Sialon ceramics are presently seen as promising materials with high hardness, strength, fracture toughness and corrosion resistance for friction and wear applications. The objective of present work is to improve of mechanical properties and wear resistance of $\alpha$-Sialon(x=0.4) by addition of SiC whisker. $\alpha$-sialon(x=0.4)/SiC whisker composites were obtained by hot-isostatic pressing at 173$0^{\circ}C$ for 1 hour under 1757Kg/$\textrm{cm}^2$ N2 pressure after pressureless sintering the mixture of Si3N4, Y2O3, AlN at 1780~180$0^{\circ}C$ for 3~5 hours in N2 atmosphere. As the amount of SiC whisker content increased, relative density and hardness were decreased, however fracture toughness, bending strength and tribological properties were improved. Tribological properties of $\alpha$-Sialon/15 vol% SiC whisker composite were improved in spite of its low mechanical properties.

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2000년도 춘계총회,특별강연,심포지움,연구발표회
• /
• pp.100.1-100.1
• /
• 2000

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 1996년도 재료학회 춘계학술발표회
• /
• pp.55-55
• /
• 1996

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2000년도 추계총회,초청강연,특별강연,연구발표회
• /
• pp.205.2-205
• /
• 2000

• 한국재료학회지
• /
• 제9권6호
• /
• pp.577-582
• /
• 1999

전도성 $Si_3N_4$-TiN 세라믹 복합재료를 제조하기 위해 성형체를 $1450^{\circ}C$에서 20시간 질화처리한 후 $1950^{\circ}C$에서 3.5시간 가스압소결 기술에 의해 후소결하였다. 초기 분말로 약 $10\mu\textrm{m}$로 된 상용 Si분말, 100mesh와 325mesh로된 Ti분말, 그리고 미세한 $\2.5mu\textrm{m}$ TiN분말을 사용하였다. Ti분말울 사용한 $Si_3N_4$-TiN 소결체에서 상대밀도 및 파괴인성값은 다량의 조대한 기공의 존재로 인하여 낮은 값을 보였다. 그러나 TiN분말을 사용한 $Si_3N_4$-TiN 복합체에서 파괴인성, 파괴강도 및 전기저항은 각각 $5.0MPa{\cdot}m^{1/2}$, 624MPa 그리고 $1400{\omega}cm$였다. 복합체에서 TiN 업자의 분산은 $Si_3N_4$ 업자의 조대한 봉상형태로의 성장올 방해하며 $Si_3N_4$/TiN 계면에 강한 변형장울 만든다. $Si_3N_4$-TiN 복합체의 전기전도도 및 기계적 특성을 향상시키기 위해 TiN 업자가 균일하게 분산 된 미세조직 제어가 요망된다.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 1992년도 추계학술발표강연 및 논문개요집
• /
• pp.143-143
• /
• 1992

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2000년도 추계총회,초청강연,특별강연,연구발표회
• /
• pp.165.1-165
• /
• 2000

• 소성∙가공
• /
• 제3권4호
• /
• pp.427-439
• /
• 1994

The high temperature deformation behavior of $SiC_p/Al-Si$ composites and Al-Si matrix was studied by hot torsion test in a range of temperature from $270^{\circ}C$ to $520^{\circ}C$ and at strain rate range of $1.2{\times}10_{-3}~2.16{\times}10_{-1}/sec$. The hot restoration mechanisms for both matrix and composites were found to be dynamic recrystallization(DRX) from the investigation of flow curves and microstructural evolutions. The Si precipitates and SiC particles promoted DRX, and the peak strain$({\varepsilon}_p)$ of the composites was smaller than that of the matrix. Flow stresses of $SiC_p/Al-Si$ composites were found to be generally higher than the matrix, but the difference was quite small at higher temperature due to the decrease of capability of load transfer by SiC particles. With increasing temperature, failure strain of matrix and composites are inclined to increase, the increasing value of failure strain for the $SiC_p/Al-Si$ composites was small compared to that of matrix. The stress dependence of both materials on strain rate() and temperature(T) was examined by hyperbolic sine law, $\.{\varepsilon}=A_1[sinh({\alpha}{\cdot}{\sigma})]_n$exp(-Q/RT)

• 한국재료학회지
• /
• 제3권4호
• /
• pp.381-387
• /
• 1993

${Si_3}{N_4}$와 BN의 선택적 산화반응과 질소분위기 소결에 의하여 $Si_2N_2O$로 결합된$Si_3N_4-BN$복합재료를 개발하였으며, 이때 산화반응 온도와 CaO의 첨가가 $Si_2N_2O$의 생성에 미치는 영향을 고찰하였다. $Si_2N_2O$상이 도입된 $Si_3N_4-BN$복합재료는 내열충격성 및 용강에 대한 내침식성이 우수하여 연속제강새안의 부품인 break ring등의 소재로 사용될 수 있다.

• The Korean Journal of Ceramics
• /
• 제5권4호
• /
• pp.324-330
• /
• 1999

$Si_3N_4$-$TiB_2$ with 2 wt% $Al_2O_3$ and 4 wt% $Y_2O_3$ additives was hot pressed in a flowing $N_2$ environment with varying $TiB_2$ content from 10 to 50 vol%. Variations of mechanical (hardness, fracture toughness, and flexual strength), and tribological properties as a function of $TiB_2$ content were investigated. As the content of $TiB_2$ increased, relative density decreased due to the chemical reaction of $TiB_2$in $N_2$ environment. The reduction of density causes mechanical properties to be degraded with an increase of $TiB_2$ in $Si_3N_4$. Tribological properties were dependent of microstructure as well as mechanical properties, however, they were degraded strongly by the chemical reaction of $Si_3N_4$-$TiB_2$ during hot pressing in $N_2$ environment. SEM and TEM observations, and X-ray diffraction analysis that the chemical reaction products at the interface are TiCN, Si, and $SiO_2$. Also, the comparison of XRD patterns of the $Si_3N_4$-40 vol% $TiB_2$ composites hot pressed at $1,750^{\circ}C$ for 1 hour between in $N_2$ and in Ar gas was made. The XRD peaks of Si and $SiO_2$ were not found in Ar, but still a weak peak of TiCN was presented.