• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.54 no.12
• /
• pp.573-577
• /
• 2005

[$TiO_2$] sol and $SiO_2$ sol were prepared using sol-gel method. As $H_{2}O$/Alkoxide ratios increased, sol had cluster structure and as $H_{2}O$/Alkoxide ratios decreased, sol had linear structure. Gelation time of $TiO_2$ sol was faster than that of $SiO_2$ sol according to the time. In comparison with initial viscosity between $TiO_2$ sol and $SiO_2$ sol, $TiO_2$ sol was highest at $H_{2}O/Ti(OC_{3}H_{7})_{4}=5$, $SiO_2$ sol was almost constant according to $H_{2}O/Si(OC_{2}H_{5})_{4}$ ratios.

• Journal of the Korean Ceramic Society
• /
• v.41 no.6
• /
• pp.471-475
• /
• 2004

TiO$_2$, SiO$_2$, and PBA(Pseudo Boehemite Alumina) sol were prepared by sol-gel process. The particle sizes of these sol exhibited uniform 10∼30 nm. As the amount of SiO$_2$ sol increased, the temperature of phase transition (from anatase phase to rutile phase) was raised temperature than $600^{\circ}C$, which attributed to the enhanced photocatalyst properties. Also, the anatase phase was obtained with very small amount of the rutile phase from the addition of SiO$_2$ (10∼30 wt%) at annealing temperature of 120$0^{\circ}C$. The specimen with 20 wt% SiO$_2$ sol exhibited the maximum photocatalyst properties. But, the specimen with PBA sol did not affect photocatalytic activity due to the presence of rutile phase.

• Journal of the Korean Ceramic Society
• /
• v.32 no.1
• /
• pp.63-70
• /
• 1995

A crack-free ceramic composite membrane with micropores has been synthesized by the pressurized sol-gel coating technique using the mixed Al2O3-SiO2 sols. The mixed sols were prepared by mixing nanoparticulate SiO2 and boehmite sols. These sols were more stable at lower pH, but very unstable when their copositions were in the range of 50~75mol% of SiO2 at the same pH. The mixed Al2O3-SiO2 membrane prepared from the mixed sol (0.2mol/$\ell$ of solid content and pH=2) containing 40mol% of SiO2 had the mean pore radius of 0.80nm and the specific surface area of 280$m^2$/g. The nitrogen permeability through the coated Al2O3-SiO2 layer was 42$\times$107mol/$m^2$.s.Pa. It was found that the thermal stability of aluminosilicate membranes, even through similar to that of SiO2 membranes, was much improved in comparison with ${\gamma}$-alumina membranes.

• Journal of the Korean Ceramic Society
• /
• v.32 no.4
• /
• pp.507-515
• /
• 1995

The monolithic dry gels of the Li2O-Al2O3-TiO2-SiO2 system were prepared by the sol-gel technique using metal alkoxides as starting materials to obtain monolithic glass-ceramics at low temperature without melting. Activation energy for the crystal growth of the gel with 6.05% TiO2, nucleating ageng, for the preparation of Li2O-Al2O3-TiO2-SiO2 system glass-ceramic was 101.14kcal/mol. As a result of the analysis of DTA & XRD, it was confirmed that the crytallization of Li2O-Al2O3-TiO2-SiO2 system glass-ceramic was the most efficient when 6.05% TiO2, nucleating agent, was added. $\beta$-eucryptite solid solution crystals and $\beta$-spodumene solid solution crystals were detected in the sample heat treated above 85$0^{\circ}C$. The sintered gel heat treated at 85$0^{\circ}C$ had the specific surface area of 185$m^2$/g, the pore volume of 0.19cc/g and the average pore radius of 20.8$\AA$. This shows that the sintered gel is also comparatively porous material. In temperature range of 25~85$0^{\circ}C$ thermal expansion coefficient of the specimen which was crystallized for 10hrs at 85$0^{\circ}C$ was 6.7$\times$10-7/$^{\circ}C$, which indicated that the crystallized specimen was turned out to be the glass-ceramic with low thermal expansion.

• Journal of the Korean Ceramic Society
• /
• v.32 no.7
• /
• pp.853-857
• /
• 1995

ZrSiO4 powders were prepared from partially hydrolyzed solution of Si(OC2H5)4 and ZrOCl2.8H2O solution by the sol-gel method and formation rate of ZrSiO4 on the reaction parameter was investigated. In order to prepare homogeneous ZrSiO4 precursor gels, the H2O/Si(OC2H5)4 molar ratio of about 2, the pH of the ZrOCl2.8H2O solution fo about 4 and stirring time of the mixed solutions of about 2 hrs were appropriate. Formation of temperature of ZrSiO4 reduced about 15$0^{\circ}C$ by milling and formation of ZrSiO4 at 1300~135$0^{\circ}C$ showed an accelerative increase through the hedvall effect by silica.

• Journal of Environmental Science International
• /
• v.11 no.6
• /
• pp.597-603
• /
• 2002

Photocatalytic degradation of phenol was carried out with UV-illuminated TiO$_2$-SiO$_2$ in aqueous suspension. TiO$_2$-SiO$_2$ catalysts were prepared by sol-gel method from the titanium isopropoxide and tetraethylorthosilicate at different Ti/Si ratio and some commercial TiO$_2$ catalysts were used as purchased. All catalysts were characterized by X-ray Diffraction(XRD) and BET surface area analyzer. The effect of reaction conditions, such as initial concentration of phenol, reaction temperature and catalyst weight on the photocatalytic activity was studied. In addition, TiO$_2$-SiO$_2$(49: 1) prepared by sol-gel method showed higher activity than commercial TiO$_2$catalysts on the photocatalytic degradation of phenol. The addition of SiO$_2$ into TiO$_2$hepled to increase the thermal stability of titania which suppressed the formation of anatase into rutile. The photocatalytic degradation of phenol showed pseudo-1st order reaction and the degradation rate increases with decreasing initial phenol concentration.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.8 no.2
• /
• pp.307-314
• /
• 1998

PZT thin films were fabricated by the Sol-gel method. Starting materials used for the preparation of the stock solution were Pb-acetate trihydrate, Zr-normal propoxide and Ti-isopropoxide. 2-Methoxyethanol and iso-propanol were used for solution. For studying the diffusion of Pb ion into the substrates. We used bare Si substrate, $SiO_2/Si$ substrates which was produced by thermal oxidation and $TiO_2/SiO_2/Si$ which was mad by Sol-gel method. Densification and adhesion of thin films were observed by SEM. Phase formation of thin films and diffusion of Pb ion into the substrate were examined by XRD and ESCA, respectively. In the case of bare Si and $SiO_2/Si$ substrate, we obtained the perovskite phase at $700^{\circ}C$ and restricted a little the diffusion of Si ion into the film with $SiO_2$ buffer layer. In the case of $TiO_2/SiO_2/Si$, perovskite phase were obtained at $500^{\circ}C$ and the diffusion of Pb ion and Si ion were restriced.

• Journal of Ceramic Processing Research
• /
• v.13 no.spc2
• /
• pp.373-376
• /
• 2012

Thin films of Ag-SiO2-TiO2 composite oxides with SiO2/TiO2 of 20/80 molar compositions were prepared by the sol-gel method, using tetraethylorthosilicate (TEOS) and titanium isopropoxide (TIP) as precursors. Ag-SiO2-TiO2 films coated on commercial glass substrates have successfully been synthesized using sol-gel method. The Ag-SiO2-TiO2 film with 0.5% Ag-added concentration and 20 mol% SiO2-mixture gives optimal results on crystalline structure, optical property, surface area, and photochromic property. Absorption near the wavelength of the incident light decreased gradually. The reversibility of the two-photon writing process in Ag-SiO2-TiO2 film is clearly seen.

• Journal of the Korean Ceramic Society
• /
• v.44 no.3 s.298
• /
• pp.137-141
• /
• 2007

$La_{2}O_{3}-TiO_{2}-SiO_{2}$ glass, a type that could not obtained so far by the conventional melting method, was prepared successfully using a sol gel process. Glass derived with the sol-gel process has compositions of $5La_{2}O_{3}-5TiO_{2}-90SiO_{2},\;5La_{2}O_{3}-10TiO_{2}-85SiO_{2}$, and $5La_{2}O_{3}-20TiO_{2}75SiO_{2}$. The UV-visible absorption edge of all glass compositions was below 400 nm. The measured density is in the range of 2.55-2.89, and was nearly identical to the calculated density and the refractive index of the glasses derived from the sol-gel ranges from 1.545 to 1.645. The molar additive coefficient of $TiO_{2}$ measured in this ternary system is lower than the calculated value, while the value of $La_{2}O_{3}$ is higher.

• Journal of the Korean Ceramic Society
• /
• v.38 no.9
• /
• pp.794-798
• /
• 2001

$Y_{2-x}SiO_5:Ce_x^{3+}$(x=0.002∼0.04) phosphors were prepared by sol-gel process, amorphous crystal phase was observed in calcining dry gel at 800$^{\circ}$C, but pure $X_2$ type of type $Y_2SiO_5$ phase appeared from heat treatment above 1000$^{\circ}$C. Light absorption of tye $Y_2SiO_5$ host lattice occurred at 230∼360nm, and light absorption of the $Y_{2-x}SiO_5:Ce_x^{3+}$ phosphors was observed at 300∼400nm in adding $Ce^{3+}$. $Y_{2-x}SiO_5:Ce_x^{3+}$ phosphors showed maximum emission shoulder at 436nm. Maximum CL intensities of $Y_{2-x}SiO_5:Ce_x^{3+}$ were observed in adding 0.025 $Ce^{3+}$ and the phosphor showed x=0.161, y=0.124 in color coordinate of CIE1931.