• Korean Journal of Materials Research
• /
• v.11 no.1
• /
• pp.44-47
• /
• 2001

Effects of $Er_2O_3$ addition on the dielectric properties of non-reducible $BaTi_3$-based X7R dielectrics with Ni electrode have been studied in reducing atmosphere. X7R with moderate temperature-dependence was developed after addition of $Er_2O_3$ with $MnO_2-MgO$; room-temperature dielectric constant and dissipation factor were >2900 and < 1.0%, respectively. The addition of $Er_2O_3$ greater than 3.0 mol% improved the temperature dependence of dielectric properties, but a significant decrease of the dielectric constant at room-temperature was observed. The TCC curves rebated clockwise with increasing MnO$_2$ content at a given additive system, 1.5 mol% $Er_2O_3$ and 2.0 mol% MgO.

• Applied Microscopy
• /
• v.34 no.2
• /
• pp.113-120
• /
• 2004

Microstructural characteristics of the Complex Perovskite (1-x) $(Li_{1/2}Sm_{1/2})TiO_3-x (Na_{1/2}Sm_{1/2})TiO_3$ (LNST) system have been investigated using the transmission electron microscopy (TEM). When $0.0{\leq}x{\leq}0.6$, the vacancy ordering forming the 1/2 (001) superlattice reflections due to the A-site cation deficiencies has apperaed. It could be confirmed by presence of ABPs. But it was difficult to form the vacancy ordering since vacancy concentration gradually lowered as the amount of the substituted Li ions decrease. Antiphase boundaries (APBs) were presented in microstructures of LNST when $0.8{\leq}x{\leq}1.0$. It was considered that these boundaries were caused by the 1:1 chemical ordering of A-site cations, Na and Sm ions. LNST had not only the antiphase tilting of oxygen octahedron but also the inphase tilting of oxygen octahedron and the antiparallel shift of cations all of them. It could be confirmed by presence of ferroelastic domains

• Journal of the Korean Ceramic Society
• /
• v.40 no.1
• /
• pp.81-86
• /
• 2003

Microwave dielectric properties have been investigated in the$(1-x)CaTiO_3-xYAlO_3$ (x=0.1~1.0) solid solution system. The mixtures of $CaTiO_3$ and $YalO_3$using solid state method were sintered at various temperatures. Their dielectric constants and related temperature coefficients were strongly depend on the composition of the solid solution. The optimum properties were recorded as for ${\varepsilon}_r=47,$ $Q{\times}f_0$=35000 and ${\tau}_f=+11ppm/^{\circ}C$ without sintering agent. Even at $1200^{\circ}C$ full densification has been achieved with addition of $CaB_2O_4$ in the $0.75CaTiO_3-0.25YalO_3$ composition. The sample of $0.3 wt%-CaB_2O_4$ added $ 0.75CaTiO_3-0.25YalO_3$ sintered at $1300^{\circ}C$ for 3 h showed optimum microwave dielectric properties of ${\varepsilon}_r=47$, $Q{\time}f_0=37000$ and ${\tau}_f=+17ppm/^{\circ}C$, which demonstrates the promising candidates for microwave dielectric materials covering 5~7 GHz range.

• Journal of the Korean GEO-environmental Society
• /
• v.15 no.1
• /
• pp.63-68
• /
• 2014

In this study, it was found that determined the photocatalytic degradation of antibiotics (lincomycin, LM) with various catalyst composite of titanium dioxide ($TiO_2$), hydroxyapatite (HAP) and germanium (Ge) under UV-A irradiation. At first, various type of complex catalysts were investigated to compare the enhanced photocatalytic potential. It was observed that in order to obtain the removal efficiencies were $TiO_2/HAP/Ge$ > $TiO_2/Ge$ > $TiO_2/HAP$. The composition of $TiO_2/HAP/Ge$ using a statistical approach based on mixture analysis design, one of response surface method was investigated. The independent variables of $TiO_2$ ($X_1$), HAP ($X_2$) and Ge ($X_3$) which consisted of 6 condition in each variables was set up to determine the effects on LM ($Y_1$) and TOC ($Y_2$) degradation. Regression analysis on analysis of variance (ANOVA) showed significant p-value (p < 0.05) and high coefficients for determination value ($R^2$ of $Y_1=99.28%$ and $R^2$ of $Y_2=98.91%$). Contour plot and response curve showed that the effects of $TiO_2/HAP/Ge$ composition for LM degradation under UV-A irradiation. And the estimated optimal composition for TOC removal ($Y_2$) were $X_1=0.6913$, $X_2=0.2313$ and $X_3=0.0756$ by coded value. By comparison with actual applications, the experimental results were found to be in good agreement with the model's predictions, with mean results for LM and TOC removal of 99.2% and 49.3%, respectively.

• Korean Journal of Materials Research
• /
• v.11 no.8
• /
• pp.708-712
• /
• 2001

Microwave dielectric properties of $(Pb_{0.2}Ca_{0.8})[(Ca_{1/3}Nb{2/3})_{1-x}Ti_x]O_3$ ceramics were investigated as a function of $Ti^{4+}$ content (0.05$\leq$x$\leq$0.35). A single perovskite phase was obtained from x=0.05 to x=0.15, and $TiO_2$ and $CaNb_2O^6$ were detected as a secondary phase beyond x=0.2. The structure was changed from orthorhombic at x=0.05 to cubic at x=0.35. Dielectric constant(K) was increased with increase of $Ti^{4+}$ content due to increase of rattling effect, and was inversely proportional to the cube of the average radius of B-site cation, however, Qf value was decreased, which was due to the decrease of grain size and the secondary phase. With the increase of $Ti^{4+}$ content, the temperature coefficient of resonant frequency(TCF) was controlled from -27.36 ppm/$^{\circ}C$ value to +18.4 ppm/$^{\circ}C$ value, which was caused by the influence of tolerance factor(t) and the bond valence of B-site. Typically, K of 51.67, Qf of 7268(GHz), TCF of 0 ppm/$^{\circ}C$ were obtained in the $(Pb_{0.2}Ca_{0.8})[(Ca_{1/3}Nb_{2/3})_{0.8}Ti_0.2]O_3$ sintered at 13$50^{\circ}C$ for 3h.

• Bulletin of the Korean Chemical Society
• /
• v.33 no.10
• /
• pp.3407-3412
• /
• 2012

The Ti incorporation at Fe-site in the double perovskite lattice of $Sr_2FeNbO_6$ (SFNO) system is studied. The Ti concentration optimization yielded an efficient photocatalyst. At an optimum composition of Ti as x = 0.07 in $Sr_2Fe_{1-x}Ti_xNbO_6$, the photocatalyst exhibited 2 times the quantum yield for photolysis of $H_2O$ in presence of $CH_3OH$, than its undoped counterpart under visible light (${\lambda}{\geq}420nm$). Heavily Ti-doped $Sr_2Fe_{1-x}Ti_xNbO_6$ lattice exhibited poor photochemical properties due to the existence of constituent impurity phases as observed in the structural characterization, as well as deteriorated optical absorption. The higher electron-density acquired by n-type doping seem to be responsible for the more efficient charge separation in $Sr_2Fe_{1-x}Ti_xNbO_6$ (0.05 < x < 0.4) and thus consequently displays higher photocatalytic activity. The Ti incorporated structure also found to yield stable photocatalyst.

• Journal of the Korean Ceramic Society
• /
• v.43 no.1 s.284
• /
• pp.55-61
• /
• 2006

The microwave dielectric properties and low temperature sintering of $Ca[Ti_{1-x}(Ni_{1/3}Nb_{2/3})_x]O_3$ system were investigated at the sintering temperature $1,200\~1,350^{\circ}C$. The density and quality factors $(Q{\times}f)$ increased while dielectric constants slightly decreased with the decrease of Ti. The dielectric constant, quality factor, and temperature coefficient of resonance frequency $(\tau_f)$ were 64, 17,000 GHz, and $-9.1\;ppm/^{\circ}C$ respectively, when $CaTi_{1/2}(Ni_{1/3}Nb_{2/3})_{1/2}O_3$ ceramics were sintered at $1,300^{\circ}C$ for 4 h. $2Li_2O-B_2O_3$ was added to $CaTi_{1/2}(Ni_{1/3}Nb_{2/3})_{1/2}O_3$ to decrease the sintering temperature for LTCC application. The microwave dielectric properties of the samples sintered at $925^{\circ}C$ for 2 h with the addition of $6\;wt\%\;2Li_2O-B_2O_3$ were $\varepsilon_r=48.7,\;Q{\times}f=8,460\;GHz$, and $\tau_f=+5.6ppm/^{\circ}C$. Compatibility test of the composition with silver electrode shows no reaction with silver electrode, implying the feasibility as a high-K LTCC material.

• Journal of Environmental Science International
• /
• v.15 no.4
• /
• pp.333-340
• /
• 2006

A (5 wt.%)Mn-(1 wt.%)$V_{2}O_{5}/TiO_{2}$ catalyst were prepared by co-precipitation method and used for low-temperature selective catalytic reduction (SCR) of $NO_x$ with ammonia in the presence of oxygen. The properties of the catalysts were studied by X-ray diffraction (XRD), temperature programmed reduction (TPR) and scanning electron microscope-energy dispersive X-ray spectroscopy (SEM-EDS). The experimental results showed that (5 wt.%)Mn-(1 wt.%)$V_{2}O_{5}/TiO_{2}$ catalyst yielded 81% NO conversion at temperature as low as $150^{\circ}C$ and a space velocity of $2,400\;h^{-1}$. Crystalline phase of $Mn_{2}O_3$ was present at ${\ge}\;15%$ Mn on $V_{2}O_{5}/TiO_{2}$. XRD confirmed the presence of manganese oxide ($Mn_{2}O_{3}$) at $2{\theta}=32.978^{\circ}(222)$. The XRD patterns presented of (5 wt.%)Mn-(1 wt.%)$V_{2}O_{5}/TiO_{2}$ did not show intense or sharp peaks for manganese oxides and vanadia oxides. The TPR profiles of (5 wt.%)Mn-(1 wt.%)$V_{2}O_{5}/TiO_{2}$ catalyst showed main reduction peat of a maximum at $595^{\circ}C$.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.171-171
• /
• 2003

공정기술의 향상으로 DRAM(dynamic random acess memory)의 고집적화가 이루어지고 있으며, 각 개별소자 및 셀 영역의 점유면적의 감소가 요구되어지고 있다. 따라서 기존에 사용하던 NO (Si$_3$N$_4$/SiO$_2$)박막보다 유전율이 높은 고유전물질에 대한 연구가 진행되고 있다. Ta$_2$O$_{5}$, $Y_2$O$_3$, HfO$_2$, ZrO$_2$,Nb$_2$O$_{5}$, BaTiO$_3$, SrTiO$_3$ 및 (BaSr)TiO등이 고유전물질로 연구되고 있는데 그 중 공정의 안정성, 누설전류의 우수성으로 인해 Ta$_2$O$_{5}$이 많이 연구되고 있다. 본 실험에서는 TiO$_2$가 8 mol%가 첨가된 Ta$_2$O$_{5}$의 열처리 온도에 따른 전기적, 유전특성을 살펴보려고 한다살펴보려고 한다

• Proceedings of the Korean Ceranic Society Conference
• /
• 2000.04a
• /
• pp.29.1-29.1
• /
• 2000