$(Ba_{1-x}Sr_xTiO_3$ (BST) thin films have been grown on Pt-coated MgO by metal -organic chemical vapor deposition. X-ray diffraction results showed that BST films were grown on a Pt/MgO substrate with (100) preferred orientation perpendicular to the surface. The lineawr relationship of P-E curve obtained form hysteresis loop measurement indicated that the BST films had a Curie transitions below room temperature . Films deposited at $900^{\circ}C$ exhibited a smooth and dense microstructure, a dielectric constant of 202, and a dissipation facotr of 0.02 at 100kHz. The leakage current density of the BST films is about $2\times10^{-10} \;A/\textrm{cm}^2$$ at an applied electric field of 0.2 MV/cm. The electrical behavior on the current-voltage characteristics is well explained by the bulk-limited Pool-Frenkel emission.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.33A no.2
• /
• pp.114-121
• /
• 1996

Thin film Ba$^{0.7}Sr^{0.3}TiO^{3}$ (BST) capacitors were fabricated on SiO$_{2}$/Si substrates by RF magnetron sputtering method and characterized at microwave frequencies ranging from 40 MHz to 1GHz to examine the dielectric dispersion of the capacitors. The BST thin films were electrode material of BST thin films capacitor which is known as one of the best electrode materials for BST films. 50$\AA$-thick titanium (Ti) layers were introduced to increase adhesion between bottom Pt and SiO$_{2}$. The leakage current density of the capacitors was about 1.7${\times}10^{7}A/cm^{2}$ at 1.5V and the dielectric constant was about 140 at 1MHz. Microwave measurement patterns having a coplanar waveguide type were fabricated and their S parameters were measured using network analyzer. After de-embedding parasitic components in microwave measurement patterns nearly frequency-invariant dielectric constant of about 120 was extracted in the measurement range of 40 MHz to 1 GHz.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.05b
• /
• pp.42-45
• /
• 2001

The high permittivity are applied to DRAM and FRAM. (Ba,Sr)$TiO_3$ (EST) thin films were prepared by Sol-Gel method. BST solution was made and spin-coated on $Pt/SiO_2/Si$ substrate at 4000 [rpm] for 10 seconds in a time coating. Coated specimens were dried at $90[^{\circ}C]$ for 5 minutes. Coating process was repeated from 3 times to 5 times and then sintered at $750[^{\circ}C]$ for 30 minutes. Each specimen was analyzed structure and electrical characteristics. Thickness of BST ceramics thin films are about 2600-2800[$\AA$] in 3 times. Dielectric constant of thin films was little decreased at 1[KHz]~1[MHz]. Dielectric constant and loss to frequency were 250 and 0.02 in BST3. The property of leakage current was stable When the applied voltage was 0~3[V] Leakage current was $10^{9}\sim10^{11}$[A] at 0~3[V].

• Proceedings of the Korea Electromagnetic Engineering Society Conference
• /
• 2002.11a
• /
• pp.370-374
• /
• 2002

This paper describes the design and fabrication of distributed analog phase shifter circuit. The phase shifter consist of coplanar waveguide(CPW) lines that are periodically loaded with voltage tunable (Ba,Sr)TiO$_3$ thin film interdigital(IDT) capacitors deposited by the pulsed laser deposition(PLD) on (001) MgO single crystals. The phase velocity on these IDT loaded CPW lines is a function of applied bias voltage, thus resulting in analog phase shifting circuits. The measured differential phase shift is 48$^{\circ}$ and the insertion loss decreases from -5㏈ to -3㏈ with increasing bias voltage from 0 to 40 V at 100㎐.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.455-458
• /
• 2001

The thin films of high pemitivity in ferroelectric materials using a capacitor are applied to DRAMs and FRAMs. (Ba, Sr)$TiO_3$ thin films as ferroelectric materials were prepared by the sol-gel method and made by spin-coating on the Pt/Ti/$SiO_2/Si$ substrate at 4,000 [rpm] for 10 seconds. The devices of BST thin films to composite $(Ba_{0.7},Sr_{0.3})TiO_3$ were fabricated by changing of the depositing layer number on $Pt/Ti/SiO_2/Si$ substrate. The thin film capacitor to be ferroelectric devices was investigated by structural and electrical properties. The thickness of BST thin films at each coating numbers 3, 4 and 5 times was $2500[\AA]$, $3500[\AA]$, $3800[\AA]$. The dielectric factor of thin film when the coating numbers were 3, 4 and 5 times was 190, 400 and 460 on frequency l[MHz]. The dielectric loss of BST thin film was linearly increased by increasing of the specimen area.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.455-458
• /
• 2001

The thin films of high permitivity in ferroelectric materials using a capacitor are applied to DRAMs and FRAMs. (Ba, Sr)TiO$_3$ thin films as ferroelectric materials were prepared by the sol-gel method and made by spin-coating on the Pt/Ti/SiO$_2$/Si substrate at 4,700 [rpm] for 10 seconds. The devices of BST thin films to composite (Ba$\_$0.7/Sr$\_$0.3/)TiO$_3$ were fabricated by changing of the depositing layer number on Pt/Ti/SiO$_2$/Si substrate. The thin film capacitor to be ferroelectric devices was investigated by structural and electrical properties. The thickness of BST thin films at each coating numbers 3, 4 and 5 times was 2500[${\AA}$], 3500[${\AA}$], 3800[${\AA}$]. The dielectric factor of thin film when the coating numbers were 3, 4 and 5 times was 190, 400 and 460 on frequency 1[MHz]. The dielectric loss of BST thin film was linearly increased by increasing of the specimen area.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1996.11a
• /
• pp.51-51
• /
• 1996

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.11 no.6
• /
• pp.252-258
• /
• 2001

($Ba_{0.7}Sr_{0.3})TiO_3$thin films were perpared on ITO-coated glass substrate by spin-coating method. The sol was sonicated in an ultrasonic bath to promote homogenization and the results were compared with untreated case. By application of the sonication process, crystallization temperatures of films were reduced, microstructers of films were more uniform and denser and the surface roughness of the films was lower from 8.4nm to 5.6nm. In addition, optical transmittances and electrical properties of films prepraed from sonicated sol were superior to those of films from untreated.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2002.10a
• /
• pp.33.2-33
• /
• 2002

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.11a
• /
• pp.132-135
• /
• 1999

Recently, the ceramics of high permittivity are applied to DRAM and FRAM. In this study, (B $a_{x}$ S $r_{l-x}$)Ti $O_3$(BST) ceramics thin films were prepared by Sol-Gel method. BST solution was made and spin-coated on Pt/ $SiO_2$/Si substrate at 4000 [rpm] for 10 seconds. Coated specimens were dried at 150[$^{\circ}C$] for 5 minutes. Coating process was repeated 3 times and then sintered at 750[$^{\circ}C$] for 30 minutes. Each specimen was analyzed structure and electrical characteristics. Thickness of BST ceramics thin films are about 2000($\AA$). Dielectric constant and loss of thin films was little decreased at 1[KHz] ~1[KHz]. Dielectric constant and loss to frequency were 250 and 0.02 in $Ba_{0.7}$S $r_{0.3}$Ti $O_3$. The properly of leakage current as the realation between the current and the voltage was that change of the leakage current was stable when the applied voltage was 0~3[V].