• 전자공학회논문지A
• /
• 제28A권11호
• /
• pp.880-886
• /
• 1991

Multi-layered chip inductors were prepared with good magnetic properties by sintering Ni-Zn-Cu ferrites at a lower temperature. A slurry with 49.5mol%Fe$_{2}O_{3}$, 20.5mol% ZnO, 20mol% NiO and 10nol% CuO was cast into tapes with 60-100\ulcorner of thickness with a doctor blade techniques. The tapes were screen-pronted with 100% silver electrodes, layered and pressed at 250kg/cm$^{2}$ and then sintered ant 900$^{\circ}C$ for 2h. Inductance with internal electrodes printed 5, 10, and 15 turns showed 4.9, 15 and 24$\mu$, respectively, at 1MHz.

• 대한기계학회논문집A
• /
• 제21권9호
• /
• pp.1507-1519
• /
• 1997

This paper aims to clarify the effects of grinding conditions on bending strength in surface grinding of various ferrites with the resin bond diamond wheel. The main conclusions obtained were as follows. At a constant material removal rate, the strength improves with increased wheel depth of cut and decreased workpiece speed. It is desirable to grind at higher peripheral wheel speed and under the critical workpiece speed presented in this paper. Grinding the ferrite of higher brittleness, the wheel depth of cut limited to hold 50% of their inherent strength becomes lower. The effect of various grinding conditions on bending strength becomes more larger in the order of Sr, Mn-Zn and Cu-Ni-Zn. When using the diamond grain of the lower toughness, the bending strength becomes higher, and the wheel wear occurs faster. Considering both bending strength and wheel wear rate, the best concentration of wheel is 100. The ground surfaces exhibit that the fracture process during grinding becomes more brittle in the order of Sr, Mn-Zn and Cu-Ni-Zn.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1999년도 춘계학술대회 논문집
• /
• pp.80-83
• /
• 1999

We have studied properties(crystal structure, density, absorption, contraction, initial permeability, and permeability) of Ni$_{0.175-x}$Cu$_{x}$Zn$_{0.33}$Fe$_{0.495}$ (x=0~0.175) ferrites with various NiO and CuO, because of development of materials for high frequency inductor. The XRD peaks of all of samples were observed only spine이 phase. As a results of the density, absorption rate, and shrinkage rate, the grain growth progressed rapidly in x=0.1 at 95$0^{\circ}C$, x=0.075 at 105$0^{\circ}C$, and x=0.025 at 115$0^{\circ}C$ for 3 hours. Initial permeability increased with increasing CuO concentration until x=0.1, and then decreased. The complex permeability as a function frequency were high values at sintered 105$0^{\circ}C$ fotr3 hours in x=0.075, 0.1., 0.1.1.

• Journal of Magnetics
• /
• 제8권4호
• /
• pp.138-141
• /
• 2003

$Ni_{0.65}Zn_{0.35}Fe_2O_4$thin films were prepared by using a sol-gel method. Their crystallographic, dielectric and magnetic properties were investigated as a function of Cu contents by means of an X-ray diffractometer (XRD), X-ray reflectivity, LCZ meter (NF2232), a vibrating sample magnetometer (VSM), and an atomic force microscope (AFM). From typical C-V measurements for $Ni_{0.65}Zn_{0.35}Fe_2O_4$ thin films on p-type silicon substrate, the surface charge density was calculated as 1.4 ${\mu}$C/$m^2$. The dielectric constant evaluated from the capacitance at the accumulation state was 28. The high $H_{c}$ and low $M_{sat}$ at x=0.0 and 0.1 were due to the growth of the ${\alpha}$-$Fe_2O_3$ phase having antiferromagnetic properties. The rapidly decreased $H_{c}$ and increased $M_{sat}$ at x=0.2 and 0.3 can be explained that the ${\alpha}$-$Fe_2O_3$ phases have completely disappeared at x=0.3 and so, non-magnetic defects are minimized. The $M_{sat}$ was slightly decreased and the $H_{c}$ was increased above at x=0.3 because the increase of grain boundary due to smaller grain size acts as defects during magnetization process.

• 한국자기학회지
• /
• 제13권3호
• /
• pp.109-114
• /
• 2003

NiCuZn 페라이트에 $V_2O_{5}$를 0~0.5 wt% 첨가하여 페라이트 페이스트를 준비한 후,스크린 인쇄법으로 내부전극이 4.5회 회전된 임의의 크기(7.7$\times$4.5$\times$l.4 mm)의 칩인덕터를 제조하여, $V_2O_{5}$ 첨가량에 따른 미세구조 및 자기적 특성 변화를 분석하였다. $V_2O_{5}$첨가량이 증가할수록 액상소결이 발달하여 페라이트 입계에 내부전극 Ag의 확산과 Cu 석출 현상이 촉진되고, 이로 인하여 과대입자성장이 발달되었다. 이러한 현상은 칩인덕터의 자기적 특성에 큰 영향을 미쳐,900 $^{\circ}C$에서 소결된 $V_2O_{5}$ wt% 첨가시편의 주파수 10 MHz에서의 인덕턴스 값이 3.7$\mu$H로 0.3 wt% 첨가 시편의 4.2 $\mu$H보다 작게 나타났는데, 이는 Ag와 Cu의 석출량이 많아짐에 따라 잔류응력 발생이 심화되기 때문으로 생각된다 또한 $V_2O_{5}$ 0.5 wt% 첨가한 시편의 경우 소결온도가 증가함에 따라 품질계수 값이 감소하였는데, 이 결과도 페라이트 입계에서의 Ag나 Cu의 금속성분의 석출량 증가 및 과대입자성장에 의한 입자크기 증대로 인하여 전체 전기비저항이 감소되기 때문인 것으로 생각된다. 결론적으로 자기적 특성을 고려할 때 0.3 wt%가 적정 첨가량으로 나타났다.

• 한국분말재료학회지
• /
• 제15권4호
• /
• pp.292-296
• /
• 2008

The electromagnetic (EM) wave absorption properties of the $Fe_{73}Si_{16}B_7Nb_3Cu_1$ nanocrystalline powder mixed with 5 to 20 vol% of Ni-Zn ferrites has been investigated in a frequency range from 100MHz to 10GHz. Amorphous ribbons prepared by a planar flow casting process were pulverized and milled after annealing at 425 for 1 hour. The powder was mixed with a ferrite powder at various volume ratios to tape-cast into a 1.0mm thick sheet. Results showed that the EM wave absorption sheet with Ni-Zn ferrite powder reduced complex permittivity due to low dielectric constant of ferrite compared with nanocrystalline powder, while that with 5 vol% of ferrite showed relatively higher imaginary part of permeability. The sheet mixed with 5 vol% ferrite powder showed the best electromagnetic wave absorption properties at high frequency ranges, which resulted from the increased imaginary part of permeability due to reduced eddy current.