• 한국세라믹학회지
• /
• 제51권3호
• /
• pp.170-176
• /
• 2014

Effective glass frit compositions enabled to absorb laser energy, and to seal a commercial dye-sensitized solar-cell-panel substrate were developed by using $V_2O_5$-based glasses with various amounts of $TeO_2$ substitution. The latter was intended to increase the lifetime of the solar cells. Substitution of $V_2O_5$ by $TeO_2$ provided a strong network structure for the glasses via the formation of tetrahedral pyramids in the glass, and changed the various glass properties, such as glass transition temperature ($T_g$), dilatometric softening point ($T_d$), crystallization temperature, coefficient of thermal expansion (CTE), and glass flowage without any detrimental effect on the laser absorption property of the glasses. The thermal expansion mismatch (${\Delta}{\alpha}$) between the glass frit and the substrate could be controlled within less than ${\pm}5%$ by addition of 10 wt% of ${\beta}$-eucryptite. An 810 nm diode laser was used for the sealing test. The laser sealing test revealed that the VZBT20 glass frit with 10 wt% ${\beta}$-eucryptite was successfully sealed the substrates without interfacial cracks and pores. The optimum sealing conditions were provided by a beam size of 3 mm, laser power of 40 watt, scan speed of 300 mm/s, and 200 irradiation cycles.

• ETRI Journal
• /
• 제23권4호
• /
• pp.151-157
• /
• 2001

Spectroscopic and thermal analysis indicates that tellurite glasses doped with $B_2O_3$ and $GeO_2$ are promising candidate host materials for wide-band erbium doped fiber amplifier (EDFA) with a high 980 nm pump efficiency. In this study, we measured the thermal stabilities and the emission cross-sections for $Er^{3+}:^{4}I_{13/2}\;{\to}\;^{4}I_{15/2}$ transition in this tellurite glass system. We also determined the Judd-Ofelt parameters and calculated the radiative transition rates and the multiphonon relaxation rates in this glass system. The 15 mol% substitution of $B_2O_3$ for $TeO_2$ in the $Er^{3+}-doped\;75TeO_2-20ZnO-5K_2O$ glass raised the multiphonon relaxation rate for $^4I_{11/2}\;{\to}\;^4I_{13/2}$ transition from 4960 $s^{-1}$ to 24700 $s^{-1}$, but shortened the lifetime of the $^4I_{13/2}$ level by 14 % and reduced the emission cross-section for the $^4I_{13/2}\;{\to}\;^4I_{15/2}$ transition by 11%. The 15 mol% $GeO_2$ substitution in the same glass system also reduced the emission cross-section but increased the lifetime by 7%. However, the multiphonon relaxation rate for $^4I_{11/2}{\to}^4I_{13/2}$ transition was raised merely by 1000 $s^{-1}$. Therefore, a mixed substitution of $B_2O_3$ and $GeO_2$ for $TeO_2$ was concluded to be suitable for the 980 nm pump efficiency and the fluorescence efficiency of $^4I_{13/2}{\to}^4I_{15/2}$ transition in $Er^{3+}-doped$ tellurite glasses.

• 대한화학회지
• /
• 제37권11호
• /
• pp.923-928
• /
• 1993

$K_2NiF_4$형 구조를 갖는 $Sr_{1+x}Ho_{1-x}FeO_{4-y}$ (x = 0.00, 0.25, 0.50, 0.75 및 1.00) 고용체계를 대기압과 1550$^{\circ}$C에서 제조하였다. 이 시료들의 X-선 회절도는 전 x 영역에서 모든 시료와 결정학적 상이 정방정계임을 나타내고 있다. 격자부피는 $Sr^{2+}$ 이온이 치환되는 양이 증가함에 따라 계속적으로 증가한다. 전체 철이온에 대한$ Fe^{4+}$ 이온의 몰비인${\tau}$값은 시료의 Mohr 염 적정으로 결정하였으며 x값과 ${\tau}$값으로부터 산소비화학량인 y값을 계산하였다. ${\tau}$값과 y값은 x값의 증가에 따라서 증가함을 알 수 있었다. x값, ${\tau}$값 y값을 일반식 $Sr_{1+x}Ho_{1-x}Fe^3_{1-}\;^+_{\tau}Fe_{\tau}^{4+}O_{4-y}$에 대입하여 비화학량론적 화학식을 결정하였다. Mossbauer 스펙트라는 $Fe^{3+}$ 이온과 $Fe^{4+}$ 이온의 혼합원자가 상태와 배위상태를 나타낸다. 각 시료들의 자기적 성질은 상온에서 상자성임을 알 수 있다. 전기전도도는 1.0 ~ 1 ${\times}\;10^{-9}{\Omega}^{-1}cm^{-1}$의 범위의 반도체 영역에서 변한다. 전기전도도의 활성화 에너지는${\tau}$값이 증가함에 따라 감소함을 알 수 있다. 전도성 메카니즘은 $Fe^{3+}$ 와 $Fe^{4+}$ 이온간에 전도성 전자의 건너뜀 모델로 설명되어야 한다.

• 한국자기학회지
• /
• 제14권1호
• /
• pp.46-50
• /
• 2004

자성 garnet $Y_3$F $e_{5}$ $O_{12}$의 Y자리에 Ce이 치환된 $Y_{3-x}$C $e_{x}$F $e_{5}$ $O_{12}$(x=0.0, 0.1, 0.2, 0.3) 분말을 졸-겔법으로 합성하였다. $Y_{3-x}$C $e_{x}$F $e_{5}$ $O_{12}$의 결정학적 자기적 성질을 X-선 회절기(XRD), 진동시료 자화율 측정기(VSM)및 Mossbauer분광기를 이용하여 연구하였다. $Y_{3-x}$C $e_{x}$F $e_{5}$ $O_{12}$의 결정구조는 cubic이며, 격자상수는 x = 0.0에서 0.3까지 치환하였을 때 12.3758 $\pm$ 0.0005 $\AA$부터 12.4062 $\pm$ 0.0005 $\AA$으로 선형적으로 증가함을 보였다. VSM 측정 결과 $Y_{3-x}$C $e_{x}$F $e_{5}$ $O_{12}$의 포화 자화(saturation magnetization) 값은 거의 변화가 없었던 반면, 보자력(coercivity) 값은 $Y_3$F $e_{5}$ $O_{12}$과 $Y_{2.9}$C $e_{0.1}$F $e_{5}$ $O_{12}$일때 각각 18.3 Oe에서 5.8 Oe로 감소하였다. 이들 시료의 Mossbauer spectrum을 13K부터 Neel온도까지 측정을 하였다. Fe원자 위치의 분포를 고려하여 16a와 24d에 site의 2set으로 분석하였으며, 또한 $Y_{3-x}$C $e_{x}$F $e_{5}$ $O_{12}$의 자성 이온간의 상호작용을 Neel 이론으로 해석할 수 있었으며 개별 부격자간의 초교환 상호작용의 세기를 결정하였다. Debye 온도를 분석 결과 24d site 의 고체의 굳기가 16a site 경우보다 더 큰 것으로 분석 되었다.te 의 고체의 굳기가 16a site 경우보다 더 큰 것으로 분석 되었다.다. 분석 되었다.다.