• 한국정밀공학회지
• /
• 제19권1호
• /
• pp.180-185
• /
• 2002

Aluminum casting/forging process is used to produce an aluminum tie-rod end for the steering system of automobiles. Firstly, casting experiments were carried out to get a good preform for forging the tie-rod end. In the casting experiment, the effects of additives, Ti+B, Zr, Sr, and Mg, on the mechanical properties and the microstructure of a cast preform were investigated. And a finite element analysis was performed to determine an optimal configuration of the cast preform. Lastly, a forging experiment was carried out to make the final product of aluminum tie-rod end by using the above cast preform. In the casting experiments, when 0.2% Ti+B and 0.25% Zr were simultaneously added into molten Al-Si alloy, the highest values of tensile strength and elongation of the cast preform were obtained. When 0.04% Sr were added into the molten aluminum alloy, the finest silicon-structure was observed in the cast preform. The highest hardness was obtained when 0.2% Mg was added. In the forging experiment, It was confirmed that the optimal configuration of a cast preform predicted by FE analysis was very useful. The hardness of a cast/forged product using designed preform was superior to that of required specification.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2010년도 하계학술대회 논문집
• /
• pp.330-330
• /
• 2010

이동통신 시스템의 소형화, 경량화, 다기능화 추세에 따라 이동통신 부품도 단위 부피당 소자의 집적도를 증가시키기 위하여 고집적화 추세로 급진전되고 있다. 이에 따라 세라믹 공정 기술도 고집적 추세로 다층화 되고 있어 수동소자의 내장화에 대한 필요성이 증대되고 있다. 이를 위하여 다양한 유전율 대역의 이종소재간 접합을 시도하지만 de-lamination, 내부 crack 등의 결함들이 발생하므로 열팽창계수 조절이 용이한 동종의 글라스를 사용하는 것이 유용하다. 본 연구에서는 공통의 글라스를 개발한 후 다양한 필러들을 혼합하여 mm파 대역에서 다양한 유전율을 갖는 LTCC 소재를 개발함으로써, 수동소자의 내장화에 따른 이종접합시의 매칭성을 극대화하고자 하였다. 이를 위하여 CaO-$Al_2O_3-SiO_2-B_2O_3$계 공통글라스에 $CaZrO_3$, $1.3MgTiO_3$, $2La_2O_3TiO_2$ 필러를 혼합하여 소결체의 미세구조, 유전특성 및 열기계적 특성을 고찰하였다. 이때 유전율 6에서 20에 이르는 저손실 소재를 개발할 수 있었다.

• 암석학회지
• /
• 제22권2호
• /
• pp.137-151
• /
• 2013

단층활동 과정에서 암석 내 화학조성과 광물 조성 간의 연관성을 이해하기 위한 목적으로 경주시 양북면 용당리에 발달하는 단층암에 대하여 XRF, ICP, XRD, EPMA/BSE 분석을 시행하여 단층암 내의 광물 조성 및 원소의 거동 경향성을 파악하였다. 단층암의 대표적인 주성분으로서 $SiO_2$는 61.6~71.0%의 범위로 가장 높은 함량을 나타내며, $Al_2O_3$는 10.8~15.8%이다. $Na_2O$는 0.22~4.63%, $K_2O$는 2.02~4.89%이고, $Fe_2O_3$는 3.80~12.5% 범위로 나타나 단층암 내에서 특히 이들 원소의 편차가 크다. 각력대에서 비지대로 갈수록 감소하는 경향을 나타내는 원소에는 $Na_2O$, $Al_2O_3$, $K_2O$, $SiO_2$, CaO, Ba, Sr 등이 있고, 증가하는 경향을 나타내는 원소에는 $Fe_2O_3$, MgO, MnO, Zr, Hf, Rb 등이 있다. 이러한 화학적 거동은 각력대가 대부분 석영, 장석류와 같은 주요 조암광물로 구성되는 반면, 비지대는 일라이트와 같은 점토광물이 다량 함유되는 것과 밀접한 관련성이 있다. 본 단층대에서는 기존 광물의 변질과 동시에 점토광물이 생성되는 데 있어 단층 활동에 수반된 유체활동이 큰 영향을 끼쳤다. 단층활동 초기에는 파쇄대가 열수의 통로로 작용하는 과정에서, 주원소 및 미량원소, 희토류원소는 기존 광물로부터 용탈되어 높은 원소 유동성을 나타내었으나, 파쇄대 중심부가 비지대로 점차 변화하는 과정에서는 이차적으로 형성된 점토광물로 인해 단층대의 투수성이 감소하고, 점토광물이 풍부해진 비지대 내에 농집되므로 낮은 원소 유동성을 가진 것으로 해석된다.

• 한국전기전자재료학회논문지
• /
• 제24권3호
• /
• pp.200-207
• /
• 2011

Abstract: The effect of lead free glass frit compositions on the properties of thick film conductor and resistor pastes were investigated. Two types lead free frits, HBF-A(without $Bi_2O_3$) and HBF-B(with $Bi_2O_3$) were made from $SiO_2$, $B_2O_3$, $Al_2O_3$, CaO, MgO, $Na_2O$, $K_2O$, ZnO, MnO, $ZrO_2$, $Bi_2O_3$. And Ag based conductor pastes and $RuO_2$ based resistor paste were prepared by mixed with these frits and functional phase(Ag and $RuO_2$), and organic vehicle. The properties of thick film conductor and resistor sintered at $850^{\circ}C$ were studied after printing on $Al_2O_3$ substrate. The morphology of the sintered films surface were SEM and EDS were carried out to analysis the chemical composition on resistor surface and state of Ru atom in frit matrix.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 추계학술대회 논문집
• /
• pp.48-48
• /
• 2009

최근 빠른 동작속도와 고 집적도를 얻기 위해 metal oxide semiconductor field effect transistor (MOSFET) 의 크기는 계속 해서 줄어들고 있다. 동시에 게이트의 절연층도 얇아지게 된다. 절연층으로 사용되는 $SiO_2$ 의 두께가 2nm 이하로 얇아 지게 되면 터널링에 의해 누설 전류가 발생하게 된다. 이 문제를 해결하기 위해 $SiO_2$ 를 대체할 고유전체 물질의 연구가 활발하다. 고유전체 물질 중에는 $ZrO_2,\;Al_2O_3,\;HfO_2$ 등이 많이 연구 되어 왔다. 하지만 유전상수 이외에 band gap energy, thermodynamic stability, recrystallization temperature 등의 특성이 좋지 않아 대체 물질로 문제점이 있다. 이를 보안하기 위해 산화물을 합금과 결합시키면 서로의 장점들이 합쳐져 기준들을 만족하는 물질을 만들 수 있고 $HfAlO_3$가 그 중 하나이다. Al를 첨가하는 이유는 문턱전압을 낮추기 위해서다. $HfAlO_3$는 유전상수 18.2, band gap energy 6.5 eV, recrystallization temperature 800 $^{\circ}C$이고 열역학적 특성이 안정적이다. 게이트 절연층은 전극과 기판사이에 적층구조를 이루고 있어 이방성인 드라이 에칭이 필요하고 공정 중 마스크물질과의 선택비가 높아야한다. 본 연구는 $HfAlO_3$박막을 $BCl_3/Ar,\;N_2/BCl_3/Ar$ 유도결합 플라즈마를 이용해 식각했다. 베이스 조건은 RF Power 500 W, DC-bias -100 V, 공정압력 15 mTorr, 기판온도 40 $^{\circ}C$ 이다. 가스비율, RF Power, DC-bias, 공정 압력에 의한 마스크물질과 의 선택비를 알아보았다.

• 센서학회지
• /
• 제15권3호
• /
• pp.168-172
• /
• 2006

Potentiometric $CO_{2}$ sensors were fabricated using a NASICON ($Na_{1+x}Zr_{2}Si_{X}P_{3-X}O_{12}$, 1.8 < x < 2.4) thick film and auxiliary layers. The powder of a precursor of NASICON with high purity was synthesized by a sol-gel method. By using the NASICON paste, an electrolyte was prepared on the alumina substrate by screen printing and then sintered at $1000^{\circ}C$ for 4 h. A series of $Na_{2}CO_{3}-CaCO_{3}$ auxiliary phases were deposited on the Pt sensing electrode. The electromotive force (emf) values were linearly dependent on the logarithm of $CO_{2}$ concentration in the range between 1,000 and 10,000 ppm. The device attached with $Na_{2}CO_{3}-CaCO_{3}$ (1:2 in mol.%) showed good sensing properties in the low temperatures.

• 한국재료학회지
• /
• 제17권1호
• /
• pp.18-24
• /
• 2007

Mullite-PSZ composite was prepared by sol-gel method using $Al(sec-OC_4H_9)_3,\;Si(OC_2H_5)_4,\;ZrOCl_2\;8H_2O\;and\;Y_2O_3$. The sinterability ana mechanical properties of powder compacts sintered at $1,650^{\circ}C$ for 4 hrs were investigated for various PSZ contents. In result Al-Si spinel formed at $980^{\circ}C$ from amorphous dried gel, and zirconia as well as mullite crystal formed above $1,200^{\circ}C$. The sintered body was densified to $97{\sim}98%$ except the specimen containing 25vol% PSZ which showed the relative density of about 95% obtained by sintering at $1,650^{\circ}C$ for 4 h. The flexural strength of the sintered body was a maximum value of 290 MPa in 20 vol% PSZ, which was also considerably larger than the value of 200 MPa without PSZ. The value of the fracture toughness increased linearly with increase of PSZ content and showed a maximum value of $4.3MPam^{1/2}$ in 25 vol% PSZ, Namely this value was remarkably larger than the $value(2.6MPam^{1/2})$ of pure mullite without PSZ.

• 한국세라믹학회지
• /
• 제35권10호
• /
• pp.1061-1069
• /
• 1998

The thermal instability of Al2TiO5 Ceramics was contrlled by solid solution with MgO SiO2 and ZrO2 through electrofusion in an arc furnace. The thermal expansion properties of Al2TiO5 composites show the hysteresis due to the strong anisotropy of The crystal axes of these material. These phenomena are ex-plained by the opening and closing of microcracks. The difference in microcracking temperatures e.g 587.6(ATG2), 405.9(ATG3) and 519.7$^{\circ}C$(ATG4) is caused by the difference in grain size and stabilizer type. The thermal shock behaviour under cyclic conditions between 750-1400-75$0^{\circ}C$ show no change in mi-crostructure and phase assemblage for all three stabilized specimens. After the thermal loading test at 110$0^{\circ}C$ for 100hrs. ATG1 and ATG2 materials decomposes completely to its components corundum and ru-tile in both cases. However with approximatelly 20% retention of the Al2TiO5 Thus in order to prevent decomposition of the stabilized material in the critical temperature range 800-130$0^{\circ}C$ it must be traversed within a short period of time.

• 동력기계공학회지
• /
• 제12권3호
• /
• pp.60-65
• /
• 2008

This study aims at investigating the wear properties of thermally sprayed $Al/Al_2O_3$ metal matrix composite(MMC) coating against different counterparts. $Al/Al_2O_3$ MMC coatings were fabricated using a flame spray system on an Al 6061 substrate. Dry sliding wear tests were performed using the sliding speeds of 0.2m/s and the applied loads of 1 and 2 N. AISI 52100, $Al_2O_3$, $Si_3N_4\;and\;ZrO_2$ balls(diameter: 8mm) were used as counterpart materials. Wear properties of $Al/Al_2O_3$ MMC coatings were analyzed using a scanning electron microscope(SEM) and energy dispersive X-ray spectroscopy (EDX). It was revealed that wear properties of $Al/Al_2O_3$ composite coatings were much influenced by counterpart materials. In the case of AISI 52100 used as counterparts, the wear rate of composites coating layer increased according to the increase of the applied load. On the contrary, in the case of ceramics used as counterparts, the wear rate of composites coating layer decreased according to the increase of the applied load.

• 자원환경지질
• /
• 제28권4호
• /
• pp.351-367
• /
• 1995

보포트-맥켄지 분지의 리인디어 D-27 시추공 시료에 대한 원소 지화학 및 산소동위원소 연구가 수행되었다. $K_2O$, Rb, 희토류원소의 함량 증가, Mg, Ti, Sc, Zn, Zr 등의 팔면체 원소의 감소, Be, V 등의 사면체 원소의 증가는 깊이에 따라 일라이트층의 구성비가 증가하는 일라이트/스멕타이트의 속성경향과 대비된다. 스멕타이트층과 일라이트층의 구조식은 각각 $[Al_{1.57}Fe_{.19}Mg_{.31}Ti_{.07}][Si_{3.84}A_{1.16}]O_{10}(OH)_2$와 $[Al_{1.84}Mg_{.16}][Si_{3.33}Al_{.67}]O_{10}(OH)_2$로 추정된다. 일라이트/스멕타이트의 속성과 연관하여 희토류원소의 유동이 관찰되었다. 희토류원소, 특히 La와 Ce의 깊이에 따른 함량 증가는 높은 전하가를 갖는 사면체 원소 ($V^{5+}$)의 유입과 관련이 있다. $V^{5+}$에 의한 잉여 전하는 부분적으로 낫은 전하가를 갖는 $Be^{2+}$에 의하여 상쇄되며, 또한 $Be^{2+}$에 의하여 발생되는 지엽적인 전하 불균형은 층간 이온으로는 높은 전하가 (+3)를 갖는 희토류 원소에 의하여 해소된다. 일라이트/스멕타이트의 ${\delta}^{18}O$가 (SMOW)는 2.91~15.72‰의 범위를 보이며, 걸프연안 등의 일라이트/스멕타이트와는 달리 깊이에 따라 증가한다. 일라이트/스멕타이트의 ${\delta}^{18}O$가의 증가는 공극수의 ${\delta}^{18}O$ 증가도가 깊이에 따라 증가하는 온도로 인한 동위원소 분별작용정수 (${\Delta}_{I/S-water}$)의 감소도보다 크기 때문이다. 일라이트/스멕타이트와 평형인 공극수의 ${\delta}^{18}O$가의 계산결과는 공극수의 근원이 지표수임을 지시한다. 중간 깊이에서 낮은 ${\delta}^{18}O$가를 보이는 450m 두께의 구간은 공극수가 층상화되어 있음을 의미한다. 그러나 이 깊이 구간이 낮은 일라이트층 구성비와 낮은 $K_2O$ 함량을 보이는 구간과 일치하지 않는 것으로 볼때 동위원소 교환 반응과 광물학적, 지화학적 반응은 서로 독립적으로 일어나는 것으로 해석된다.