• Journal of Electrochemical Science and Technology
• /
• v.15 no.1
• /
• pp.168-177
• /
• 2024

Ni-rich cathode is one of the promising candidates for high-energy lithium-ion battery applications. Due to its specific capacity, easy industrialization, and good circulation ability, Ni-rich cathode materials have been widely used for lithium-ion batteries. However, due to the limitation of the co-precipitation method, including sewage pollution, and the instability of the long production cycles, developing a new efficient and environmentally friendly synthetic approach is critical. In this study, the Ni_0.91Co_0.06Mn_0.03CO₃ precursor powder was successfully synthesized by an efficient spray-drying method using carbonate compounds as a raw material. This Ni_0.91Co_0.06Mn_0.03CO₃ precursor was calcined by mixing with LiOH·H₂O (5 wt% excess) at 480℃ for 5 hours and then sintered at two different temperatures (780℃/800℃) for 15 hours under an oxygen atmosphere to complete the cathode active material preparation, which is a key component of lithium-ion batteries. As a result, LiNi_0.91Co_0.06Mn_0.03O₂ cathode active material powders were obtained successfully via a simple sintering process on the Ni_0.91Co_0.06Mn_0.03CO₃ precursor powder. Furthermore, the obtained LiNi_0.91Co_0.06Mn_0.03O₂ cathode active material powders were characterized. Overall, the material sintered at 780℃ shows superior electrochemical performance by delivering a discharge capacity of 190.76 mAh/g at 1^st cycle (0.1 C) and excellent capacity retention of 66.80% even after 50 cycles.