• 한국세라믹학회지
• /
• 제32권12호
• /
• pp.1331-1336
• /
• 1995

The glass-ceramics for ferro-electric were made from compositions of 70PbO.16TiO2.8SiO2.4B2O3.2AlPO4 (wt%) and 67.5PbO.20TiO2.8.5SiO2.2B2O3.2AlPO4 (wt%). The crystallization kinetics for PbTiO3 crystalline phase formation from glass was studied using non-isothermal DSC techniques. The values of activation energy, ΔE using variables of heating rate and temperature were calculated at various reaction fractions obtained from peak area over DSC. The results indicated that activation energy was lowest at 60% reaction fractions and the activation energy of glass containing 20.0 wt% TiO2 is higher than that of glass containing 16.0 wt% TiO2. The crystallization mechanism was three dimensional growth (n=4).

• 한국세라믹학회지
• /
• 제21권4호
• /
• pp.349-354
• /
• 1984

The purpose of present study is to find the structure crystallization mechanism and physical properties in $TiO_2$ containing lead zinc borosilicate glass system. The experiments such as differential thermal analysis infrared spectral analysis. X-ray diffraction analysis and thermal expansion measurements have been done. Differential thermal analysis of coarse and fine glass powder showed bulk nucleating mechanism for high $TiO_2$ containing glasses and surface nucleation mechanism for low $TiO_2$ containing glasses. The prepared glasses crystallized to crystalline mixture of PbO.2ZnO. $B_2O_3$ .4PbO.2ZnO.$5B_2O_3$and 2PbO.ZnO.$B_2O_3$ when heat-treated in the range of 480 and 51$0^{\circ}C$ and crystallized to PbTiO3 when heat-treated at $600^{\circ}C$. Obtained crystalline phase of $PbTiO_3$ in glass matrix strongly affects to thermal expansion coefficient and the value of crystallized glass varied 68.0 to $107.1{\times}10-7$/$^{\circ}C$ depending on the amount of $TiO_2$added. Infrared spectral analysis showed that [$BO_3$] triangle and [$BO_3$] tetrahedral units were coexisted in the glass with high content of PbO.

• 한국세라믹학회지
• /
• 제37권1호
• /
• pp.63-69
• /
• 2000

Electrically-induced strain(S) and polarization(P) for Pb(Sc1/2Nb1/2)O3-PbTiO3(1-x)PSN-xPT) crystalline solutions were studied. From the compositional dependence of S and P we could observe two maximum values at x=0.10 and x=0.425. It is considered that PSNT10(x=0.10) composition is the structural phase boundary to indicate the variable order-disorder[VOD] region. PSNT(x=0.425) composition is the morphotropic phase boundary[MPB] to indicate the rhombohedral to tetragonal phase transition. Higher S (0.437%) and P (0.3974$\mu$C/$\textrm{cm}^2$) values were attained by the La substitution (5 wt%) at Pb site in the MPB composition of 57.5PSN-42.5PT.

• 한국결정성장학회지
• /
• 제13권1호
• /
• pp.24-30
• /
• 2003

The preparation of $PbTiO_3$ powder was carried out using the oxide starting material by hydrothermal method. The powder of a crystalline phase with perovskite structure was synthesized. The optimum conditions for the preparation of powder were as follows; hydrothermal solvent; 8M-KOH or 8M-NaOH, reaction temperature; 250~$270^{\circ}C$, run time; 10 h. The ,shape of synthesized powders were well developed crystalline faces with specific surface area of about 2.3 $\textrm m^2$/g in KOH solution and about 5.0 $\textrm m^2$/g in NaOH solution. The cell parameters of powder were a = 3.90$\AA$, c = 4.14 $\AA$ and cell volume was 57.30 $\AA^3$. The cell ratio (c/a) of powder was the same as the theoretical ratio with c/a = 1.06 and the phase transition temperature(Tc) of the powders was about $470^{\circ}C$.

• 한국세라믹학회지
• /
• 제33권4호
• /
• pp.399-404
• /
• 1996

Hydrothemal synthesis of PbTiO3 has been investigated. A comprehensive thermodynamic model for heteroge-nous reacting solid-aquous system has been used to predict the optimum condition for the synthesis. Synthesis were performed using lead acetate trihydrate as Pb source crystalline TiO2 as Ti source and KOH as minerali-zer. The synthesis has been examined at low temperature (16$0^{\circ}C$) Phase pure perovskite PbTiO3 has been obtained at high pH(above 0.5 mol KOH). The morphology of PbTiO3 was acicular shape. It has been found sible for a distortion in the c direction. The water is gradully released on annealing the powder to 40$0^{\circ}C$ and the normal crystallographic properties are restored.

• 한국재료학회지
• /
• 제1권4호
• /
• pp.206-213
• /
• 1991

PbO 77-80wt%, ZnO 4.5-6wt%, $B_2O_3$ 7.5-8.5wt%, $TiO_2$ 3-7wt%, $P_2O_5$ 0.5-2wt%의 조성을 갖는 IC Package봉착용 저융점($400-460^{\circ}C$) 결정화유리 frit를 제조하였다. DTA-TMA, X-선 회절분석, SEM 등을 이용하여 봉착용 유리의 결정화 특성을 연구하였다. $TiO_2$ 함량이 3wt% 함유시료는 $420-440^{\circ}C$에서 $2PbO{\cdot}ZnO{\cdot}B_2O_3$의 결정이 균일성장하였다. $TiO_2$ 함량이 4wt% 첨가된 시료는 $420-440^{\circ}C$에서 $2PbO{\cdot}ZnO{\cdot}B_2O_3와\;PbTiO_3$ 결정이 섞여서 혼합결정을 이루고 있었다. 또한 $TiO_2$ 5wt% 첨가된 시료는 $440-460^{\circ}C$에서 perovskite $PbTiO_3$ 결정만 석출되었다.

• E2M - 전기 전자와 첨단 소재
• /
• 제9권10호
• /
• pp.991-1000
• /
• 1996

PbTiO$_{3}$-PbZrO$_{3}$-Pb(Ni$_{1}$3/Nb$_{2}$3/O$_{3}$) (PZT-PNN) thin films were prepared from corresponding metal organics partially stabilized with diethanolamine by the sol-gel spin coating method. Each mol ratio of PT:PZ:PNN solutions were #1(50:40:10), #2(50:30:20), #3(45:35:20), #4(40:40:20), #5(40:50:10), #6(35:45:20) and #7(30:50:20) respectively. The spin-coated PZT-PNN films were heat-treated at 350.deg. C for decomposition of residual organics, and were sintered from 450.deg. C to 750.deg. C for crystallization. The substrates, such as Pt and Pt/TiN/Ti/TiN/Si were used for the spin coating of PZT PNN films. The perovskite phase was observed in the PZT-PNN films heat-treated at 500.deg. C. The crystalline of the PZT-PNN films was optimized at the sintering of 700.deg. C. By the result of AES analysis, It is confirmed that the films of TiN/Ti/TiN was a good diffusion barrier and that co-diffusion into the each films was not observed.

• 한국재료학회지
• /
• 제4권5호
• /
• pp.541-549
• /
• 1994

공침법으로 제조된 비정질 $PbTiO_{3}$전구체의 결정화거동과 구조적 변화를 XRD, 라만스펙트럼, TEM, RDF등으로 조사하였다. 전구체는 이온안정제로 $H_2O_2$혹은 $NH_4NO_3$를 사용하여 제조된 질산납과 사염화티탄의 혼합수용액으로부터 $45^{\circ}C$, pH 9에서 제조되었다. 이온안정제로 $H_2O_2$를 사용한 경우보다 $NH_4NO_3$를 사용하여 제조된 공침물이 더 낮은 온도에서 결정화가 시작되며 결정화의 활성화에너지도 더 작은 값을 가진다. 비정질의 공침물은 transient phase를 거쳐 결정 $PbTiO_{3}$로 변태된다. 비정질 상태의 평균 원자거리는 열처리온도의 증가에 따라 감소한다.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1994년도 추계학술대회 논문집 학회본부
• /
• pp.196-198
• /
• 1994

The dielectric and electrical properties of $Pb(Mg_{1/3}Nb_{2\3})O_3-PbTiO_3-BaTiO_3$ have been investigated. Perovskite crystalline phase of the specimens are confirmed by XRD at $1270^{\circ}C$. The curie temperature is around $40^{\circ}C$ with the amount of $BaTiO_3$ and $PbTiO_3$. Every specimens shows the slim loop hysteresis curves which is electrostrictive characteristic. The strain vs. applied voltage characteristics exhibits nonlinear relationship, and the specimen of 0.85PMN-0.125PT-0.025BT shows the largest strain.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1994년도 하계학술대회 논문집 C
• /
• pp.1481-1483
• /
• 1994

The dielectric and electrical properties of $Pb(Mg_{1/3}Nb_{2/3})O_3-PbTiO_3-BaTiO_3$ have been investigated. Perovskite crystalline phase of the specimens is confimed by XRD. The curie temperature decrease with increasing $BaTiO_3$ and hysteresis phenomena decrease with increasement of $BaTiO_3$. The strain vs. applied voltage characteristics exhibit nonlinear relationship and the specimen. of 0.9PMN-0.08PT-0.02BT shows the largest strain.