• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2001년도 추계학술대회 논문집
• /
• pp.272-276
• /
• 2001

Multicomponent $Zr_{41.2}Ti_{13.8}Cu_{12.5}Ni_{10}Be_{22.5}$ bulk matallic glass alloy shows good bulk glass forming ability due to its high resistance to crystallization in the undercooled liquid state.1) In this study, DSC and X-ray diffractometry have been performed to confirm the amorphous structure of the master $Zr_{41.2}Ti_{13.8}Cu_{12.5}Ni_{10}Be_{22.5}$ alloy. To investigate the mechanical properties and deformation behaviors of the bulk metallic $Zr_{41.2}Ti_{13.8}Cu_{12.5}Ni_{10}Be_{22.5}$ alloy, a series of compression tests has been carried out at the temperatures ranging from $351^{\circ}C$ to $461^{\circ}C$ and at the various initial strain rates from $2{\times}10^{-4}s^{-1}\;to\;2{\times}10^{-2}s^{-1}$. There are two types of nominal stress-strain curves. The one shows linear stress-strain relationship meaning fracture at maximum stress, the other shows plastic deformation including steady-state flow. Also DSC analysis for the compressed specimens has been performed to investigate the change of thermal stability and crystallization behavior for the various test conditions.

• 열처리공학회지
• /
• 제5권3호
• /
• pp.149-156
• /
• 1992

Transformation behavior and reversible shape memory effct of Ti-Ni-Cu alloys with various Cu content has been investigated by means of electrical resistivity measurement, differential scanning calorimetry. X-ray diffraction and strain gage sensor. The transformation sequence in Ti-Ni-Cu alloys substituted by Cu for Ni up to 5at.% occurs to $B2{\leftrightarrow}B19^{\prime}$ and it proceeds in two stages by addition of 10 at.%Cu. i.e. $B2{\leftrightarrow}B19{\leftrightarrow}B19^{\prime}$. But the content of Cu increases up to 20at.%, it has been transformed in one stage ; $B2{\leftrightarrow}B19$. The shape change of Ti-40Ni-10Cu alloy which was constrain aged in circular form bended in $B2{\leftrightarrow}B19$ transformation but it spreaded out in $B19{\leftrightarrow}B19^{\prime}$ transformation. The amount of reversible shape change (${\Delta}{\varepsilon}$) of Ti-47Ni-3Cu alloy constrain aged at $400^{\circ}C$ after solution treatment has a maximum value of about $5.6{\times}10^{-3}$, but that of cold rolled and constrain aged specimens exhibits a little value independent of Cu concentrations.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1995년도 하계학술대회 논문집 C
• /
• pp.1165-1167
• /
• 1995

The Cu-Si alloy has been proposed as a new matrix materal for filamentary Nb-Ti wires in AC use. The Cu-Si alloy shows approprite mechanical and electrical properties, and is economically more favourable than the Cu-Ni alloy matrix used currently. Moreover, the addition of Si to Cu prevents the formation of intermetallic compounds around the filaments. After we investigated resistivity and hardness of Cu-Si alloy as matrix materal, investigated CuSi/NbTi interface reactions and superconductivities of superconducting wires that were made by various heat treatment.

• 열처리공학회지
• /
• 제12권2호
• /
• pp.145-156
• /
• 1999

The distribution of the second phase, the change of transformation temperature and mechanical properties with thermomechanical treatment conditions were investigated by metallography, calorimetry, EDS, tensile test and fractography in a Cu-Al-Ni-Ti-Mn alloy. The cast structure revealed Ti-rich precipitates($X_L$ phase) between dendrite arms, which have been identified as $(Cu,Ni)_2TiAl$ intermetallic compounds. By homogenizing above $900^{\circ}C$, the $X_L$ phase was melted in the matrix, while the Xs phase was precipitated in matrix and the volume fraction of it was increased. When hot-rolled specimen was betatized below $750^{\circ}C$, recrystallization could not be observed. However, the specimen betatized above $800^{\circ}C$ was recrystallized and the grain size was about $50{\mu}m$, while Xs phase was precipitated in matrix. With raising betatizing temperature, $M_s$ and $A_s$ temperatures were fallen and transformation hysteresis became larger. The strain of the specimen betatized at $800^{\circ}C$ was 8.2% as maximum value. The maximum shape recovery rate could be obtained in the specimen betatized at $800^{\circ}C$ but it was decreased due to the presence of Xs phase with increasing betatizing temperature.

• 한국분말재료학회지
• /
• 제22권3호
• /
• pp.181-186
• /
• 2015

In this study, the effect of the friction stir welding (FSW) was compared with that of the gas tungsten arc welding (GTAW) on the microstructure and microhardness of Cu-Ni alloy weldment. The weldment of 10 mm thickness was fabricated by FSW and GTAW, respectively. Both weldments were compared with each other by optical microstructure, microhardness test and grain size measurement. Results of this study suggest that the microhardness decreased from the base metal (BM) to the heat affected zone (HAZ) and increased at fusion zone (FZ) of GTAW and stir zone (SZ) of FSW. the minimum Hv value of both weldment was obtained at HAZ, respectively, which represents the softening zone, whereas Hv value of FSW weldment was little higher than that of GTAW weldment. These phenomena can be explained by the grain size difference between HAZs of each weldment. Grain size was increased at the HAZ during FSW and GTAW. Because FSW is a solid-state joining process obtaining the lower heat-input generated by rotating shoulder than heat generated in the arc of GTAW.

• 열처리공학회지
• /
• 제16권2호
• /
• pp.90-96
• /
• 2003

The effect of betatizing temperature on microstructure and transformation characteristics in a Cu-AI-Ni based pseudoelastic alloy fabricated by heated mold continuous casting by using metallography, XRD and calorimetry. The microstructure of cast rod betatized at $600^{\circ}C$ revealed a ${\beta}_1$ parent phase and a ${\gamma}_2$ phase precipitated along the casting direction. When the cast rod was betatized at the elevated temperature above $600^{\circ}C$, the ${\gamma}_2$ phase is completely dissolved into the matrix so that the volume fraction of the ${\gamma}_2$ phase was decreased. The parent phase was stabilized by betatizing at $600^{\circ}C$. However, the ${\beta}_1$ parent phase was transformed to both ${{\beta}_1}^{\prime}$ and ${{\gamma}_1}^{\prime}$ martensites with increasing betatizing temperatures above $600^{\circ}C$, while $M_s$ and $A_s$ temperatures were decreased. The stress-strain curves for compression test were not same with betatizing temperature; the stress-strain curves of the specimen betatized at $600^{\circ}C$ and $700^{\circ}C$ were linear but those of the specimen betatized at $800^{\circ}C$ and $900^{\circ}C$ were not linear.

• 한국초전도ㆍ저온공학회논문지
• /
• 제10권1호
• /
• pp.24-27
• /
• 2008

For the development of superconducting fault current limiters(SFCLs) having large current capacity, we fabricated an SFCL element that consists of Bi-2212 superconductor and Cu-Ni alloy tubes. First, Ag was plated on the surface of the Bi-2212 for the enhancement of soldering process. On the Ag-plated Bi-2212 tube, a Cu-Ni alloy tube was soldered using optimized solders and soldering conditions. The BSCCO/Cu-Ni composite was processed mechanically to have a helical shape for the improvement of the SFCL characteristics. The total current path of the SFCL element was 1330 mm long with 12 turns, and had critical current of 340 A at 77 K. Finally, we carried out the fault test using the fabricated SFCL element. It showed successful current limiting performance under the fault condition of 50 $V_{rms}$ and 5.5 kA. From the results, the rated voltage of the SFCL element was decided to be 0.4 V/cm, and the power capacity was 12 kVA at 77 K. The fabrication process of the SFCL and the fault test results will be presented.

• 한국초전도학회:학술대회논문집
• /
• 한국초전도학회 2005년도 High Temperature Superconductivity Vol.XV
• /
• pp.88-88
• /
• 2005

• 한국분말재료학회지
• /
• 제11권3호
• /
• pp.193-201
• /
• 2004

1960년 Au-Si계 합금에서 처음으로 비정질상이 급속 응고법에 의해 보고된 이래/sup 1)/ 지난 40년 간 많은 합금계에서 비정질상이 보고되어졌다. 대표적으로 Fe-, Ni-, Co기 합금 등 많은 합금계에서 비정질상이 보고되었으나, 비정질상의 형성을 위해서는 약 105 K/s이상의 높은 냉각속도를 필요로 하였다. 1980년대 수백 K/s의 낮은 냉각속도 하에서도 비정질상이 형성될 수 있는 다원계 합금(multi-component alloy)이 Mg-Ln-(Ni, Cu, Zn), Ln-Al-TM 합금에서 보고되어 졌으나 많은 관심을 받지 못하다가 1993년 Zr-Ti-Ni-Cu-Be 합금에서 수 ㎝ 크기의 비정질합금 제조가 보고되면서 전 세계적으로 많은 관심을 받게 되었다. Zr-Ti-Ni-Cu-Be계 벌크 비정질 합금이 보고된 후 Zr-(Nb,Pd)-Al-TM, Pd-Cu-Ni-P, Fe-Co-Zr-Mo-W-B, Ti-Zr-Ni-Cu-Sn등 여러 합금계에서 벌크 비정질 합금이 보고되었다. (중략)

• 한국초전도저온공학회:학술대회논문집
• /
• 한국초전도저온공학회 2003년도 추계학술대회 논문집
• /
• pp.24-26
• /
• 2003

We fabricated Ni and Ni alloy substrates for YBCO coated conductors. The Ni and Ni alloy substrate was fabricated by powder metallurgy technique and cold rolling. The texture of substrates had a strong 4-fold symmetry and ［111］∥ND texture after annealing temperature of 100$0^{\circ}C$. The measured full-width half-maximum (FWHM) of in-plane and out-of-plane was in the range of 6$^{\circ}$-10$^{\circ}$. The powder metallurgy technique is fabrication of the substrates for considered to be suitable for the application of YBCO coated conductors.