• Transactions on Electrical and Electronic Materials
• /
• v.6 no.6
• /
• pp.284-288
• /
• 2005

We have systematically studied the superconducting properties and flux pinning enhancement of $(Y_{0.33}Sm_{0.33}Nd_{0.33})\;Ba_2Cu_3O_y$ [(YSN)-123] composite oxides by melt growth process in air. A sample prepared by this method showed well-textured microstructure, and $(Y_{0.33}Sm_{0.33}Nd_{0.33})\;BaCuO_5$ [(YSN)211] nonsuperconducting particles were uniformly dispersed in large (YSN) 123 superconducting matrix. The sample showed a sharp superconducting transition at 91 K. The magnetization measurements of the (YSN)-123 sample exhibited the enhanced flux pinning, compared with $YBa_2Cu_3O_y$ (Y-123) sample without Sm and Nd. Critical current densities of (YSN)-123 sample was $2.5{\times}10^4 A/cm^2$ at 2 T and 77 K.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.15 no.4
• /
• pp.141-144
• /
• 2005

[ $(Y_{0.5}Sm_{0.25}Nd_{0.25})Ba_2Cu_3O_y$ ] [(YSN)-123] high $T_c$ composite superconductors with $CeO_2$ addition were systematically investigated by top seeded melt growth (TSMG) process in air atmosphere. A melt textured $NdBa_2Cu_3O_y$ (Nd-123) single crystal was used as a seed for achieving the c-axis alignment large grains perpendicular to the surface of (YSN)-123 composite oxides. The size of $(Y_{0.5}Sm_{0.25}Nd_{0.25})_2BaCuO_5$ [(YSN)211] nonsuperconducting inclusions of the melt textured (YSN)-123 samples with $CeO_2$ addition were remarkably reduced and uniformly distributed within the (YSN)123 superconducting matrix except in the region very close to the Nd-123 seed crystal. The sample showed a sharp superconducting transition of 91 K.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.21 no.5
• /
• pp.199-204
• /
• 2011

$(YSmNd)_{1.8}Ba_{2.4}Cu_{3.4}O_{7-x}$ [(YSN)1.8] high $T_c$ superconductor was directionally grown by zone melt growth process, in air atmosphere. In this study, optimum melting temperature and growth rate were $1100^{\circ}C$ and 3.5 mm/hr, respectively. The microstructure of well-textured (YSN)1.8 samples were examined by XRD, optical microscopy, TEM and SQUID magnetometer. The critical current density of these samples were measured by the direct transporting current method. In the observation using an optical microscopy, nonsuperconducting $(YSmNd)_2BaCuO_5$[(YSN)211] inclusions of (YSN)1.8 superconductor uniformly distributed within the superconducting (YSmNd)$Ba_2Cu_3O_x$[(YSN)123] matrix. The directionally melt-textured (YSN)1.8 superconductor showed an onset $T_c{\geq}90\;K$ and sharp superconducting transition. The transport $J_c$ values were 830 A and $3.93{\times}10^4$ (A/$cm^2$) at 77 K self-field, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.280-281
• /
• 2005

We have studied the superconducting properties and flux pinning enhancement of $(Y_{0.5}Nd_{0.25}Sm_{0.25})_{1.8}Ba_{2.4}Cu_{3.4}O_y$ [(YNS)-1.8] composite oxides by melt growth process in air. A sample prepared by this method showed well-textured microstructure, and $(Y_{0.5}Nd_{0.25}Sm_{0.25})_2BaCuO_5$ [(YNS)211] nonsuperconducting particles were uniformly dispersed in large (YNS)123 superconducting matrix. The sample showed a sharp superconducting transition at 91 K. The magnetization measurements of the (YSN)-1.8 sample exhibited the enhanced flux pinning, compared with $YBa_2Cu_3O_y$ (Y-123) sample without Sm and Nd.