• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.18 no.1
• /
• pp.50-56
• /
• 2005

The electrical properties, clamping voltage characteristics, and stability of dysprosia-doped ZnO-P $r_{6}$ $O_{11}$-based varistors were investigated with different dysprosia contents from 0 to 2.0 mol%. The incorporation of dysprosia in varistor ceramics greatly increased the varistor voltage from 50 to 481.0 V/mm. It was found that the dysprosia is good additive improving a nonlinearity, in which the nonlinear exponent is above or near 50, and the leakage current is below 1.0 $\mu$A. The dysprosia-doped varistors exhibited superior clamping voltage characetristics, in which clamping voltage ratio is above or neat 2 at surge current of 50 A. The 0.5 mol% dysprosia-doped varistors only exhibited high stability, with the rate of varistor voltage of -0.9%, under DC acceleraetd aging stress, 0.95 $V_{lmA}$/15$0^{\circ}C$/24 h.h.h.h.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.10
• /
• pp.897-901
• /
• 2003

The microstructure and varistor characteristics of ZnO-Pr$_{6}$O$_{11}$-CoO-Cr$_2$O$_3$-Dy$_2$O$_3$(ZPCCD)-based ceramics were investigated with Dy$_2$O$_3$ content in the range of 0.0∼2.0 mol%. As Dy$_2$O$_3$ content is increased, the average grain size was decreased in the range of 18.6∼4.7 $\mu$m and the density was decreased in the range of 5.53∼4.34 g/cm$^3$. While, the varistor voltage was increased in the range of 39.4∼436.6 V/mm and the nonlinear exponent was in the range of 4.5-66.6 with increasing Dy$_2$O$_3$ content. The addition of Dy$_2$O$_3$ highly enhanced the nonlinear properties of varistors, compared with the ceramics without Dy$_2$O$_3$ Particularly, the ceramics with Dy$_2$O$_3$ content of 0.5 mol% exhibited the highest nonlinearity, in which the nonlinear exponent is 66.6 and the leakage current is 1.2 $\mu$A.A.A.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.3
• /
• pp.244-252
• /
• 2002

The electrical and dielectric behavior fort DC accelerated aging stress of P $r_{6}$ $O_{11}$-based Zno varistors cnsisting of ZnO-P $r_{6}$ $O_{11}$-CoO-C $r_2$ $O_3$-E $r_2$ $O_3$ were investigated with sintering temperature in the range of 1325~1345$^{\circ}C$. The varistor ceramics with increasing sintering temperature were more densified. A more densified varistors leaded to high stability for DC accelerated aging stress. Furthermore, the stability for DC accelerated aging stress was increased with the leakage current and dtan $\delta$/dV decreasing in order of 1325longrightarrow1335longrightarrow1345longrightarrow134$0^{\circ}C$ in sintering temperature. It was found that the stability for DC stress is affected more greatly by the leakage current and dtan $\delta$/dV than the densification. It is considered that the stability of varistors for DC stress can be estimated by considering the factors, such as the densification, leakage current, and dtan $\delta$/dV. As a result, the varistor sintered at 134$0^{\circ}C$ exhibited the highest stability, with %$\Delta$ $V_{lmA}$=-1.54%, %$\Delta$$\alpha$=-2.49%, %$\Delta$ $I_{\ell}$=+240.68%, 5%$\Delta$tan$\delta$=+29.96%.96%.96%.%.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.8
• /
• pp.664-670
• /
• 2002

The electrical characteristics of $ZnO-Pr_6O_{11}-CoO-Cr_2O_3-Y_2O_3$(ZPCCY)-based varistors were investigated with $Y_2O_3$ content in the range of 0.0~4.0 mol%. As $Y_2O_3$ content is increased, the average grain size was markedly decreased in the range of 18.6~3.2 $\mu m$ and the density of the ceramic was decreased in the range of 5.53 ~3.74 $g/\textrm{cm}^3$. While, the varistor voltage was increased in the range of 39.4~748.1 V/mm and the nonlinear exponent was in the range of 4.5~51.2 with increasing $Y_2O_3$ content. The addition of $Y_2O_3$ greatly enhanced the nonlinear properties of varistors, compared with the varistor without $Y_2O_3$. In particular, the varistors with $Y_2O_3$content of 0.5 mol% exhibited the highest nonlinearity, in which the nonlinear exponent is 51.2 and the leakage current is 1.3 $\mu A$. The donor concentration and the density of interface states were decreased in the range of (4.19~0.14) $\times$10$^{18}$ /㎤ and (5.38~1.15)${\times}10^{18}/\textrm{cm}^3$, respectively, with increasing $Y_2O_3$ content.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.410-414
• /
• 2001

The microstructure, V-I characteristics, and stability of ZnO-Pr$_{6}$O$_{11}$-CoO-Cr$_2$O$_3$-Y$_2$O$_3$based vairstors were investigated with cooling rate in the range of 2~8$^{\circ}C$/min. The cooling rate relatively weakly affected the microstructure, and the varistor voltage and the leakage current in the V-I chracteristics. But the nonlinear exponent relatively strongly affected by cooling rate. And the cooling rate also greatly affected the stability for DC stress. In gross, the varistors cooled with 4$^{\circ}C$/min exhibited the highest performance in the densification, nonlinearity, and stability. Especially, they exhibited a high stability, in which the variation rate of the varistor voltage and the nonlinear exponent is -1.44% and -4.85%, respectively, under more severe DC stress such as (0.80 V$_{1mA}$9$0^{\circ}C$/12 h)+(0.85 V$_{1mA}$115$^{\circ}C$/12 h)\`(0.90 V$_{1mA}$12$0^{\circ}C$/12 h)+(0.95 V$_{1mA}$1$25^{\circ}C$/12 h)+(0.95 V$_{1mA}$15$0^{\circ}C$/12 h). It should be emphasized that the stability of these varistors is much superior to that of others.s.of others.s.