Synthesis and Characterization of Fe Doped TiO2 Nanoparticles by a Sol-Gel and Hydrothermal Process

  • Kim, Hyun-Ju;Jeong, Kwang-Jin;Bae, Dong-Sik
    • 한국재료학회지
    • /
    • 제22권5호
    • /
    • pp.249-252
    • /
    • 2012

  • Fe doped $TiO_2$ nanoparticles were prepared under high temperature and pressure conditions by mixture of metal nitrate solution and $TiO_2$ sol. Fe doped $TiO_2$ particles were reacted in the temperature range of 170 to $200^{\circ}C$ for 6 h. The microstructure and phase of the synthesized Fe doped $TiO_2$ nanoparticles were studied by SEM (FE-SEM), TEM, and XRD. Thermal properties of the synthesized Fe doped $TiO_2$ nanoparticles were studied by TG-DTA analysis. TEM and X-ray diffraction pattern shows that the synthesized Fe doped $TiO_2$ nanoparticles were crystalline. The average size and distribution of the synthesized Fe doped $TiO_2$ nanoparticles were about 10 nm and narrow, respectively. The average size of the synthesized Fe doped $TiO_2$ nanoparticles increased as the reaction temperature increased. The overall reduction in weight of Fe doped $TiO_2$ nanoparticles was about 16% up to ${\sim}700^{\circ}C$; water of crystallization was dehydrated at $271^{\circ}C$. The transition of Fe doped $TiO_2$ nanoparticle phase from anatase to rutile occurred at almost $561^{\circ}C$. The amount of rutile phase of the synthesized Fe doped $TiO_2$ nanoparticles increased with decreasing Fe concentration. The effects of synthesis parameters, such as the concentration of the starting solution and the reaction temperature, are discussed.

  • https://doi.org/10.3740/MRSK.2012.22.5.249 인용 PDF KSCI

The Comparison of Property and Visible Light Activity between Bulk and Surface Doped N-TiO2 Prepared by Sol-gel and N2-plasma Treatment

  • Hu, Shaozheng;Li, Fayun;Fan, Zhiping
    • Bulletin of the Korean Chemical Society
    • /
    • 제33권1호
    • /
    • pp.199-203
    • /
    • 2012

  • A modified sol-gel method and $N_2$-plasma treatment were used to prepare bulk and surface doped N-$TiO_2$, respectively. XRD, TEM, UV-vis spectroscopy, $N_2$ adsorption, Elemental Analyzer, Photoluminescence, and XP spectra were used to characterize the prepared $TiO_2$ samples. The N doping did not change the phase composition and particle sizes of $TiO_2$ samples, but increased the visible light absorption. The photocatalytic activities were tested in the degradation of an aqueous solution of a reactive dyestuff, methylene blue, under visible light. The photocatalytic activity of surface doped N-$TiO_2$ prepared by $N_2$-plasma was much higher than that of bulk doped N-$TiO_2$ prepared by sol-gel method. The possible mechanism for the photocatalysis was proposed.

  • https://doi.org/10.5012/bkcs.2012.33.1.199 인용 PDF KSCI

Sol-gel법에 의한 $Pb(Zr_xTi_{1-x})O_3$ 강유전 박막의 전기특성 (Electrical properties of $Pb(Zr_xTi_{1-x})O_3$ferroelectric thin films prepared by sol-gel processing)

  • 백동수;박창엽
    • E2M - 전기 전자와 첨단 소재
    • /
    • 제9권2호
    • /
    • pp.132-137
    • /
    • 1996

  • Pb(Zr$_{x}$Ti$_{1-x}$ )O$_{3}$ solutions prepared by sol-gel processing with different Zr/Ti ratio were coated on Pt/SiO$_{2}$/Si substrates using spin coating method. Coated films were annealed by rapid thermal annealing at 650.deg. C for 20sec to fabricate Pb(Zr, Ti)O$_{3}$ ferroelectric thin films. Electrical properties of the films such as dielectric constant and loss, ferroelectric hysteresis, fatigue, switching time, and leakage current were measured. Hysteresis of the films with different Zr/Ti ratio yield Pr ranging 10-21.mu.C/cm$^{2}$, E$_{c}$ ranging 37.5-137.5kV/cm. Hysteresis curve was changed from square-type to slim type according to increasing Zr contents. Switching time was faster than 180ns, and leakage current was about 20.mu.A/cm$^{2}$. The film underwent above 10$^{8}$ cycles of reversed polarization showed fatigue with increased coercive field and decreased remnant polarization.tion.

  • PDF