• Elastomers and Composites
• /
• v.45 no.4
• /
• pp.263-271
• /
• 2010

Intermittent CSR testing was used to investigate the degradation of an FKM O-ring, also the prediction of its life-time. An intermittent CSR jig was designed taking into consideration the O-ring's environment under use. The testing allowed observation of the effects of friction, heat loss, and stress relaxation by the Mullins effect. Degradation of O-rings by thermal aging was observed between 60 and $160^{\circ}C$. In the high temperature of range ($100-160^{\circ}C$) O-rings showed linear degradation behavior and satisfied the Arrhenius relationship. The activation energy was about 60.2 kJ/mol. From Arrhenius plots, predicted life-times were 43.3 years and 69.9 years for 50% and 40% failure conditions, respectively. Based on TTS (time-temperature superposition) principle, degradation was observed at $60^{\circ}C$, and could save testing time. Between 60 and $100^{\circ}C$ the activation energy decreased to 48.3 kJ/mol. WLF(William-Landel-Ferry) plot confirmed that O-rings show non-linear degradation behavior under $80^{\circ}C$. The life-time of O-rings predicted by TTS principle was 19.1 years and 25.2 years for each failure condition. The life-time predicted by TTS principle is more conservative than that from the Arrhenius relationship.

• Journal of Korean Society for Quality Management
• /
• v.35 no.2
• /
• pp.45-52
• /
• 2007

The danger of self-ignition of single base propellants will increase with time. Therefore, a good prediction of the safe storage time is very important. In order to determine the remaining shelf-life of the propellants, the content of stabilizer is determined. The propellants stored under normal storage conditions about 10 to 18 years were investigated and accelerated aging test was carried out by storing propellant sample at higher temperature. Finally, we analyzed the results by various methods in order to show the best way to predict the realistic shelf-life. The safe storage life of the propellants will be 24 years, at least 15 years. In case of applying Arrhenius's law, using the reaction rate constant at 28$^{\circ}C$ to 30$^{\circ}C$ to predict the shelf-life by accelerated aging test is reasonable for a good prediction.

• Journal of Applied Reliability
• /
• v.4 no.2
• /
• pp.73-90
• /
• 2004

We performed the heat aging test to predict the useful lifetime of Elastomeric Bearing Chloroprene Rubber (CR) used for supporting bridge. During the test, we measured elongation that are influenced by temperature and aging time. The failure of a test piece is defined as the point at which the elongation reaches to 75% of the initial value. This failure criterion is based on KS F 4420: 1998 (Elastomeric Bearing for bridge). Through the accelerated heat aging test, we found that the Arrhenius relationship and the Weibull lifetime distribution are appropriate as the life-temperature relationship and lifetime distribution of the CR, respectively. Using the Arrhenius -Weibull model, the parameters of the model are estimated and the lifetime of the CR at use condition is predicted.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.26 no.7
• /
• pp.1416-1425
• /
• 2002

In this study, the effects of combined environmental factors on mechanical and thermal analysis properties of graphite/epoxy composites were evaluated by the use of an accelerated aging test. Environmental factors such as temperature, moisture. and ultraviolet were considered. A xenon-arc lamp was utilized for ultraviolet light. and exposure times of up to 3000 hours were applied. Several types of specimens - tensile. bending, and shear specimens those are transverse to the fiber direction, and bending specimens those are parallel to the tiber direction - were used to investigate the effects of environmental factors on mechanical properties of the composites. Also, glass transition temperature, storage shear modulus, loss shear modulus, and tan ${\delta}$ were measured as a function of exposure times through a dynamic mechanical analyzer. In addition. a suitable testing method for determining the effect of environmental factors on mechanical properties is suggested by comparing the results from using two different types of strain measuring sensors. Finally, composite surfaces exposed to environmental factors were examined using a scanning electron microscope.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.31 no.3 s.258
• /
• pp.295-303
• /
• 2007

Degradation behaviors of filament-winded composites have been evaluated under the accelerated environmental test of high temperature, water immersion and thermal impact conditions. Two kinds of laminated composites coated by an urethane resin have been used: carbon-fiber reinforced epoxy(T700/Epon-826, CFRP) and glass-fiber reinforced phenolic (E-glass/phenolic, GFRP). For tensile strength of $0^{\circ}$ composites, CFRP showed little degradation while GFRP did high reduction by 25% under the influence of high temperature and water However for water-immersed $90^{\circ}$ composites tensile strength of both CFRP and GFRP showed high reduction. Bending strength and modulus of $90^{\circ}$ composites were largely reduced in water-immersion as well as high temperature environment. Urethane coating on the composite surface improved the bending properties by 20%, however hardly showed such improvement for water-immersed $90^{\circ}$ composites. In case of shear strength and modulus, both CFRP and GFRP showed high reduction by water-Immersion test but did a slight increase by high temperature and thermal impact conditions.

• Textile Coloration and Finishing
• /
• v.29 no.3
• /
• pp.155-161
• /
• 2017

In CPB(Cold-Pad-Batch) dyeing, the rubber of the padder roll is influenced by the heat, chemical and mechanical influences and thus aging of the padder roll rubber occurs. This study presents an accelerated thermal aging test of the CPB padder roll rubber with strong alkali conditions. Using Arrhenius formula of the various property values for the various aging temperatures($80^{\circ}C$, $90^{\circ}C$, $100^{\circ}C$) of the padder roll, the accelerated life predictions could be calculated. The threshold value of the property was set at different values. The hardness was set at the point where 5% degradation occurs based on the actual use conditions, and the tensile strength was set at the point where 50% degradation occurs based on the general life prediction standards. From the results of the different physical properties at differing temperatures, the Arrhenius plot could be obtained. Through the usage of the Arrhenius Equation, significant duration expectation could be predicted, and the chemical aging behavior of the CPB padder roll could be found at the arbitrary and actual temperatures.

• Journal of Applied Reliability
• /
• v.9 no.4
• /
• pp.275-290
• /
• 2009

This paper considers accelerated thermal degradation tests which are performed for rubber seal materials used for undersea tunnels constructed by immersion method. Three types of rubber seals are tested; rubber expansion seal, omega seal, and shock absorber hose. Main ingredient of rubber expansion seal is EPDM(Ethylene Propylene Diene Monomer) and that of both omega seal and shock absorber hose is SBR(Styrene Butadiene Rubber). The accelerated stress is temperature and an Arrhenius model is introduced to describe the relationship between the lifetime and the stress. From the accelerated degradation tests, dominant failure mode of the rubber seals is found to be the loss of elongation. The lifetime distribution and the service life of the rubber seals at use condition are estimated from the test results. The acceleration factor for three types of rubber seals are also investigated.

• Journal of the Korean Society of Propulsion Engineers
• /
• v.2 no.3
• /
• pp.62-69
• /
• 1998

Mechanical properties of polyethyleneglycol(PEG)/cyclo-tetramethylene tetranitramine(HMX) propellant were studied by adding polycaprolactone(PCP) and silane derivatives as coupling agent. Mechanical properties of the propellant were enhanced by increasing the content of PCP which was partially replaced with PEG. PCP/HMX propellant showed 17% increase in maximum tensile strength and 59% increase in elongation compared to those of PEG/HMX propellant. However, as the content of PCP was increased, the hydrolytic stability of this propellant was found to be deteriorated due to the ester group of PCP by measuring hardness drop of cured propellant and swell ratio difference of PEG/PCP binder stored at $40^{\cire}C$ and 90% relative humidity. Hardness of the PEG/PCP/HMX propellant was decreased with increasing triethoxysilyl propionitrile(TESPN) and dinitrosalicylic acid (DNSA) content from accelerated aging at $60^{\cire}C$.

• Proceedings of the Korean Reliability Society Conference
• /
• 2006.05a
• /
• pp.27-31
• /
• 2006

Rubber hoses for automobile radiators are apt to degraded and thus failed due to the influence of contacting stresses of air and coolant liquid under thermal and mechanical loadings. The aging behaviors of the skin part of the hoses due to thermo-oxidative and electro-chemical stresses were experimentally analyzed. Through the thermo-oxidative aging test, it was shown that the surface hardness IRHD(International Rubber Hardness Degrees) of the rubber increased with a considerable reduction of failure strain as the aging time and temperature were large. On account of the penetration of coolant liquid into the skin part the weight of rubber specimens influenced by electro-chemical degradation (ECD) test increased, whereas their failure strain and IRHD hardness decreased. The hardness decreased further as the test site on the hose skin approached to the negative pole.

• Proceedings of the Korea Information Processing Society Conference
• /
• 2015.10a
• /
• pp.1384-1387
• /
• 2015

고령화 사회로 진입하면서 노인들은 노화과정에 의한 보행능력의 감소 및 근력 약화와 같은 신체적 변화로 인해 잦은 낙상을 경험한다. 이에 따라 낙상 사고를 감지하는 연구가 활발히 진행되고 있다. 낙상은 사전 예방도 중요하지만 사고 발생 후의 신속한 대처도 중요하다. 낙상을 감지하고 의료진에게 즉시 낙상정보를 제공하여 후속적 조치를 취하는 것은 사고 후 대처의 핵심이다. 본 논문에서는 스마트폰 환경에서 사용자의 낙상 후 방향을 판별하기 위해 두 가지 센서 데이터의 특정 값들을 추출하였으며, 이에 5 가지 기계학습 알고리즘을 적용하였다. 사용자는 스마트폰을 착용한 상태로 전후좌우 4 방향 낙상 실험을 진행하며 스마트폰 내에 내장된 3 축 가속도 센서와 3 축 자이로 센서값을 측정한다. 피험자 11 명을 대상으로 낙상 실험 결과, 5 가지의 분류기 중 k-NN에서 98.6%의 인식률을 나타내었다. 뽑아낸 특징 값과 분류 알고리즘은 낙상의 방향 검출에 유용한 것으로 판단된다.