• Journal of the Korean Ceramic Society
• /
• v.31 no.8
• /
• pp.879-885
• /
• 1994

Coprecipitation technique was used to synthesize ZrO2+12 mol% CeO2 powders with ZrOCl2.8H2O and Ce(NO3)3.6H2O as starting materials. The powders were dried on different conditions such as distilled water, ethanol, and azeotropic distillation. The powders prepared by azeotropic distillation showed weak aggregation of particles and the average particle size of powders calcined at 85$0^{\circ}C$ for 1 hour was 0.19 ${\mu}{\textrm}{m}$. The optimum sintering temperature and holding time are 130$0^{\circ}C$ and 2.5~10 hours, respectively. Beyond the optimum conditions, a phase transition from tetragonal to monoclinic causes to produce cracks in the sintered bodies and to decrease the density.

• Journal of the Korean Ceramic Society
• /
• v.34 no.1
• /
• pp.102-108
• /
• 1997

ZrO2 powders stabilized with Y2O3 and CeO2 of various compositions were prepared by the coprecipitation of water-soluble ZrOCl2.8H2O, YCl3.6H2O and Ce(NO3)3.6H2O, and their compacts were pressurelessly sintered at 1400 and 150$0^{\circ}C$ for 2hrs in air. 2mol% Y2O3-ZrO3 showed the most superior strength (1003MPa) and microhardness (12.6GPa), while 10 mol%CeO2-ZrO2 had the hightest toughness (13.3 MPa.m1/2) after sintering at 140$0^{\circ}C$. The addition of Y2O3 into Y2O3-ZrO3 decreased mean grain size and increased strength and hardness but decrease toughness. On the other hand, the addition of CeO2 into Y2O3-ZrO2 enhanced the stability of tetragonal phase during low-temperature aging for a long time under hydrothermal atmosphere.

• Journal of the Korean Ceramic Society
• /
• v.33 no.9
• /
• pp.1057-1063
• /
• 1996

Y2O3-CeO2-ZrO2 powders were prepared from water-soluble salts using a coprecipitation method. The forming process of oxide and the characteristics of the calcined powders treated in different drying conditions were investigated. The oxidation was occurred at the temperature of around 40$0^{\circ}C$ and the main crystallization of ZrO2 around $600^{\circ}C$. On calcination at $600^{\circ}C$ heating lamp-dried powders consisted of agglomerates of globular morphology with average agglomerate size of 2.27${\mu}{\textrm}{m}$ and specific surface area of 68.3m2/g and spray dried powders contained dense spheric particles with average agglomerate size of 1.35${\mu}{\textrm}{m}$ and specific surface area of 11.0m2/g which exhibited low agglomeration tendency. Removal of the water by a freeze-drying technique produced calcined powders containing flake-like secondary particle structures with wide agglomerate size distri-bution of 0.1-60${\mu}{\textrm}{m}$ and specific surface area of 24.5${\mu}{\textrm}{m}$. The 20 MPa-pressed density (36.8-41.4% T,D) of calcined powders did not nealy depend on drying methods whilst compaction ratio of calcined powders derived from freeze-drying was the highest ( 6.24) among three drying methods. On continuous heating up to 150$0^{\circ}C$ the sinterability of calcined powders derived from heating lamp-drying was superior to those derived from spray-and freeze-drying. The final sintered density of calcined powders was the highest (96% T,D at 150$0^{\circ}C$) in case of heating lamp-drying.

• Journal of the Korean Ceramic Society
• /
• v.36 no.12
• /
• pp.1390-1395
• /
• 1999

Zr(Y,Ce)O2 TZP ceramics were prepared by sintering compacts of 3 mol% Y2O3-TZP(3Y-TZP) powders with different amount of 12 mol% CeO2-TZP(12Ce-TZP) in air at 140$0^{\circ}C$ for 2 h. The phase changes microstructure and mechanical properties of Zr(Y. Ce)O2 TZP after hydrothermal aging(20$0^{\circ}C$ 5h) were investigated. Although an addition of 12Ce-TZP accelerated the grain growth of Zr(Y, Ce)O2 TZP it restrained the transformation of tetragonal to the monoclinic phase during aging. The degradation in mechanical properties of sintered bodies was governed by the formed monoclinic phase and chemical composition. Induced Vickers indentation crack was propagated intergranually. From SEM observation of the fracture surfaces the pull-out of individual grain was confirmed.

• Journal of the Korean Ceramic Society
• /
• v.33 no.10
• /
• pp.1177-1185
• /
• 1996

Y-TZP/Ce-TZP ceramics having relative sintered densities of>95% average grain sizes of 0.36$\mu\textrm{m}$ microhar-dness of 1150 kg/mm2 fracture strength of 390-830 MPa and toughness of 6.4-10.2 MPa$.$mm1/2 were prepared by conventional sintering of 3 mol% Y2O3-ZrO2 and 12 mol% CeO2-ZrO2 powders at 1400 and 1500$^{\circ}C$ The average grain sizes of Y-TZP/Ce-TZP ceramics were mainly governed by those of Ce-TZP. White increasing Ce-TZP content toughness increased while microhardness and fracture strength decreased. With comparing microhardness and toughness fracture strength was more sensitive on not only grain size but also other factors such as microstructural and compositional variations. The densification of Y-TZP/Ce-TZP cermaics was not greatly affected by composition and soaking time at temperature over 1400$^{\circ}C$ With increasing CE-TZP content the stability of t-ZrO2 decreased under thermal aging in air whereas increased in hydrothermal atmosphere and aqueous solution.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.113-113
• /
• 2003

고체전해질체로 사용되는 산소이온전도체로는 $Y_2$O$_3$ 안정화 ZrO$_2$가 널리 연구되어 왔고, 실질적으로 많이 사용되고 있다. 그러나 특히 대전력을 얻고자 하는 고체전해질 연료전지 분야에 있어서는 다른 재료를 찾고자 하는 많은 노력이 이루어지고 있다. 이에 CeO$_2$계 세라믹스는 ZrO$_2$계보다 낮은 온도에서 더 높은 이온전도도를 가지고 있어 많은 주목을 받고 있다. 그러나 이 CeO$_2$계를 소결시키는 데는 1$600^{\circ}C$이상의 고온을 필요로 한다. 이 런 고온의 소결온도를 낮추기 위한 방안으로는 균일하고 미세한 출발원료를 사용하거나 소결조제를 첨가하는 것 등이 있다. 균일하고 미세한 출발원료를 제조하는 연구는 국내외에서 많이 이루어지고 있으나 소결조제 첨가에 대한 연구는 별로 이루어진게 없다. 다만 국외에서 Co$_3$O$_4$, Fe$_2$O$_3$, CoO 첨가에 의한 연구가 최근에 이루어지고 있으며, 본 연구실을 중심으로 Ga$_2$O$_3$, $Al_2$O$_3$ 첨가에 대한 연구가 이루어지고 있다. 본 연구실에서는 그간 공침법으로 제조되는 소결조제 첨가 Gd$_2$O$_3$-doped CeO$_2$ 분말을 사용하여 소결조제 첨가효과를 살펴보았다.

• Proceedings of the Korea Association of Crystal Growth Conference
• /
• 1996.06b
• /
• pp.55-85
• /
• 1996

지르코니아 분말은 ZrO2 결정상이 온도변화에 따라 부피변화를 수반하는 상전이변태를 나타낸다. 단사정 ZrO2가 110$0^{\circ}C$에서는 정방정으로, 2$700^{\circ}C$ 내외에서는 입방정으로 결정구조가 가역적으로 변한다. 이 ZrO2에 금속산화물을 고용시키면 형석 (CaF2:Florite)형의 입방정 결정구조가 실온에서도 안정하게 존재하게 된다. 안정화제 산화물은 caO, MgO등 2가 산화물외에 3가 또는 4가의 금속산화물로서 Sc2O3, Y2O3, Sm2O3, Nd2O3, Gd2O3, Y2O3, CeO2 등이며 이들은 금속이온의 원자가가 변하기 쉬운 희토류 산화물이다. 안정화 지르코니아는 형석형 결정구조이며 결정화학적으로 보면 금속양이온이 산소이온에 대해서 정육면체형의 8배위를 하고 있다. 이때 이온반경비(양이온/음이온)에 따라 Zr+4자리와 O-2자리의 격자위치와 모양이 형성되므로 비틀어진 정육면체구조이건 이상적인 정육면체 형석구조를 이룬다. 이는 지르코니아의 결정상의 2상-3상인 부분안정화 지르코니아다결정체(PSZ : partially stabilized zirconia)이거나 단일상-2상인 정방정 지르코니아다결정체(TZP : tetragonal zirconia polycrystal)의 결정구조를 가지는데 기인한다. PSZ는 주로 MgO, CaO를 안정화제로 고용시켜 입방정 영역에서 소결하고 이를 다시 입방정과 정방정의 상 영역에서 열처리하여 입방정 입자내부에 정방정을 석출 형성시킨 것이며 TZP는 Y2O3 및 CeO2를 고용시켜 PSZ와 다르게 일반적인 상압소결한 정방정 결정상의 미립자이다. 산화지르코늄 분말은 지르콘사에서 열분해시킨 지르코늄소결.융해괴(caustic fusion clinker)를 산처리하여얻어진 지르코늄산용액(zirconyl acid solution : cloride, sulfide, nitride 등)으로부터 제조된다. 고순도 산화지르코늄은 용액 결정석출법에 의해 ZrOCl2.8H2O, 5ZrO2.3SO3.15H2O, ZrO(NO3)2.xH2O 등의 지르코늄 수화물만을 재결정화시킨 것으로부터 얻을 수 있으며 이 지르코늄염 수용액으로부터 입자미세구조를 효과적으로 제어하여 산화지르코늄 및 안정화 지르코니아 분말제조가 가능하다. 안정화 지르코니아 분말은 ZrO2와 안정화산화물의 고용을위하여 가열처리를 필요로 하며 일정온도에서 최적상태로 숙성하므로서 2가지 상(phase) 이상의 고용체를 가지게 된다. 안정화 지르코니아 분말은 고용처리온도를 낮추고 효과적으로 생성시키기 위해서는 지르코늄 및 안정화제염을 혼합하고 습식 직접합성하여 저온에서 고용체의 합해진상 영역을 생성시키는 것이다. 이는 지르코니아 원료분말의 미세구조를 제어하므로서 가능하며 이때 화학성분조성과 크기형태가 균일하게 분포된 입자분말을 얻을 수 있다.

• Journal of Korean Society on Water Environment
• /
• v.31 no.6
• /
• pp.632-636
• /
• 2015

This study aims to evaluate arsenic adsorption efficiencies over various metal oxides (CeO₂, TiO₂, Fe₃O₄, ZrO₂, AlOOH, SiO₂, α-Al₂O₃, and γ-Al₂O₃) and investigate the correlation between physico-chemical characteristics of metal oxides and their efficiencies. From XPS, XRD BET analysis and isotherm adsorption test, TiO₂ powder showed that the best adsorption efficiency, and it's mechanism was highly depended on the chemical adsorption.

• Journal of the Korean Ceramic Society
• /
• v.43 no.6 s.289
• /
• pp.369-375
• /
• 2006

[ $(Ba_{0.5}Sr_{0.5})_{0.99}Co_{x}Fe_{1-x}O_{3-{\delta}}$ ] [x=0.8, 0.2](BSCF) powders were synthesized by a Glycine-Nitrate Process (GNP) and the electrochemical performance of the BSCF cathode on a scandia stabilized zirconia, $[(Sc_{2}O_3)_{0.11}(ZrO_2)_{0.89}]-1Al_{2}O_3$ was investigated. In order to prevent unfavorable solid-state reactions between the cathode and zirconia electrolyte, a GDC ($Gd_{0.1}Ce_{0.9}O_{2-{delta}}$) buffer layer was applied on ScSZ. The BSCF (x = 0.8) cathode formed on GDC(Buffer)/ScSZ(Disk) showed poor electrochemical property, because the BSCF cathode layer peeled off after the heat-treatment. On the other hand, there were no delamination or peel off between the BSCF and GDC buffer layer, and the BSCF (x = 0.2) cathode exhibited fairly good electrochemical performances. It was considered that the observed phenomenon was associated with the thermal expansion mismatch between the cathode and buffer layer. The ohmic resistance of the double layer cathode was slightly lower than that of the single layer BSCF cathode due to the incorporation of platinum particle into the BSCF second layer.