• 한국레이저가공학회지
• /
• 제11권2호
• /
• pp.15-19
• /
• 2008

Electron beam (EB) weldability of pure grade Nb sheet was studied. One of Nb sheets was as-annealed and the other was cold rolled. Microstructures, Vickers hardness, and transverse weld tensile test were carried out for the base metal, the heat affected zone (HAZ) and weld metal. In the case of the EB welds made using the annealed Nb sheeet, fine equiaxed grains and coarse grains were dominant at the base metal and the HAZ, respectively, and columnar grains were observed at the weld metal. For the EB welds made using the cold rolled Nb sheet, elongated grains in the rolling direction at the base metal, and the microstructures of the weld metal and the HAZ are similar to those of the EB welds made using the annealed Nb sheet, respectively. For both annealed and cold rolled Nb sheet, the width of the HAZs are unusually wide in spite of using high density heat source, i.e. electron beam, and the grain sizes of both HAZs are similar. When tensile test was carried out using the transverse weld specimens, the failure occurred at the HAZ for both EB welds made using Nb sheets annealed and cold rolled, respectively and the tensile strengths of both specimens were 161MPa. Vickers hardness of EB welds made using annealed Nb was 56-57 Hv at both base metal and weld metal, 52-53 Hv at the HAZ. On the other hand, Vickers hardness of EB welds made using cold rolled Nb was 97-99 Hv at the base metal, but the hardness values of weld metal were similar to those obtained at the weld metal of annealed Nb.

• 공업화학
• /
• 제16권3호
• /
• pp.449-455
• /
• 2005

분자 내에 방무기능을 부여하기 위한 수산기와 전자선(EB) 및 자외선(UV) 경화가 가능한 아크릴레이트 관능기를 갖는 1관능성 및 4관능성 방무제 AF-1과 AF-2를 합성하여 EB 및 UV 경화시스템에 적용하였다. 합성된 AF-1과 AF-2를 UV 경화시스템에 적용하여 도막의 방무특성 및 경화물성을 측정한 결과, AF-1과 AF-2 함량을 5:17.5의 비로 함유한 배합이 표면과 내부경도, 내화학성 및 접착력이 저하되지 않으면서 김서림 방지 특성이 우수한 최적배합임을 알 수 있었다. 이 최적배합을 EB 경화시스템에 적용하였고, EB 및 UV 두 시스템에 의해 이루어진 코팅배합물을 PC sheet에 코팅하여 도막의 방무특성 및 경화물성을 비교 연구하였다. 그 결과 EB 및 UV에 의해 경화된 두 시스템 모두 우수한 방무특성을 나타냈으나 EB 시스템이 UV 시스템보다 더우수한 내부경도, 접착력 및 젖음성을 나타냄을 확인하였다.

• 한국구조물진단유지관리공학회 논문집
• /
• 제26권6호
• /
• pp.256-262
• /
• 2022

본 연구의 목적은 실험을 통하여 FRP를 이용한 철근콘크리트 부재의 표면매립 전단보강 효과를 규명하는 것이다. 연구목적을 달성하기 위하여, 3개의 철근콘크리트 T형 보를 제작하고 이중 두 개의 보에 대해서 표면매립 보강방법으로 FRP를 전단보강한 뒤 실험을 통하여 보강효과를 규명하였다. 실험에서 두 가지의 전단보강방법을 고려하였는데, 첫째 충분한 매립길이를 가진 표면매립 (NSM) 보강, 둘째 다소 짧은 표면매립길이를 가지지만 추가의 표면부착 (EB) 보강을 한 경우이다. 연구결과, FRP strip을 이용한 표면매립길이를 플랜지 하부까지 길게 확보할 경우에는 충분한 전단보강효과가 발휘되는 것으로 나타났다. 반면에 충분한 매립길이가 확보되지 않은 경우에는 FRP sheet로 추가 보강하더라도 전단보강효과가 나타나지 않는 것으로 나타났다.

• Structural Engineering and Mechanics
• /
• 제83권4호
• /
• pp.415-433
• /
• 2022

Eighteen (18) (120×300×2200 mm) beams were prepared and tested to evaluate the shear strength of Glass Fiber Reinforced Concrete (GFRC) beams with no shear reinforcement, and evaluate the effectiveness of various innovative strengthening systems to increase the shear capacity of the GFRC beams. The test variables are the amount of discrete glass fiber (0.0, 0.6, and 1.2% by volume of concrete) and the type of longitudinal reinforcement bars (steel or GFRP), the strengthening systems (externally bonded (EB) sheet, side near-surface mounted (SNSM) bars, or the two together), strengthening material (GFRP or steel) links, different configurations of NSM GFRP bars (side bonded links, full wrapped stirrups, side C-shaped stirrups, and side bent bars), link spacing, link inclination angle, and the number of bent bars. The experimental results showed that adding the discrete glass fiber to the concrete by 0.6%, and 1.2% enhanced the shear strength by 18.5% and 28%, respectively in addition to enhancing the ductility. The results testified the efficiency of different strengthening systems, where it is enhanced the shear capacity by a ratio of 28.4% to 120%, and that is a significant improvement. Providing SNSM bent bars with strips as a new strengthening technique exhibited better shear performance in terms of crack propagation, and improved shear capacity and ductility compared to other strengthening techniques. Based on the experimental shear behavior, an analytical study, which allows the estimation of the shear capacity of the strengthened beams, was proposed, the results of the experimental and analytical study were comparable by a ratio of 0.91 to 1.15.

• 전자공학회논문지A
• /
• 제30A권12호
• /
• pp.51-59
• /
• 1993

A 4${\times}10^{19}cm^{3}$ carbon-doped base AlGaAs/GaAs HBY was grown using carbontetracholoride(CCl$_4$) by atmospheric pressure MOCVD. Abruptness of emitter-base junction was characterized by SIMS(secondary ion mass spectorscopy) and the doping concentration of base layer was confirmed by DXRD(double crystal X-ray diffractometry). Mesa-type HBTs were fabricated using wet etching and lift-off technique. The base sheet resistance of R$_{sheet}$=550${\Omega}$/square was measured using TLM(transmission line model) method. The fabricated transistor achieved a collector-base junction breakdown voltage of BV$_{CBO}$=25V and a critical collector current density of J$_{O}$=40kA/cm$^2$ at V$_{CE}$=2V. The 50$\times$100$\mu$$^2$ emitter transistor showed a common emitter DC current gain of h$_{FE}$=30 at a collector current density of JS1CT=5kA/cm$^2$ and a base current ideality factor of ηS1EBT=1.4. The high frequency characterization of 5$\times$50$\mu$m$^2$ emitter transistor was carried out by on-wafer S-parameter measurement at 0.1~18.1GHz. Current gain cutoff frequency of f$_{T}$=27GHz and maximum oscillation frequency of f$_{max}$=16GHz were obtained from the measured Sparameter and device parameters of small-signal lumped-element equivalent network were extracted using Libra software. The fabricated HBT was proved to be useful to high speed and power spplications.

• 컴퓨터교육학회논문지
• /
• 제16권3호
• /
• pp.49-60
• /
• 2013

본 연구는 블렌디드 이러닝이 대학의 강의실 위주의 수업에서 효과성을 향상시킬 수 있는지를 검증하고자 하였다. 먼저, 수업 사례를 분석하여 블렌디드 이러닝 운영방식으로 CbE(Class based E-learning)와 EbC(E-learning based Class) 방식을 도출하고, 수업구조로 Z형(Zigzag model)과 H형(Ladder model)을 정의하였다. 연구의 목적을 달성하기 위하여 A대학의 "엑셀실무" 과목에 CbE 방식의 H형 블렌디드 이러닝을 운영하였다. 집단은 사이버강의 학습참여비율의 50%이상인 집단(그룹 1)과 그렇지 않은 집단(그룹 2)으로 나누고, 자료의 분석은 $x^2$-검정, t -검정으로 학업 성취도를 비교하였다. 사이버강의 학습참여비율과 합격여부의 관계를 규명하기 위해 로지스틱 회귀분석을 실시하였다. 검정 결과, 그룹 1이 학업 성취도에서 통계적으로 유의하게 높게 나타났다. 로지스틱 회귀분석 결과에서 사이버강의 학습참여비율은 합격여부를 예측하는 유의미한 변인으로 규명됨에 따라, 블렌디드 이러닝의 효과성이 확증되었다. 연구 결과, H형 블렌디드 이러닝은 강의실 수업의 단점을 보완하여 학업 성취도와 학습 만족도를 향상시키고, 학습자가 블렌디드 이러닝 수업 방식에 대해 긍정적인 인식을 갖도록 한 것으로 나타났다. 끝으로 성공적으로 블렌디드 이러닝을 운영하기 위한 전략과 대학에서의 활성화 방안에 대해 제언하였다.

• 폴리머
• /
• 제36권4호
• /
• pp.531-535
• /
• 2012

폴리아닐린(PANI) 나노섬유를 전도성 충전제로 사용하여 광경화형 전도성 투명필름을 제조하였다. 화학산화중합(chemical oxidation polymerization)으로 나노섬유 구조의 산화형 폴리아닐린(ES-PANI)을 합성하였다. ES-PANI는 디도핑을 통해 환원형 폴리아닐린(EB-PANI)으로 유도하였다. 이것을 전도성 충전제의 전구체로 사용하여 도데실벤젠설폰산(DBSA)이 포함되어 있는 광경화형 레진에 분산시키면 재도핑된 재산화형 폴리아닐린(rES-PANI)을 얻을 수 있었다. 이런 과정을 통해 나노섬유 형태가 유지되면서 높은 전도성과 분산안정성이 우수한 광경화형 전도성 레진용액을 제조할 수 있었다. 제조된 광경화형 전도성 레진용액은 상온에서 3달 정도 두어도 rES-PANI 충전제의 침전물이 생기지 않았다. 또한 이 용액을 폴리(메틸 메타크릴레이트)(PMMA) 기재 위에 스핀코팅 후 광경화하여 약 $5{\mu}m$ 두께의 전도성 투명필름을 제조하였다. rES-PANI 나노섬유 농도가 1.4 wt%일 때 표면저항 $6.5{\times}10^8{\Omega}/sq$, 550 nm 파장에서 91.1%의 투과도를 보였다. ES-PANI의 디도핑-재도핑(dedoping-redoping) 과정을 통해 광경화형 전도성 레진용액에 분산된 PANI는 농도에 따라 필름표면저항과 광학적 투명도를 조절할 수 있는 대전방지 보호필름을 제작하는 새로운 방법을 제시하였다.