• The Transactions of the Korean Institute of Electrical Engineers
• /
• v.44 no.11
• /
• pp.1488-1493
• /
• 1995

In this study, the structural, electrical and dielectric properties were investigated in (P $b_{0.76}$ $Ca_{0.24}$)[( $Co_{1}$2/ $W_{1}$2/)$_{0.04}$ $Ti_{0.96}$) $O_{3}$ system ceramics which were manufactured with the addition of Mn $O_{2}$. According to the increment of Mn $O_{2}$ addition, tetragonality was decreased. The specimen added with 1.5 mol% Mn $O_{2}$ and sintered at 1150.deg. C showed the highest density of 7.06[g/c $m^{3}$]. The variations of grain xize as a function of Mn $O_{2}$ addition were negligibly small. But grain was grown until 7.88[.mu.m] with increasing sintering temperature. Electromechamical coupling factor planar mode $K_{p}$ was decreased to a small value of $K_{p}$ = 0 in all the specimens added with Mn $O_{2}$ and sintered at 1150.deg. C & 1200.deg. C.& 1200.deg. C.

• Resources Recycling
• /
• v.7 no.4
• /
• pp.64-75
• /
• 1998

The purpose of this study is to produce high putity composite powder composed of Fe-oxide, Mn-oxide and Mn-ferrite having superior homogencity in composition and particle size distribution by co-roasting process. Binary component metal (Fe, Mn) chloride solutions were produced by dissolving mill scale and ferro-mangancse alloy in hydrochloric acid. These chloride solutions contained the impurities such as SiO$_{2}$, P, Al, Ca and Na, which were originated from the Fe/Mn source materials. The neutralization and polymeric coagulant method were adoped to refine the hydrochloric liquor. When pH is far below the isoelectric point (pH 2-3), the SiO$_{2}$ was the most effectively reduced element, while other impurities remained unchanged. By increasing pH above 3, most of the impurities could be reduced effectively due to the coprecipitation reaction. The polymeric coagulants such as poly vinyl alcohol, resin amine and ammonium molybdate were found to have no effect on the spray roaster designed by the authors. The produced oxide powders were confirmed to be mixtures of Fe-oxide, Mn-oxide and mn-ferrite. the powders were homogeneously mixed and the particle size increased sleeply with increasing co-roasting temperature.

• Journal of Technologic Dentistry
• /
• v.7 no.1
• /
• pp.41-51
• /
• 1985

This study has been to survey the present situation of satisfaction to the occupation and dental laboratory by means of selscting 200 dental technicians who are woked in Pusan, Deagu, Kwangju, Deajun. Questionaires were distributed to them and the summerized results were as follows; 1. In general, the dental technician's satisfaction of the occpation was revealed as moderate(Mn, 2.83), the dental technician's satisfaction of the laboratory was revealas moderate(Mn, 2.80). The highest degree item out of the satisfaction of occpation was the outlook(Mn, 3.23), and the lowest degree item was the advancement and the rise to a high position(Mn, 2.22). The highest degree item out of the satisfaction of laboratory was dental material(Mn, 3.07), and the lowest degree item was the equipment of dust collection(Mn, 2.49) 2. By age, the highest degree item out of the satisfaction of occpation was 30 to 43 group(Mn, 3.28), 50 and over group was the lowest degree item(Mn, 2.89). The highest degree item out of the satisfaction of laboratory was 40 to 50 group(Mn, 3.10), the lowest degree item was 35 to 39 group(Mn, 2.88). 3. By school career, the satisfaction of occpation and dental laboratory were higher in the graduated college group than the graduated highschool group. 4. By personal health state, the highest degree item of the satisfaction of occpation was the health group(Mn, 3.25). The highest degree item of the satisfaction of laboratory was the unhealthy group(Mn, 3.07). 5. By religion, the satisfaction if iccupation of laboratory ws higher in the religious group than the non-religious group. 6. By job career, the highest degree item of occupation satisfaction was 15 to 20 years group(Mn, 3.27), the lowest degree item was 20 and over group(Mn, 3.02). The highest degree item out of the satisfaction of laboratory was 15 to 20 years group(Mn, 3.05), The lowest degree item was 7 to 10 years group (Mn, 2.90). 7. By job position, the highest degree item out of satisfaction of occupation was the chief of laboratory group(Mn, 3.33), the head of laboratory group was the lowest degree item(Mn, 3.07). The hightest degree item out of the satisfaction of laboratory was the head of laboratory group(Mn, 3.10), the lowest degree item was the chief of laboratory group(Mn, 2.88). 8. By the place of employment, the degree of occpational satisfaction by items was found that the highest degree in the group engagel in general hospital(Mm, 3.43), the group engaged in dental clinic and hospital(Mn. 3.24), and the dental laboratory group(Mn. 3.14) in order. The difference among the group was significant emough(P<0.05). The highest degree item out of the satisfaction of laboratory was dental laboratory group(Mn. 2.70). The difference among the group was significant emough(P<0.01). 9. By monthly salary, the highest degree item out of the satisfaction of occupation was ￦500,000 to 600,000 group(Mn. 3.32), the lowest degree item was ￦600,000 and over group(Mn, 3.07). The highest degree item out of the laboratory satisfaction was ￦100,000 to 200,000 group(Mn, 3.03), the lowest degree group was ￦300,000 to 400,000 group(Mn, 2.95). 10. As compared with the degree of satisfaction according to job satisfaction, the highest degree item out of the occupational satisfaction was much satisfied group(Mn, 3.65), the lowest degree item was non-satisfied group(Mn, 2.68). The difference among the group was significant enough(P<0.05). The highest degree item out of the satisfaction of laboratory was non-satisfied group(Mn, 30.9), the lowest degree item was satisfied group(Mn, 2.84). The difference among the group was significant enough(P<0.01).

• Journal of the Korean Vacuum Society
• /
• v.15 no.5
• /
• pp.527-533
• /
• 2006

Spinel $LiNi_xMn_{2-x}O_4$ thin films were synthesized up to x = 0.9 by a sol-gel method employing spin-coating. The Ni-substituted films were found to maintain cubic structure at low x but to exhibit tetragonal structure for $x{\geq}0.6$. Such cubic-tetragonal phase transition indicates that $Ni^{3+}(d7)$ ions with low-spin $(t_{2g}^6,e_g^1)$ state occupy the octahedral sites of the compound, thus being subject to the Jahn-Teller distortion. By x-ray photoelectron spectroscopy both $Ni^{2+}$ and $Ni^{3+}$ ions were detected. Optical properties of the $LiNi_xMn_{2-x}O_4$ films were investigated by spectroscopic ellipsometry (SE) in the visible?ultraviolet range. The measured dielectric function spectra by SE mainly consist of broad absorption structures attributed to charge-transfer (CT) transitions, $O^{2-}(2p){\rightarrow}Mn^{4+}(3d)$ for 1.9 $(t_{2g})$ and $2.8{\sim}3.0$ eV $(e_g)$ structures and $O^{2-}(2p){\rightarrow}Mn^{3+}(3d)$ for 2.3 $(t_{2g})$ and $3.4{\sim}3.6$ eV $(e_g)$ structures. Also, sharp absorption structures were observed at about 1.6, 1.7, and 1.9 eV, interpreted as due to d-d crystal-field transitions within the octahedral $Mn^{3+}$ ion. The strengths of these absorption structures are reduced by the Ni substitution. Rapid reduction of the CT transition strength involving the eg states for x = 0.6 is attributed to the reduced wavefunction overlap between the $e_g$ and the $O^{2-}(2p)$ states due to the tetragonal extension of the lattice constant by the Jahn-Teller effect.

• Corrosion Science and Technology
• /
• v.16 no.1
• /
• pp.15-22
• /
• 2017

An oxidation-reduction scheme is an alternative approach for improving the galvanizability of advanced high-strength steel in the continuous hot-dip galvanizing process. Here, we investigated the effect of oxygen partial pressure ($P_{O_2}$) on the oxidation behavior of a transformation-induced plasticity steel containing 1.5 wt% Si and 1.6 wt% Mn during heating to and holding for 60 s at $700^{\circ}C$ under atmospheres with various $P_{O_2}$ values. Irrespective of $P_{O_2}$, a thin amorphous Si-rich layer of Si-Mn-O was formed underneath the Fe oxide scale (a $Fe_2O_3/Fe_3O_4$ bilayer) in the heating stage. In contrast to Si, Mn tended to segregate at the scale surface as $(Fe,Mn)_2O_3$. The multilayered structure of $(Fe,Mn)_2O_3/Fe_2O_3/Fe_3O_4$/amorphous Si-Mn-O remained even after extended oxidizing at $700^{\circ}C$ for 60 s. $Fe_2O_3$ was the dominantly growing oxide phase in the scale. The enhanced growth rate of $Fe_2O_3$ with increasing $P_{O_2}$ resulted in the formation of more Kirkendall voids in the amorphous Si-rich layer and a less Mn segregation at the scale surface. The mechanisms underlying the absence of FeO and the formation of Kirkendall voids are discussed.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.10
• /
• pp.1056-1060
• /
• 2004

In this study, 0.96B $i_{0.5}$($Na_{0.84}$ $K_{0.16}$)$_{0.5}$Ti $O_3$ + 0.04SrTi $O_3$ + 0.3 wt% N $b_2$ $O_{5}$+0.2 wt% L $a_2$ $O_3$ + xwt % Mn $O_2$ were investigated as a function of the amount of Mn $O_2$ addition in order to improve dielectric and piezoelectric properties of Lead-free piezoelectric ceramics. With increasing the amount of Mn $O_2$ addition, the density, electromechanical coupling factor( $k_{p}$), piezoelectric constant( $d_{33}$, $g_{33}$) and curie temperature (Tc) showed the maximum value of 5.7 g/㎤, 38 %, 219 pC/N, 26 mVㆍm/N and 32$0^{\circ}C$ at 0.1 wt% Mn $O_2$ addition, respectively, and mechanical quality factor( $Q_{m}$ ) showed the maximum value of 158 at 0.3 wt% Mn $O_2$ addition.ddition.ion.n.

• Journal of Mushroom
• /
• v.11 no.2
• /
• pp.87-91
• /
• 2013

When No. 42 strain of Pleurotus ostreatus was cultivated at five different media, MnP and Lac but no LiP activity was detected throughout the culture period in the media. The production of MnP and Lac by No. 42 strain of Pleurotus ostreatus were correlated with wheat bran composition in the medium. In the liquid culture, maximum production of MnP and Lac were observed in the medium contained glucose-peptone- yeast-wheat bran(GPYW). However, in solid medium, maximum production of MnP was observed in wood meal-wheat bran(WMW) medium, but that of Lac was observed in wheat bran(W) medium.

• Transactions on Electrical and Electronic Materials
• /
• v.6 no.5
• /
• pp.202-209
• /
• 2005

Phase evolution, microstructure and the electrical properties such as $k_p$ and $Q_m$ of $Pb(Mg_{1/3}Nb_{2/3})O_3[PMN]-Pb(Mn_{1/3}Nb_{2/3})O3[PM'N]-PbZrO_3[PZ]-PbTiO_3[PT]$ quaternary system were investigated within the compositional ranges $0{\leq}y{\leq}0.125$, y+z=0.125, and $0.39{\leq}x{\leq}0.54$ of the formula $Pb_{0.97}Sr_{0.03}[Mg_{1/3}Nb_{2/3})_y\;(Mn_{1/3}Nb_{2/3})_z\;(Zr_{x}Ti_{1-x})_{1-(y+z)}]O_3$. In the case of increasing Mn/(Mg+Mn) ratio for a fixed Zr/Ti ratio of 47.5/52.5, phase relation remained unchanged but the grain size drastically decreased, and the electrical properties changed as following: both $k_P$ and $Q_m$ reached the peak values at $Mn/(Mg+Mn)\cong0.3l7$ and gradually decreased; $\varepsilon33^T$ showed a monotonic decrease; P-E hysteresis loop gradually changed to asymmetrical one, and $E_i$ increased in correspondence. With increasing Zr/Ti ratio for a fixed Mn/(Mg+Mn) ratio of 0.317, on the contrary, the cell parameter $(\alpha^2c)^{1/3}$ gradually increased, and tetragonal-rhombohedral morphotropic phase boundary appeared in the range of $51/49{\leq}Zr/Ti{\leq}54/46$. the meantime, the grain size substantially increased, and the electrical properties changed as following: $k_P$ and $\varepsilon33^T$ reached peak values at Zr/Ti=51/49 and 48/52, respectively, and then gradually decreased; change of $Q_m$ was adverse to $k_P$; both $E_C\;and\;E_i$ considerably decreased while $P_S$ moderately increased. For the system 0.125(PMN+PM'N)-0.875PZT studied, the composition Mn/(Mg+Mn)=0.3l7 and Zr/Ti=51/49 revealed some promising electrical properties for piezoelectric transformer application such as $k_P=0.58,\;Q_m\cong1000$, and $\varepsilon^T_{33}=970$, as well as dense and fine-grained microstructure.

• Journal of Sensor Science and Technology
• /
• v.13 no.2
• /
• pp.152-156
• /
• 2004

The dielectric and piezoelectric properties of 0.36Pb($Sc_{1/2}Nb_{1/2}$)$O_{3}$-0.25Pb($Ni_{1/3}Nb_{2/3}$)$O_{3}$-0.39Pb$TiO_{3}$ (hereafter PSNNT) at the morphotropic phase boundary (MPB) composition were investigated with $0{\sim}2.5$ mot% $MnO_{2}$ doping. Bulk density, dielectric loss and tetragonality of crystal structure were all improved with increasing $MnO_{2}$ additive content. With increasing $MnO_{2}$ additive content, the electromechanical coupling factor and quality factor were also increased: Electromechanical coupling $k_{p}$ and quality factor $Q_{m}$ at 2.0 mol% $MnO_{2}$ doping with were showed highest values of 55.6 % and 252, respectively.

• The Korean Journal of Ceramics
• /
• v.6 no.4
• /
• pp.348-353
• /
• 2000

The effects of MnO$_2$ and Fe$_2$O$_3$ on the piezoelectric properties of 0.05PMN-0.451PT-0.499PZ ceramics were investigated. The addition of MnO$_2$ increased mechanical quality factor (Q$_m$) but decreased the dielectric constant (K$^{T}_{33}$) and compliance (S$^{E}_{11}$) of the specimens. These results indicated that MnO$_2$ behaves as an acceptor in 0.05MN-0.451PT-0.499PZ ceramics. The electromecanical coupling coefficient (K$_P$) of 0.05PMN-0.451PT-0.499PZ ceramics slightly increased with the addition of MnO$_2$ however, the enhancement of $K_P$ was insignificant. A small amount of Fe$_2$O$_3$ was added to enhance the $K_P$ of the 0.05PMN-0.451PT-0.499PZ + 0.5 wt% MnO$_2$ ceramics. The addition of Fe$_2$O$_3$ largely increased $K_P$ through the increase of the K$^{T}_{33}$ and the polarization. The mechanical quality factor of the specimens decreased with the addition of Fe$_2$O$_3$however, the reduction was negligible.