• Corrosion Science and Technology
• /
• 제20권4호
• /
• pp.196-203
• /
• 2021

To improve corrosion resistance and reduce the hydrogen uptake of 22MnB5, up to 5% Mg was added to the AlSi coating of 22MnB5. After hot-stamping and electrocoating were done on the metallic-coated specimen, the surface characteristics of the steel, hydrogen uptake content, and corrosion resistance were examined by transmittance electron microscopy, thermal desorption spectrometry, cyclic corrosion testing, and electrochemical impedance spectroscopy. Mg was investigated as MgO on the surface layer after hot-stamping while it existed as Mg₂Si before hot-stamping. The total hydrogen content of 22MnB5 was decreased along with the Mg content. However, there was no difference at 0.2 wt% or more. When a small amount of Mg was added, the coating corrosion resistance was decreased, but when it was added at around 1.0 wt%, the greatest corrosion resistance increase was seen. However, when 3 wt% or more was added excessively, the corrosion resistance was decreased. MgO on the surface was considered to suppress H uptake by the AlSi melting solution and increase the barrier effect of the coating.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 1997년도 제26회 추계학술대회
• /
• pp.183-190
• /
• 1997

The wear behaviors of $Al_2O_3-40%TiO_2$ deposited on casting aluminum alloy(ASTM A356) by plasma spray against SiC ball have been investigated experimentally. Friction and wear tests are carried out at room temperature. The friction coefficient of $Al_2O_3-40%TiO_2$ coating is lower than that of pure $Al_2O_3$ coating(APS). It is found that low friction correspond to low wear and high friction to high wear in the experimental result. The thickness of $Al_2O_3-40%TiO_2$ coatings indicated the existence of the optimal coating thickness. It is found that a voids and porosities of coating surface result in the crack generated. As the tensile stresses in coating increased with the increased friction coefficient. The columnar grain of coating will be fractured to achieve the critical stress. It is found that the cohesive of splats and the porosity of surface play a role in wear characteristics. It is suggested that the mismatch of thermal expansion of substrate and coating play an important role in wear performance. Tensile and compressire under thermo-mechanical stress may be occurred by the mismatch between thermal expansion of substrate and coating. This crack propagation above interface is observed in SEM.

• Bulletin of the Korean Chemical Society
• /
• 제10권6호
• /
• pp.535-543
• /
• 1989

We have investigated the infrared absorption spectra for carbon monoxide chemisorbed on reduced and oxidized Rh/$SiO_2$ with and without potassium coating within the frequency range of 1800-2200 $cm^{-1}$ at various Rh concentrations, CO pressures, and temperatures. In case of no potassium coating, only two bands at 2070 and 1900 $cm^{-1}$ appeared for CO adsorbed on reduced Rh/$SiO_2$ while for oxidized Rh/$SiO_2$ four bands were found at 2100, 2070, 2040, and 1900 $cm^{-1}$. We have successfully tried to explain the differences between our observations and those by other investigators who used the Rh/$Al_2O_3$ system instead of Rh/$SiO_2$ on the basis of the suggestions by Yates et al. Accordingly, we propose that the surface OH groups are deeply involved in producing the $Rh^{+1}$ sites which are responsible for the gem-dicarbonyl species. On coating with potassium all the IR bands for three carbonyl species were found to suffer red shift, the magnitude of which increased with increasing Rh/CO ratio.

• 대한기계학회논문집A
• /
• 제33권9호
• /
• pp.957-962
• /
• 2009

Sialon was produced by hot-pressing the mixtures of $Si_3N_4$, AlN and $Y_2O_3$ powders. All fracture tests were performed on a three-point loading system with a 30 mm bending span. Fracture toughness and Vickers hardness of smooth specimen were average 7.05 $MPa{\cdot}m^{0.5}$ and Hv = 1580, respectively. Density of three kinds of specimens, smooth specimen, smooth and healed specimen, smooth with $SiO_2$ colloidal coating and healed specimen, had beyond 99 % of theoretical density. Bending strength of smooth healed specimens had high strength more than 1 GPa. Crack healed specimens recovered as strength as smooth specimen. That is, cracked specimen with $SiO_2$ colloidal coating on cracked part recovered strength by heat treatment, completely. Crack healing of $Si_3N_4$ composite ceramics had contributed glassy $SiO_2$ to strength recovery. Limiting high temperature for bending strength of heat treated smooth specimen for bending strength was about 1273 K.

• 한국세라믹학회지
• /
• 제34권3호
• /
• pp.314-322
• /
• 1997

극저 유전특성을 갖는 SiO2 에어로겔의 박막화의 층간 절연막으로써의 응용성이 연구되었다. 점도가 10~14cP인 SiO2 폴리머 졸을 이소프로판을 분위기 하에서 1000~7000m으로 p-Si(111) 웨이퍼 상에 스핀코팅한 습윤겔 박막을 25$0^{\circ}C$와 1160 psing 조건에서 초임계건조하여 0.5 g/㎤ 정도의 밀도(78% 기공율) 와 4000~21000$\AA$ 범위의 두께를 갖는 SiO2 에어로겔 박막을 제조하였다. 박막의 두께와 미세구조를 제어할 수 있는 주요 인자는 졸의 농도, 회전속도 및 습윤겔 숙성시간임을 알 수 있었다. SiO2 에어로겔 박막의 유전상수 값은 giga급 이상의 차세대 반도체 소자에 충분히 응용될 수 있을 정도로 낮은 2.0 정도이었다.

• 한국세라믹학회지
• /
• 제33권12호
• /
• pp.1353-1364
• /
• 1996

Recently semiconductor doped glasses have attracted attention as nonlinear optical materials because of their large third order nonlinear optical properties. The transparent and homogeneous CdS-doped SiO2 glass thin films were obtained by the dip=coating process of the sol-gel method. Thin films were consisted of glasses containing CdS microcrystallites which were formed by dissolved Cd2+ and S2- ions in a SiO2 matrix solutions. A subsequent thermal treatment of this samples led the formation of colloidal agglomerates and finally of microcrystallites. The size of CdS microcrystallites was about 4 to 15 nm after thermal treatments at various heating conditions. From the optical absorption spectra of the CdS-doped SiO2 glass films it was found that the absorption edge was blue-shifted compared with that of the bulk CdS crystal(~2, 4 eV) and that the amount of energy shift was inversely proportional to the crystal size. And the band gap energy increased with the decrease in crystallite size indicating that the quantum size effects occured.

• 한국재료학회지
• /
• 제24권2호
• /
• pp.93-97
• /
• 2014

In this study, a cobalt sulfate ceramic coating was sintered on various clays at $1250^{\circ}C$. The specimen characteristics were investigated by X-ray diffraction(XRD), scanning electron microscopy(SEM), TG-DTA, UV-vis spectrophotometer, and HRDPM. The ceramic coating had a constant thickness of thousands ${\mu}m$, and the surface was confirmed to be densely fused. Other new compounds were produced by the cobalt sulfate sintering process and reactions. These compounds were a $CoAl_2O_4$ phase, $Co_2SiO_4$ phase, anorthite($CaAl_2Si_2O_8$) phase, and $FeAl_2O_4$ phase, respectively. UV properties of the coated specimen were investigated, celadon clay specimen in 530-550 nm band is showing a dark gray color. The white clay and white mix clay specimen in 460-500 nm band is showing a blue color. The cobalt-aluminate($CoAl_2O_4$) spinel and the cobalt-silicate olivine($Co_2SiO_4$) were the strongest of the ceramic pigments, producing a very pure, navy blue color.

• Corrosion Science and Technology
• /
• 제19권2호
• /
• pp.100-107
• /
• 2020

The demand for powder-coated steel used in the marine industry is increasing owing to their superior corrosion resistance. However, the powder coatings used in commercial products can deteriorate easily by the penetration of brine. In an attempt to suppress brine penetration into the powder coating and significantly increase the corrosion resistance, three types of oxide particles were added to the coating. Electrochemical impedance spectroscopy tests in 3.5% NaCl solution were performed to evaluate the corrosion behaviors of the powder coating with oxide particles. The results showed that the addition of SiO₂ particles to a powder coating severely decreased the corrosion resistance due to the easy detachment of agglomerated SiO₂ particles with a coarse size from the coating layer. In contrast, the TiO₂ and SnO₂-added coatings showed better corrosion resistance, and the TiO₂-added coating performed best in the test conducted at room temperature. However, conflicting results were obtained from tests conducted at a higher temperature, which may be attributed to the effective suppression of brine penetration by the fine SnO₂ particles uniformly distributed in the coating.

• 한국재료학회지
• /
• 제22권10호
• /
• pp.526-530
• /
• 2012

Silica-based ceramic-matrix composites have shown promise as advanced materials for many applications such as chemical catalysts, ceramics, pharmaceuticals, and electronics. $SiO_2$-CuO-$CeO_2$ multi-component powders and their thin film, using an oxalic acid template as a chelating agent, have larger surface areas and more uniform pore size distribution than those of inorganic acid catalysts. $SiO_2$-CuO-$CeO_2$ composite powders were synthesized using tetraethylorthosilicate, copper (II) nitrate hemi (pentahydrate), and cerium (III) nitrate hexahydrate with oxalic acid as template or pore-forming agent. The process of thermal evolution, the phase composition, and the surface morphology of these powders were monitored by thermogravimetry-differential thermal analysis (TG-DTA), X-ray diffractometry (XRD), field-emission scanning electron microscopy (FE-SEM), and energy dispersive X-ray spectrometry (EDXS). The mesoporous property of the powders was observed by Brunner-Emmett-Teller surface (BET) analysis. The improved surface area of this powder template with oxalic acid was $371.4m^2/g$. This multi-component thin film on stainless-steel was prepared by sol-gel dip coating with no cracks.

• 한국전기전자재료학회논문지
• /
• 제26권1호
• /
• pp.6-12
• /
• 2013

Aerosol deposition(AD) coating that enable fabricate films at low temperature have begun to be widely researched for the integration of ceramics as well to realize high-speed deposition rates. For application of ceramic thick film by AD to display and electronic ceramic industry, fabrication of dense structure with a no cracking is required. In this study, to fabricate dense ceramic thick film, the effect of crystal phase of starting powder was investigated. For this study, amorphous and crystalline $SiO_2$ powders were used as starting powders. Two types of $SiO_2$ powders were deposited on glass substrate by AD. In the case of amorphous $SiO_2$ powder, the deposited films had extremely incompact and opaque layer, irrespective of particle size. In contrast to amorphous powder, in the case of crystalline powder, porous structure layer and dense microstructure with no cracking layer were fabricated depending on the particle size. The optimized starting powder size for dense coating layer was $1{\sim}2{\mu}m$. The transmittance of film reached a maximum of 76% at 800 nm.