• Journal of the Korean Ceramic Society
• /
• v.38 no.3
• /
• pp.245-250
• /
• 2001

BaO-TiO$_2$계의 TiO$_2$-rich 조성영역에 대한 상평형 관계를 완전 고상 반응법을 통하여 재평가하였다. 출발 시료로는 이 계의 end-member인 BaO와 TiO$_2$(rutile)를 이용하였다. 각 시료들은 대기 중에서 800~120$0^{\circ}C$의 온도구간에서 선택적으로 열처리되었다. 열처리된 시편들은 상온까지 급냉 처리되었으며, 상 분석은 X-ray 회절 분석을 통하여 이루어졌다. 연구결과에서 BaTi$_2$O$_{5}$(1:2)상과 BaTi$_{5}$O$_{11}$(1:5)상이 저온에서의 고상 반응을 통해서도 쉽게 형성될 수 있음을 알 수 있었으며, 각 저온 상들의 불변 반응 온도를 열처리 온도에 따른 상 분석을 통하여 확인할 수 있었다.

• Journal of Sensor Science and Technology
• /
• v.7 no.2
• /
• pp.83-89
• /
• 1998

$TiO_{2-x}$ thin film humidity sensors have been fabricated by sputtering method and their physical and hygroscopic characteristics have been investigated. The sputtering conditions and sintering conditions affect the sensor's sensitivity toward humidity. AES and SEM micrographs were taken for the analysis of crystal structures, surface morphology caused by adsorbed water vapour. $TiO_{2-x}$ humidity sensors showed negative impedance-humidity characteristics and the sensor which was fabricated by experimental condition 2(rf power of 200W) showed higher sensitivity and linearity than others. Then the slope of the sensor was about $0.794\;K{\Omega}/%RH$ and the response time of $TiO_{2-x}$ humidity sensors was about 2 min. for adsorption and about 3 min. for desorption at the operating temperature of $30^{\circ}C$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.05b
• /
• pp.78-81
• /
• 2002

Ferroelectric thin film is a very attractive material for the tunable microwave device applications such as electronically tunable mixers, delay lines, filters and phase shifters. Thin films of $Pb_{x}Sr_{1-x}TiO3(PST)$ were fabricated onto Pt/Ti/SiO2/Si substrate by the sol-gel method. We have investigated the structural and dielectric properties of PST(50/50) thin films for tunable microwave device applications. The PST thin films show typical polycrystalline structure with a dense microstructure without secondary phase formation. Dielectric properties of PST films are strongly dependent on annealing temperature. The dielectric constants, loss and tunability of the PST (50/50) thin films were 404, 0.023 and 51.73 %, respectively.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.50 no.10
• /
• pp.504-508
• /
• 2001

The$(Sr_{1-x}Ca_x)TiO_3$(SCT) thin films are deposited on Pt-coated electrode $(Pt-TiN /SiO_2Si)$ using RF sputtering method at various deposition temperature. The crystallinity of thin films was increased with increased of deposition temperature n the temperature range of 200~500 $[^{\circ}C]$. The capacitance changes almost linearly in temperature ranges of -80~+90$[^{\circ}C]$. All SCT thin films used in the study the phenomena of dielectric relaxation with the increase of frequency, and the relaxation frequency is observed above 200[kHz]. V-I characteristics of SCT thin films show the increasing leakage current with the increases of deposition temperature.

• Applied Chemistry for Engineering
• /
• v.26 no.2
• /
• pp.193-198
• /
• 2015

Ceria supported on various commercial $TiO_2$ catalysts were prepared by wet-impregnation method. We confirmed that the correlation between physicochemical properties of $TiO_2$ supports and SCR activities. Physicochemical properties of the various $TiO_2$ were evaluated using X-ray diffraction (XRD), Brunauer-Emmett-Teller (BET) surface area, X-ray photoelectron spectroscopy (XPS), and pH analysis. Ce/Ti catalyst exhibited different SCR activities with respect to physicochemical properties of $TiO_2$. An excellent activity was obtained as the surface area of $TiO_2$ increased. In the case of CeOx surface density, the excellent activity in a range of $2.5{\sim}14.5CeOx/nm^2$ was achieved and the activity tended to decrease above $14.5CeOx/nm^2$. The O/Ti mole ratio of $TiO_2$ in the range of 1.32 to 1.79 showed an excellent SCR activity. It was also confirmed that the pH of the $TiO_2$ has no effects on the SCR activity. In order to achieve excellent SCR activities, ceria oxide should be supported on $TiO_2$ possessing a high specific surface area and certain O/Ti mole ratio. In addition, the catalyst with the low CeOx surface density resulted from the high dispersed ceria oxide should be prepared.

• Applied Chemistry for Engineering
• /
• v.28 no.5
• /
• pp.547-553
• /
• 2017

This study focused on the difference of photocatalytic performance by the incorporation of Pd into the $TiO_2$ framework and suggested five different catalysts composed of $TiO_2$ and x mol% $Pd-TiO_2$ (x = 0.25, 0.5, 0.75, and 1.0). A typical sol-gel method was used to synthesize catalysts, and the phenol photodegradation performance of each catalysts was evaluated. The physicochemical and optical properties of catalysts were confirmed by X-ray diffraction (XRD), transmission electron microscopy (TEM), scanning electron microscopy/energy dispersive spectrometer (SEM/EDS), ultraviolet/visible spectroscopy (UV/Vis), photoluminescence spectroscopy (PL), and photocurrent measurements. With the addition of Pd ions, the band gap of catalysts was shortened and the charge separation between photogenerated electrons and holes easily also occurred. As a result, the phenol photo-destruction performance over 0.75 mol% $Pd-TiO_2$ catalyst was 3 times higher than that of pure $TiO_2$. This is believed to be due to Pd ions acted as an electron capturing function during photocatalysis.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.119-119
• /
• 2016

Over the last years the anodic formation of ordered $TiO_2$ nanotube layers has created significant scientific interest. Titanium oxide nanotube formation on the titanium or titanium alloy surface is expected to be important to improve cell adhesion and proliferation under clinical conditions. It should be possible to control the nanotube size and morphology for biomedical implant use by controlling the applied voltage, alloying element, current density, anodization time, and electrolyte. $TiO_2$ nanotubes show excellent biocompatibility, and the open volume in the tubes may be exploited as a drug release platform and so on. Therefore, in this study, Nanotube shape on the Ti-29Nb-xHf alloys with applied potentials was reserched. $TiO_2$ nanotube formation on Ti-29Nb-xHf alloys was carried out using anodization technique as a function of applied DC potential (10 V to 30 V and 30 V to 10 V) and anodization time for 60~120 min in $1MH_3PO_4$ with small additions of (0.8 wt. %, to 1.2 wt. %) NaF. The morphology change of anodized Ti-29Nb-xHf alloys was determined by FE-SEM, XRD, and EDS.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1997.05a
• /
• pp.62-62
• /
• 1997

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.31A no.9
• /
• pp.89-95
• /
• 1994

BaTiO$_{x}$ thin film as insulator and ZnS:Mn film as phosphour layer for thin film electrouminescent device have been deposited by thermal evalporation and dependence of electrical and opeical characeristics have been studied. The optimum deposition conditions for the BaTiO$_{x}$ thin film are such that BaTiO$_{3}$/TiO$_{2}$ mixing ratio was 0.7, sub strate temperature was 100 $^{\circ}C$ and annealing time was 1 hour at 300 $^{\circ}C$. In this case, the dielectric constant of BaTiO$_{x}$ thin film fabricated under those optimum conditions was 26, and for AnS:Mn thin films, the crystallization was done well and the deposition rate was 1300 $\AA$/min when substrate temperature was 200$^{\circ}C$. Thin film Electroluminescent devices were fabricated using BaTiO$_{x}$ and AnS:Mn thin films. The luminescence threshold voltage of device was 41.5 V and brightness was 1.2${\mu}W/cm^{2}$ at appied voltage of 50 V.

• 한국전자현미경학회:학술대회논문집
• /
• 2004.05a
• /
• pp.80-83
• /
• 2004