• 대한기계학회논문집
• /
• 제17권10호
• /
• pp.2498-2508
• /
• 1993

$Al/SiC/Al_{2}O_{3}$ hybrid composites are fabricated by squeeze infiltration method. From the misconstructive of $Al/SiC/Al_{2}O_{3}$ hybrid composites fabricated by squeeze infiltration method, uniform distribution of reinforcements and good bondings are found. Hardness value of $Al/SiC/Al_{2}O_{3}$ hybrid composites increases linearly with the volume fraction of reinforcement because SiC whisker and $Al_{2}$O$_{3}$ fiber have an outstanding hardness. Optimal aging conditions are obtained by examining the hardness of $Al/SiC/Al_{2}O_{3}$ hybrid composites with different aging time. Tensile properties such as Young's modulus and ultimate tensile strength are improved up to 30% and 40% by the addition of reinforcements, respectively. Failure mode of $Al/SiC/Al_{2}O_{3}$ hybrid composites is ductile on microstructural level. Through the abrasive wear test and wear surface analysis, wear behaviour and mechanism of 6061 aluminum and $Al/SiC/Al_{2}O_{3}$ hybrid composites are characterized under various testing conditions. The addition of SiC whisker to $Al/SiC/Al_{2}O_{3}$ composites gives rise to improvement of the wear resistance. The wear resistance of $Al/SiC/Al_{2}O_{3}$ hybrid composites is superior to that of Al/SiC composites. The wear mechanism of aluminum alloy is mainly abrasive wear at low speed range and adhesive and melt wear at high speed range. In contrast, that of $Al/SiC/Al_{2}O_{3}$ hybrid composites is abrasive wear at all speed range, but severe wear when counter material is stainless steel. As the testing temperature increases, wear loss of aluminum alloy decreases because the matrix is getting more ductile, but that of $Al/SiC/Al_{2}O_{3}$ hybrid composites is hardly varied. Oil lubricant is more effective to reduce the wear loss of aluminum alloy and $Al/SiC/Al_{2}O_{3}$ hybrid composites at high speed range.

• 한국결정성장학회지
• /
• 제7권4호
• /
• pp.658-664
• /
• 1997

자기질 도자기 소지조성에 필수적으로 함유되는 부산화물들($K_2O, MgO, CaO,Al_2O_3$, 그리고 $TiO_2$)이 순수한 $SiO_2$의 상형태에 미치는 영향을 조사하였다. 또한 장석, 도석, 카올린, 그리고 점토를 이용하여 조합된 자기질 도자기 소지 조성에서 $SiO_2/Al_2O_3$의 비를 조정하여 안정화된 $\beta$-cristobalite 상을 갖는 도자기 소지 조성을 개발하였으며, 여기에 첨가된 부산화물들이 $SiO_2$의 상형태에 미치는 영향을 조사하였다. $SiO_2$에 $K_2$O와 MgO를 첨가할 경우 준안정한 주상은 $\alpha$-cristobalite, CaO와 $Al_2$O$_3$를 첨가할 경우 $\alpha$-quartz, 그리고 $TiO_2$를 첨가할 경우는 비정질상이었다. 장석, 도석, 카올린, 그리고 점토를 사용하여 조합한 도자기 소지에서 $SiO_2/Al_2O_3$비가 작아질 수록 $\beta$-cristobalite 상의 안정화가 촉진되었으며, $\beta$-cristobalite 상이 안정화되는 임계의 $SiO_2/Al_2O_3$의 비는 68.10/22.75이었다. Cristobalite 상이 안정화된 실용 도자기 조성에 부산화물들이 첨가될 경우 $\alpha$, $\beta$-cristobalite 상생성이 억제되었다.

• 한국세라믹학회지
• /
• 제26권1호
• /
• pp.31-36
• /
• 1989

In order to synthesize AlN-polytypes from AlN-SiO2-Al2O3 system, composition A (AlN/SiO2/Al2O3=1/0.3/0.05, mole ratio) and composition B(AlN-SiO2-Al2O3=1/0.2/0.05, mole ratio) were used. AlN-polytypes were produced by nitriding the mixture at 175$0^{\circ}C$~190$0^{\circ}C$ under N2 atmosphere. For lower reaction temperature, 15R phase was produced and in the case of higher reaction temperature, AlN phase was only produced. As each composition was heated at 185$0^{\circ}C$ in N2 atmosphere, produced main phases were 15R phase for composition A and 21R phase for composition B respectively. The fracture surfaces of produced reactants showed porous skeleton structure.

• 한국세라믹학회지
• /
• 제28권8호
• /
• pp.625-625
• /
• 1991

2wt% Al2O3와 10wt% Al2O3를 첨가하여 2000℃와 2050℃에서 가압소결된 SiC를 37 mol% NaCl과 63 mol% Na2SO4 Salt에 의해 60분까지 hot corrosion을 시켰다. 부식은 SiC표면에 형성된 SiO2층이 Na2O 이온에 의한 basic dissolution에 이해 일어남이 관찰되었고 10wt%의 Al2O3가 함유된 시편은 입계에 Al2O3를 함유한 입계상의 존재로 2wt% Al2O3가 함유된 시편보다 낮은 corrosion rate를 나타냈다. SiC와 산화물층 사이에서 gas bubble의 형성이 관찰되었고 이 gas bubble이 산화물층을 심하게 파괴하기 전까지 corrosion rate은 linear하게 변했다. 부식 양상은 개기공과 입계에서 pitting corrosion에 의해 시작되었다.

• 한국세라믹학회지
• /
• 제34권5호
• /
• pp.483-490
• /
• 1997

Al2O3/metal composites were fabricated by oxidation and reaction of molten Al-alloy into two types of commercial Al2O3-SiO2 fibrous insulation board. The growth rate, composition and microstructure of these materials were described. An AlZnMg(7075) alloy was selected as a parent alloy. Mixed polycrystalline fiber and glass phase fiber were used as a filler. The growth surface of an alloy was covered with and without SiO2. SiO2 powder was employed as a surface dopant to aid initial oxidation of Al-alloy. Al-alloy, SiO2, fiber block and growth inhibitor CaSiO3 were packed sequentially in a alumina crucible and oxidized in air at temperature range 90$0^{\circ}C$ to 120$0^{\circ}C$. The growth rate of composite layer was calculated by measuring the mass increasement(g) per unit surface($\textrm{cm}^2$). XRD and optical microscope were used to investigate the composition and phase of composites. The composite grown at 120$0^{\circ}C$ and with SiO2 dopant showed rapid growth rate. The growth behavior differed a little depending on the types of fiber used. The composites consist of $\alpha$-Al2O3, Al, Si and pore. The composite grown at 100$0^{\circ}C$ exhibited better microstructure compared to that grown at 120$0^{\circ}C$.

• 한국세라믹학회지
• /
• 제32권1호
• /
• pp.63-70
• /
• 1995

A crack-free ceramic composite membrane with micropores has been synthesized by the pressurized sol-gel coating technique using the mixed Al2O3-SiO2 sols. The mixed sols were prepared by mixing nanoparticulate SiO2 and boehmite sols. These sols were more stable at lower pH, but very unstable when their copositions were in the range of 50~75mol% of SiO2 at the same pH. The mixed Al2O3-SiO2 membrane prepared from the mixed sol (0.2mol/$\ell$ of solid content and pH=2) containing 40mol% of SiO2 had the mean pore radius of 0.80nm and the specific surface area of 280$m^2$/g. The nitrogen permeability through the coated Al2O3-SiO2 layer was 42$\times$107mol/$m^2$.s.Pa. It was found that the thermal stability of aluminosilicate membranes, even through similar to that of SiO2 membranes, was much improved in comparison with ${\gamma}$-alumina membranes.

• 한국세라믹학회지
• /
• 제52권1호
• /
• pp.19-22
• /
• 2015

The joining behavior of YSZ ceramics to the glasses used in the $9Al_2O_3-24ZrO_2-51SiO_2-16R_2O$ and $9Al_2O_3-24ZrO_2-51SiO_2-7La_2O_3-9R_2O$ (wt%) glass systems was investigated. The glass transition and softening temperatures were determined to be $430^{\circ}C$ and $760^{\circ}C$, respectively. The behavior of the contact angle was inversely proportional to an increase in the temperature. The Zr element in YSZ acted as a nucleation agent and contributed to the bonding behavior at the interface.

• 한국결정성장학회지
• /
• 제7권4호
• /
• pp.626-631
• /
• 1997

하동고령토($Al_2O_3-SiC-C$)를 출발원료로하여 AlSiCa내화재 원료를 합성하였다. 하동고령토와 탄소분말을 혼합하여 수소분위기하에서 반응시킨결과, $1300^{\circ}C$에서$Al_2O_3-SiC-C$ 복합체가 힙성되기 시작하여$1400^{\circ}C$에서 완전 합성되었고, $SiO_2$에 대한 최적carbon량은 mole비로 1:4이었다. 합성시 알루미나 용기에 탄소분말을 충전시키지 않을 때는 미합성부분이 없이 밝은 녹색을 띈 $\beta$-SiC(cubic form) 를 형성함을 확인하였다.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2012년도 춘계학술발표회 논문집
• /
• pp.170-171
• /
• 2012

$Fe_2O_3$, Al, Cr과 Si 분말을 고 에너지 볼 밀링해서 나노분말을 제조한 후 고주파유도 가열 활성 연소합성 장치로 1분 이내의 짧은 시간에 합성 및 소결한 $Al_2O_3+4.65(Fe_{0.43}Cr_{0.17}Al_{0.323}Si_{0.077})$, $Al_2O_3$ + 5.33 ($Fe_{0.375}Cr_{0.11}Al_{0.3}Si_{0.075}$), $Al_2O_3$ + 6.15 ($Fe_{0.325}Cr_{0.155}Al_{0.448}Si_{0.072}$), $Al_2O_3$ + 3.3 ($Fe_{0.6}Cr_{0.3}Al_{0.6}$) 소결체 시편을 $700^{\circ}C$의 온도에서 100시간 동안 공기 중에서 산화 및 $N_2-H_20-H_2S$ 혼합 가스 내에서 황화 부식을 실시하였다. 그 결과 산화 및 황화 부식 후에 ${\alpha}-Al_2O_3$가 표면에 생성되어 보호 피막으로 작용하여 우수한 내식성을 보였다.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2013년도 춘계학술대회 논문집
• /
• pp.53-54
• /
• 2013

Nano-multilayered CrAlSiN films consisting of crystalline CrN nanolayers and amorphous AlSiN nanolayers were deposited by cathodic arc plasma deposition. Their oxidation characteristics were studied between 600 and $1000^{\circ}C$ for up to 70 h in air. During their oxidation, the amorphous AlSiN nanolayers crystallized. The formed oxides consisted primarily of $Cr_2O_3$, ${\alpha}-Al_2O_3$, $SiO_2$. The outer $Al_2O_3$ layer formed by outward diffusion of Al ions. Simultaneously, an inner ($Al_2O_3$, $Cr_2O_3$)-mixed layer formed by the inward diffusion of oxygen ions. $SiO_2$ was present mainly in the lower part of the oxide layer due to its immobility. The CrAlSiN films displayed good oxidation resistance, owing to the formation of oxide crystallites of $Cr_2O_3$, ${\alpha}-Al_2O_3$, and amorphous $SiO_2$.