3$, resistivity revealed $10^8{\sim}10^{12}{\Omega}-cm$. The average grain size increased with the increase of sintering temperatures. The magnetic properties obtained from the aforementioned Ni-Zn ferrite specimens were 4,000 gauss for the maximum induction, 0.25 oersted for the coercive force, 2,997 for the initial permeability, 208 for the quality factor, and $202^{\circ}C$ for the curie temperature. The physical properties indicated that the specimens could be utilized as the core of microwave communication and high permeability deflection yoke of high permeability.