• Journal of the Korean Electrochemical Society
• /
• v.27 no.1
• /
• pp.40-46
• /
• 2024

Among the electrode manufacturing processes for lithium-ion batteries, the drying process is crucial for production speed and process cost. Particularly, as the loading level of the electrode increases to enhance the energy density of the battery, optimizing process conditions for electrode drying becomes more critical. In this study, we compared the drying time and electrochemical performance of the positive electrode prepared at different drying temperatures. LiNi_0.6Co_0.2Mn_0.2O₂ (NCM622) was used as the active material and manufactured under various drying temperature conditions ranging from 120 ℃ to 210 ℃ at loading levels of 2.5 and 4.5 mAh cm^-2. The physical and electrochemical properties of the electrodes were compared. As the loading level of the electrode increases, the drying time of the electrode also increases, but this time can be reduced by increasing the drying temperature. The drying temperature used in manufacturing the NCM622 positive electrode does not significantly affect the electrochemical performance but drying above 210 ℃ resulted in an increase in the volume resistivity of the electrode and a decrease in electrochemical performance. Accordingly, in the manufacture of high-loading electrodes, the drying temperature was increased to 190 ℃ to shorten the electrode manufacturing time without a loss of performance.

• Korean Journal of Materials Research
• /
• v.32 no.4
• /
• pp.216-222
• /
• 2022

The capacity of high nickel Li(Ni_xCo_yMn_1-x-y)O₂ (NCM, x ≥ 0.8) cathodes is known to rapidly decline, a serious problem that needs to be solved in a timely manner. It was reported that cathode materials with the {010} plane exposed toward the outside, i.e., a radial structure, can provide facile Li⁺ diffusion paths and stress buffer during repeated cycles. In addition, cathodes with a core-shell composition gradient are of great interest. For example, a stable surface structure can be achieved using relatively low nickel content on the surface. In this study, precursors of the high-nickel NCM were synthesized by coprecipitation in ambient atmosphere. Then, a transition metal solution for coprecipitation was replaced with a low nickel content and the coprecipitation reaction proceeded for the desired time. The electrochemical analysis of the core-shell cathode showed a capacity retention of 94 % after 100 cycles, compared to the initial discharge capacity of 184.74 mA h/g. The rate capability test also confirmed that the core-shell cathode had enhanced kinetics during charging and discharging at 1 A/g.

• Resources Recycling
• /
• v.28 no.6
• /
• pp.79-86
• /
• 2019

Recently, the use of lithium ion battery(LIB) has increased. As a result, the price of lithium and the amount spent lithium on ion battery has increased. For this reason, research on recycling lithium in waste LIBs has been conducted1). In this study, the effect of roasting for the selective lithium leaching from the spent LIBs is studied. Chemical transformation is required for selective lithium leaching in NCM LiNi_xCo_yMn_zO₂) of the spent LIBs. The carbon in the waste EV cell powder reacts with the oxygen of the oxide at high temperature. After roasting at 550 ~ 850 ℃ in the Air/N₂ atmosphere, the chemical transformation is analysed by XRD. The heat treated powders are leached at a ratio of 1:10 in D.I water for ICP analysis. As a result of XRD analysis, Li₂CO₃ peak is observed at 700 ℃. After the heat treatment at 850 ℃, a peak of Li₂O was confirmed because Li₂CO₃ is decomposed into Li₂O and CO₂ over 723 ℃. The produced Li₂O reacted with Al at high temperature to form LiAlO₂, which does not leach in D.I water, leading to a decrease in lithium leaching ratio. As a result of lithium leaching in water after heat treatment, lithium leaching ratio was the highest after heat treatment at 700 ℃. After the solid-liquid separation, over 45 % of lithium leaching was confirmed by ICP analysis. After evaporation of the leached solution, peak of Li₂CO₃ was detected by XRD.

• Proceedings of the KIPE Conference
• /
• 2018.07a
• /
• pp.219-221
• /
• 2018

ESS용 NCM계 $LIB(Li[Ni_xCo_yMn_z]O_2)$의 양극 전이금속 설계인자 조성비(x:y:z)를 5:2:3, 6:2:2로 달리하여 제작한 전지를 사용하여 C-rate별 방전시험을 통한 기본성능평가를 진행하였고, 가속열화 시험을 통한 수명특성을 분석하였다. EIS(Electrochemical Impedance Spectroscopy) 실험을 통하여 전지의 임피던스를 확인하였고, 열화되지 않은(Fresh) 전지와 열화된(Aging) 전지의 SOC(State-of-Charge)별 임피던스 특성을 비교 분석하였다.

• Journal of the Korean Electrochemical Society
• /
• v.24 no.2
• /
• pp.28-33
• /
• 2021

Many researchers have increased the loading level of electrodes to improve the energy density of secondary batteries. In this study, high-loading NCM523 (LiNi_0.5Co_0.2Mn_0.3O₂) positive electrode is manufactured using a polytetrafluoroethylene (PTFE) binder, not the conventional polyvinylidene fluoride (PVdF) binder, which has been commonly used in lithium-ion batteries. Through the kneading process using PTFE suspension, not the conventional slurry process using PVdF solution in N-methyl-2-pyrrolidinone (NMP), thick electrodes with high loading are easily manufactured. When the PTFE and PVdF-based electrodes are prepared at a loading level of 5.0 mAh/cm², respectively, the PTFE-based electrode shows better cycle performance and rate capability than those of PVdF-based electrodes. The electrode manufactured by the kneading process using a PTFE binder has high electrode porosity due to insufficient roll-press, but the porosity can be lowered by high temperature roll-press over 120℃. However, there is no significant difference in cycle performance according to the roll press temperature. In addition, the cycle performance of the high loading electrode is slightly improved by increasing the content of the conductive material. Overall, the PTFE binder can improve the performance of the high loading electrode, but additional solutions will be needed.