• 한국세라믹학회지
• /
• 제35권9호
• /
• pp.945-952
• /
• 1998

Ferroelectric Sr0.8Bi2.4Ta2O9 stock solutions were prepared by MOD(Metaloganic Decompostion) process. The phase transformation for the layered perovskite of the SBT thin films by changing RTA(Rapid her-mal Annealing) temperatuer from 700$^{\circ}C$to 780$^{\circ}C$ were observed using XRD and SEM. Layered perovskite phase began to appear above 740$^{\circ}C$ and then SBT thin films were annealed at 800$^{\circ}C$ for 1hr for its com-plete crystallization. The specimens showed well shaped hysteresis curves without post annealing that car-ried out after deposition of Pt top electrode. The SBT thin films showed the asymmetric ferroelectric pro-perties. It was confirmed that the properties were caused by interface effect to SBT and electrode by leak-age current density measurement and asymmetric properties reduced by post annealing. At post annealing temperature of 800$^{\circ}C$ remanant polarization values (2Pr) were 6.7 9 ${\mu}$C/cm2 and those of leakage current densities were 3.73${\times}$10-7 1.32${\times}$10-6 A/cm2 at 3, 5V respectively. Also bismuth bonding types of SBT thin film surface were observed by XPS.

• 한국전기전자재료학회논문지
• /
• 제17권1호
• /
• pp.7-15
• /
• 2004

The ferroelectric SBT thin films as a material of capacitors for non-volatile FRAMs have some problems that its remanent polarization value is relatively low and the crystallization temperature is quite high abovc 80$0^{\circ}C$. Therefore, in this paper, SBTN solution with S $r_{0.9}$B $i_{2.1}$T $a_{1.8}$N $b_{0.2}$$O_{9}$ composition was synthesized by sol-gel method. Sr(O $C_2$ $H_{5}$)$_2$, Bi(TMHD)$_3$, Ta(O $C_2$ $H_{5}$)$_{5}$and Nb(O $C_2$ $H_{5}$)$_{5}$ were used as precursors, which were dissolved in 2-methoxyethanol. SBTN thin films with 200 nm thickness were deposited on Pt/Ti $O_2$/ $SiO_2$/Si substrates by spin-coating. UV-irradiation in a power of 200 W for 10 min and rapid thermal annealing in a 5-Torr-oxygen ambient at 76$0^{\circ}C$ for 60 sec were used to promote crystallization. The films were well crystallized and fine-grained after annealing at $650^{\circ}C$ in oxygen ambient. The electrical characteristics of 2Pr=11.94 $\mu$C/$\textrm{cm}^2$, Ps＋/Pr＋=0.54 at the applied voltage of 5 V were obtained for a 200-nm-thick SBTN films. This results show that 2Pr values of the UV irradiated and rapid thermal annealed SBTN thin films at the applied voltage of 5 V were about 57% higher than those of no additional processed SBTN thin films. thin films.lms.s.s.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 하계학술대회 논문집 Vol.5 No.2
• /
• pp.697-700
• /
• 2004

The SBT$(Sr_{0.8}Bi_{2.4}Ta_2O_9)$ thin films for semiconductor device were deposited on Pt-coated $Pt/TiO_2/SiO_2Si$ wafer by RF magnetron sputtering method at $400[^{\circ}C]$ and annealed at the temperature range from $600[^{\circ}C]$ to $850[^{\circ}C]$. The top electrodes(Pt) were deposited on SBT thin film by DC sputtering method. The crystallinity of SBT thin films were increased with increase of annealing temperature in the temperature range of $600[{\circ}C]\sim850[^{\circ}C]$. The annealing temperature properties were to be most excellent in the case of annealed SBT thin film at $750^{\circ}C]$. And, the maximum remanent polarization$(2P_r)$ and the coercive electric field$(E_c)$ at annealing temperature of $750[^{\circ}C]$ obtained about $11.60[{\mu}C/cm^2]$ and 48[kV/cm], respectively. Specially, it was seen that fatigue properties does not change in $10^{10}$ switching cycle.