• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제55권7호
• /
• pp.349-353
• /
• 2006

[ $TiO_2-Nb_2O_5$ ] sol was prepared using sol-gel method. Crystalline properties of gel powder changed from rutile phase to anatase phase with increasing $Nb_2O_5$ additives at $800^{\circ}C$, while they retained rutile phase regardless of $Nb_2O_5$ additives at $900^{\circ}C,\;1,000^{\circ}C$. They retained amorphous phase from $50^{\circ}C\;to\;400^{\circ}C$, retained anatase phase from $500^{\circ}C\;to\;600^{\circ}C$ and had rutile phase over $700^{\circ}C$ at 1mole% $Nb_2O_5$ additive. After $TiO_2-Nb_2O_5$ sol retained low viscosity with normal chain structure for a long time, its viscosity increased fast with network structure. DTA properties of gel powder had endothermic reaction due to evaporation of propanol and water about $78^{\circ}C$, had exothermic reaction due to propanol combustion about $290^{\circ}C$ and had exothermic reaction due to changing of $TiO_2$ phase about $640^{\circ}C$.

• 한국에너지공학회:학술대회논문집
• /
• 한국에너지공학회 1995년도 춘계학술발표회 초록집
• /
• pp.45-52
• /
• 1995

광 촉매로 널리 알려진 TiO$_2$의 광 분해 거동의 변화를 관찰하기 위하여 Nb$_2$O$_{5}$를 첨가하여 sol-gel 용법으로 제조한 후 DCA(dichloroacetic acid) 의 광분해 효율을 측정하였다. Sol-gel process 과정에서 첨가된 Nb$_2$O$_{5}$의 농도 및 열처리 온도변화에 따른 광분해 효율을 관찰한 결과, Nb$_2$O$_{5}$를 첨가한 후 40$0^{\circ}C$에서 한시간 동안 열처리 한 광 촉매의 광분해 효율이 가장 높게 나타났다. 또한 열처리 온도와 무관하게 Nb$_2$O$_{5}$의 양이 증가할수록 광분해 효율은 감소하는 것으로 관찰되었다. 이는 excess electron 의 증가로 환원 반응 혹은 recombination rate기 증가하기 때문이라고 사료된다. 분해 대상 물질의 pH가 낮을수록 광분해 효율이 증가하는 것을 알 수 있었다.알 수 있었다.

• E2M - 전기 전자와 첨단 소재
• /
• 제9권10호
• /
• pp.991-1000
• /
• 1996

PbTiO$_{3}$-PbZrO$_{3}$-Pb(Ni$_{1}$3/Nb$_{2}$3/O$_{3}$) (PZT-PNN) thin films were prepared from corresponding metal organics partially stabilized with diethanolamine by the sol-gel spin coating method. Each mol ratio of PT:PZ:PNN solutions were #1(50:40:10), #2(50:30:20), #3(45:35:20), #4(40:40:20), #5(40:50:10), #6(35:45:20) and #7(30:50:20) respectively. The spin-coated PZT-PNN films were heat-treated at 350.deg. C for decomposition of residual organics, and were sintered from 450.deg. C to 750.deg. C for crystallization. The substrates, such as Pt and Pt/TiN/Ti/TiN/Si were used for the spin coating of PZT PNN films. The perovskite phase was observed in the PZT-PNN films heat-treated at 500.deg. C. The crystalline of the PZT-PNN films was optimized at the sintering of 700.deg. C. By the result of AES analysis, It is confirmed that the films of TiN/Ti/TiN was a good diffusion barrier and that co-diffusion into the each films was not observed.

• 한국세라믹학회지
• /
• 제40권3호
• /
• pp.279-285
• /
• 2003

Sol-gel 법으로 200 nm 정도의 두께를 가진 강유전성 S $r_{0.9}$B $i_{2.1}$T $a_{1.8}$ N $b_{0.2}$ 박막을 Pt/Ti $O_2$/ $SiO_2$/Si 기판 위에 증착하였다. 본 실험에서는 Sr(O $C_2$ $H_{5}$)$_2$, Bi(TMHD)$_3$, Ta(O $C_2$ $H_{5}$)$_{5}$ 그리고, Nb(O $C_2$ $H_{5}$)$_{5}$를 출발 물질로 사용하였으며 2-methoxyethanol을 용매로 사용하였다. UV 노광과 급속열처리가 SBTN 박막의 구조와 전기적 특성에 어떤 영향을 주는 가를 연구하였다. UV 노광과 급속열처리를 한 후에 $650^{\circ}C$ 열처리한 SBTN 박막의 3V와 5V 인가 전압하에서의 잔류분극 값은 각각 8.49와 11.94 $\mu$C/$ extrm{cm}^2$이었다.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2006년도 학술대회 논문집 전문대학교육위원
• /
• pp.167-170
• /
• 2006

$TiO_{2}-Nb_{2}O_{5}$ sol was prepared using sol-gel method. DTA properties of gel powder had endothermic reaction due to evaporation of propanol and water about $78^{\circ}C$, had exothermic reaction due to propanol combustion about $290^{\circ}C$ and had exothermic reaction due to changing of $TiO_2$ phase about $640^{\circ}C$. Capacitance of thin films increased according to increasing relative humidity, whereas it decreased according to increasing measured frequency.

• 한국재료학회지
• /
• 제13권5호
• /
• pp.317-322
• /
• 2003

Bismuth layered structure ferroelectric thin films, $Bi_4$$Ti_3$$O_{12}$ / (BTO) and Nb-doped BTO (BTN) were prepared on the Pt(111)/Ti/$SiO_2$/Si(100) substrates by a sol-gel route. We investigated the Nb-doping effect on the grain orientation and ferroelectric properties. $Nb^{5＋}$ ion substitution for $Ti^{4＋}$ ion in perovskite layers of BTO decreased the degree of c-axis orientation and increased the remanent polarization (2Pr). The fatigue resistance of Nb-doped BTO thin film was shown to be superior to that of BTO, and the leakage current of Nb-doped BTO thin film was decreased about 1 order of magnitude compared with BTO. The improvement of ferroelectric properties with $Nb^{5＋}$ doping in BTO could be attributed to the changes in space charge densities and grain orientation in the thin film.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1993년도 하계학술대회 논문집 B
• /
• pp.1150-1152
• /
• 1993

$TiO_2-Nb_2O_5$ thin films are fabricated by Sol-Gel method and their electrical properties have been investigated. The crystalline form is amorphous under $400^{\circ}C$ and is anatase over $500^{\circ}C$. The surface conductivity of films is higher that of $500^{\circ}C$ than that of $600^{\circ}C$.

• 멤브레인
• /
• 제4권3호
• /
• pp.152-162
• /
• 1994

광촉매 $TiO_2$ 막에 의한 formic acid의 광분해 효율이 연구되었다. 막반응기는 용액의 정밀여과(micro-filtration)는 물론 유기물의 광분해를 동시에 수행할 수 있도록 다공성 $TiO_2$ 튜브 (평균기공: $0.2{\mu}m$)를 이용한 새로운 타입으로 개발되었으며 광원으로는 365 nm 파장을 갖는 UV를 사용하였다. 또한 반응기의 광분해 효율을 증진시키기 위하여 슬립케스팅법으로 제조한 $TiO_2$ 튜브표면을 $TiO_2$ 졸로 코팅하였다. $TiO_2$ 막 반응기의 분해효율은 용액의 투과량(flux), 막의 미세구조(졸의 pH), 공급산소량, $H_2O_2$와 같은 1차 산화제(primary oxidants)의 첨가 그리고 $Nb_2O_5$와 같은 물질의 도핑(doping)에 매우 민감함을 알 수 있었다. 최적의 광분해 반응조건에서 formic acid의 산화효율은 pH가 1.45인 $TiO_2$ 졸로 코팅한 막 반응기를 사용했을때 80% 이상이었다. Formic acid 용액에 1차 산화제 $H_2O_2$를 첨가하거나 막을 $Fe_2O_3$로 도핑함으로써 산화효율은 최고 20%까지 증가시킬 수 있었다.

• 한국결정성장학회지
• /
• 제11권1호
• /
• pp.27-32
• /
• 2001

본 연구에서는 금속 알콕시드를 이용하여 졸-겔법으로 0.9PMN-0.1PT 분말을 합성하는데 있어 과량으로 첨가되는 ${Mg(OC_{2}H_{5})}_2$와 ${Pb(CH_{3}COO)}_2.3H_{2}O$ 등이 페로브스카이트 상의 생성량에 미치는 영향을 검토하였다. 그결과 합성된 겔을 열처리할 때 하소 온도가 증가함에 따라 페로브스카이트 상의 생성량은 증가하였으며 $850^{\circ}C$에서 4시간 유지하여 하소한 경우 페로브스카이트 생성량이 최대인 것으로 나타났다. 0.9PMN-0.1PT 조성에 ${Mg(OC_{2}H_{5})}_2$를 5 wt% 과잉 첨가한 합성 분말에서 페로브스카이트 단일상을 얻을 수 있었다.

• 한국재료학회지
• /
• 제14권9호
• /
• pp.634-641
• /
• 2004

The photocatalytic performance of $TiO_2$ thin films coated on porous alumina balls using various aqueous $TiOCl_2$ solutions as starting precursors, to which 1.0 $mol\%$ transition metal ($Ni^{2+},\;Cr^{3+},\;Fe^{3+},\;Nb^{3+},\;and\;V^{5+}$) chlorides had been already added, has been investigated, together with characterizations for $TiO_2$ sols synthesized simultaneously in the same autoclave through hydrothermal method. The synthesized $TiO_2$ sols were all formed with an anatase phase, and their particle size was between several nm and 30 nm showing ${\zeta}-potential$ of $-25{\sim}-35$ mV, being maintained stable for over 6 months. However, the $TiO_2$ sol added with Cr had a much lower value of -potential and larger particle sizes. The coated $TiO_2$ thin films had almost the same shape and size as those of the sol. The pure $TiO_2$ sol showed the highest optical absorption in the ultraviolet light region, and other $TiO_2$ sols containing $Cr^{3+},\;Fe^{3+}\;and\;Ni^{2+}$ showed higher optical absorption than pure sol in the visible light region. According to the experiments for removal of a gas-phase benzene, the pure $TiO_2$ film showed the highest photo dissociation rate in the ultraviolet light region, but in artificial sunlight the photo dissociation rate of $TiO_2$ coated films containing $Cr^{3+},\;Fe^{3+}\;and\;Ni^{2+}$ was measured higher together with the increase of optical absorption by doping.