• Korean Journal of Materials Research
• /
• v.2 no.4
• /
• pp.248-256
• /
• 1992

This paper has reviewed some of the basic principles that underlie the field of defect chemistry in simple ATi$O_3$(A=Ca, Sr, Ba) perovskites. Frenkel defects in perovskite structure is very much unlikely, and Schottky defects and intrinsic electronic defects in undoped materials are negligibly small compared with background acceptor impurities. The electrical properties of perovskite ceramics are dependent on the aliovalent impurities. Since perovskite structure is a ternary system, the stoiohiometry between cations as well as cation-anion ratio will affect defect structure and electrical properties. BaTi$O_3$and SrTi$O_3$show a limited deviation from the cation stoichiometry while CaTi$O_3$has significant excess CaO and Ti$O_2$solubility.

• Journal of Powder Materials
• /
• v.19 no.4
• /
• pp.310-316
• /
• 2012

Nanocrystalline $BaTiO_3$ powder could be synthesized by solid-state reaction using the mixture which was prepared by a high energy milling process in a bead mill for $BaCO_3$ and nanocrystalline $TiO_2$ powders mixture. Effect of the milling time on the powder characteristic of the synthesized $BaTiO_3$ powder was investigated. Nanocrystalline $BaTiO_3$ with a particle size of 50 nm was obtained at $800^{\circ}C$. High tetragonal $BaTiO_3$ powder with a tetragonality(=c/a) of 1.009 and a specific surface area of $7.6m^2/g$ was acquired after heat-treatment at $950^{\circ}C$ for 2 h. High energy ball milling was effective in decreasing the reaction temperature and increasing the tetragonality.

• Journal of the Korean Ceramic Society
• /
• v.26 no.2
• /
• pp.249-257
• /
• 1989

Dielectric properties and the stability of the perovskite phase in the Pb(Mg1/3Nb2/3)O3 system have been investigated as a function of amount of BaTiO3 and firing temperature. In the specimens fired at 120$0^{\circ}C$, the pyrochlore phase was eliminated by the addition of 10-15m/o BaTiO3 and also the dielectric constant increased. However, the dielectric constant decreased with further addition of BaTiO3 even though no pyrochlore phase was found to be present. The reducing tendency of the pyrochlore phase decreased with lowering the firing temperature in the system of Pb(Mg1/3Nb2/3)O3 with BaTiO3. Dielectric properties in PMN ceramics were affected by the character of the BaTiO3 rather than the pyrochlore phase.

• Journal of the Korean Ceramic Society
• /
• v.31 no.5
• /
• pp.552-560
• /
• 1994

A composite of TiB2-Al2O3 system was successfully prepared from a mixture of TiO2, B2O3, and Al by self-propagating high temperature synthesis (SHS) with a novel characteristic, utilizing the internal oxidation heat of aluminium metal of the mixture, instead of by a conventional technique, externally heating a mixture of Ti, B and Al2O3. From a mixture with B/Ti molar ratio of =2.0, pure two phases of TiB2 and $\alpha$-Al2O3 with good crystallinity and small, uniform sizes were formed. However, when the B/Ti molar ratio of the mixture goes to a value less than 2.0, in addition to the above main minerals, a small smounts of metastable phases such as TiB and Ti3B4 were formed. It was found that about 60%, the optimum green density of compacts gave their highest reaction rate and temperature during SHS process. TiB2-Al2O3 system composite with B/Ti molar ratio of =2.0 could be pressurelessly sintered even at 190$0^{\circ}C$ under Ar gas flows without any addition of sintering aids, showing their good properties such as 91.2% in relative density, 2750 kgf/$\textrm{mm}^2$ in Vickers hardness and 2620 kgf/$\textrm{cm}^2$ in flexural strength.

• Journal of the Korean institute of surface engineering
• /
• v.56 no.6
• /
• pp.380-385
• /
• 2023

In this study, an MPB PMNT system containing 0.05 to 0.10 wt.% BaTiO₃ was synthesized using a traditional chemical method and its pyroelectricity was investigated. Pyroelectricity, dielectricity, and ferroelectricity of the synthesized BaTiO₃-PMNT system were analyzed by heat treatment at 1240~1280 ℃ for 4 hours to evaluate its applicability as a pyroelectric sensor. Unlike the simple ABO₃ ferroelectric, the BaTiO₃-doped PMNT system exhibited phase transition characteristics over a wide temperature range typical of complex perovskite structures. Although no dramatic change could be confirmed depending on the amount of BaTiO₃ added, stable pyroelectricity was maintained near room temperature and over a wide temperature range. When the amount of BaTiO₃ added increased from 0.05BaTiO₃-PMNT to 0.10BaTiO₃-PMNT, the electric field slightly increased from 5.00×10³ kV/m to 6.75×10³ kV/m, and the maximum value of remanent polarization slightly increased from 0.223 C/m² to 0.234 C/m². The pyroelectric coefficients of 0.05BaTiO₃-PMNT and 0.10BaTiO₃- PMNT at room temperature were measured to be ~0.0084 C/m²K and ~0.0043 C/m²K, respectively. The relaxor ferroelectric properties of the BaTiO₃-PMNT system were confirmed by analyzing the plot of K_max/K versus (T-T_max)^γ. The BaTiO₃-doped MPB PMNT system showed a distinct pyroelectric performance index at room temperature, and the values were F_v ~ 0.0362 m²/C, F_d ~ 0.575×10^-4 Pa^-1/2.

• Journal of the Korean Vacuum Society
• /
• v.9 no.3
• /
• pp.227-232
• /
• 2000

$MgTiO_3$thin films have been grown on various substrates by pulsed laser deposition (PLD) to investigate the application for microwave dielectrics and optical devices. Epitaxial $MgTiO_3$thin films were obtained on sapphire (c-plane$A1_2O_3$$MgTiO_3$thin films deposited on $SiO_2/Si$ and platinized silicon ($Pt/Ti/SiO_2/Si$) substrates were highly oriented. $MgTiO_3$thin films grown on sapphire were transparent in the visible and had a sharp absorption edge about 290 nm. These $MgTiO_3$thin films had extremely fine feature of surface morphology, i.e., rms roughness of 0.87 nm, which was examined by AFM. We have investigated the dielectric properties of the $MgTiO_3$thin films in $MIM(Pt/MgTiO_3/Pt)$ capacitors. Dielectric constant and loss of $MgTiO_3$thin films deposited by PLD were about 24 and 1.5% at 1 MHz, respectively. These $MgTiO_3$thin films also exhibited little dielectric dispersion.

• Applied Chemistry for Engineering
• /
• v.9 no.7
• /
• pp.998-1003
• /
• 1998

$BaTiO_3$ thin film was electrochemically deposited on Ti electrode in a 0.4 M $Ba(OH)_2$ solution of $85^{\circ}C$ using a current pulse waveform. Both $BaTiO_3$ crystallinity and faradaic efficiency for the film formation were enhanced with the increase of cathodic current density and pulse time. Based on the surface analysis and electrochemical studies, it was suggested that, during cathodic pulsed, the surface pH increase due to the reduction of $H_2O$ accelerates the structural changes of Ti oxides which were formed during anodic cycle. Prior to experiments, Ti oxides were intentionally grown in 0.1 M $H_2SO_4$ solution and the effect of initial oxide film thickness on the $BaTiO_3$ film formation was investigated. The migration of $Ti^{+4}$ ions through the oxide film was retarded with the increase of film thickness and it was observed that the crystallization of $BaTiO_3$ was only limited to the defect area of surface oxides.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.480-483
• /
• 2001

Epitaxial rutile-$TiO_2$ and anatase-$TiO_2$ films were grown at $800^{\circ}C$ on $Al_2O_3$ (1102) and $LaAlO_3$ (001), respectively, using pulsed laser deposition. The formation of different phases on different substrates could be qualitatively explained by the atomic arrangements at the interfaces. We also successfully deposited epitaxial rutile-$TiO_2$ and anatase-$TiO_2$ films on conductive $RuO_2$ and $La_{0.5}Sr_{0.5}CoO_{3}$ electrodes, respectively. Using a Kelvin probe, we measured the photovoltaic properties of these multilayer structures. A rutile-$TiO_2$ film grown on $RuO_2$ showed a very broad peak in the visible light region. An epitaxial anatase-$TiO_2$ film grown on $La_{0.5}Sr_{0.5}CoO_{3}$ showed a strong peak with a threshold energy of 3.05 eV.

• Korean Journal of Materials Research
• /
• v.18 no.9
• /
• pp.475-481
• /
• 2008

Positive temperature coefficient of resistivity (PTCR) characteristics of (1-x)$BaTiO_3-x(Bi_{0.5}K_{0.5})TiO_3$ ceramics doped with $Nb_2O_5$ were investigated in order to develop the Pb-free PTC thermistor available at high temperatures of > $120^{\circ}C$. The PTCR characteristics appearing in the ($B_{i0.5}K_{i0.5})TiO_3$ (< 5 mol%) incorporated $BaTiO_3$ ceramics, which might be mainly due to $Bi^{+3}$ ions substituting for $Ba^{+2}$ sites. The 0.99$BaTiO_3-0.01(Bi_{0.5}K_{0.5})TiO_3$ ceramics showed good PTCR characteristics of a low resistivity at room temperature (${\rho}_r$) of $31{\Omega}{\cdot}cm$ a high ${\rho}_{max}/{\rho}_{min}$ ratio of $5.38{\times}10^3$, and a high resistivity temperature factor (${\alpha}$) of $17.8%/^{\circ}C$. The addition of $Nb_2O_5$ to 0.99$BaTiO_3-0.01(Bi_{0.5}K_{0.5})TiO_3$ ceramics further improved the PTCR characteristics. Especially, 0.025 mol% $Nb_2O_5$ doped 0.99$BaTiO_3-0.01(Bi_{0.5}K_{0.5})TiO_3$ ceramics exhibited a significantly increased ${\rho}_{max}/{\rho}_{min}$ ratio of $8.7{\times}10^3$ and a high ${\alpha}$ of $18.6%/^{\circ}C$, along with a high $T_c$ of $148^{\circ}C$ despite a slightly increased ${\rho}_r$ of $31{\Omega}{\cdot}cm$.

• Journal of the Mineralogical Society of Korea
• /
• v.15 no.1
• /
• pp.59-68
• /
• 2002

Chemical analyses and Rietveld structural refinement with powder X-ray diffraction data were done for Nb-rich perovskite, named latrappite ($Ca_2NbFe^{3+}O_6$)from the Oka, Quebec, Canada. Latrappite is shown to be a member of a continuous solid solution of $CaTiO_3-NaNbO_3-Ca_2NbFe^{3+}O_6$ and approximately $(Ca_{1.5}Na_{0.4})\;(Nb_{0.1}Ti_{0.6}Fe_{0.4})O_6$ in composition. The crystal structure of latrappite, determined by Rietveld refinement, is similar to that of perovskite ($CaTiO_3$). It differs in that replacement of Ti by Nb and $Fe^{3+}$ results in greater distortion and tilting of the $TiO_6$ framework octahedra relative to $CaTiO_3$. Revised unit-cell parameters of latrappite are a=5.4474(4), b=5.5264(4), c=7.7519(5) ${\AA},\;V=233.4(3){\AA}^3$ space group Pbnm.