LiBaPO₄:Eu²⁺ phosphors with stoichiometric and nonstoichiometric compositions were prepared using a solid state reaction followed by heat treatment in reduced atmosphere, and the crystal structures and photoluminescence(PL) properties of the powders were investigated by x-ray powder diffraction and luminescence spectrometer. At 900℃, the Ba₃(PO₄)₂ phase as the intermediate phase was observed with the LiBaPO₄ phase as the main crystalline phase. Samples with a low europium concentration at 1,000℃ belonged to the trigonal structure, whereas samples with Eu²⁺ content more than 4 mol% showed monoclinic structure. In the nonstoichiometric compositions of 4 mol% Eu²⁺ and above, a single phase of Eu²⁺-doped LiBaPO₄, showing bluish green emission, was formed.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.10 no.6
• /
• pp.400-406
• /
• 2000

The fired Precursor (Y,Gd,Eu)(OH)$CO_3$.$H_2O$$900^{\circ}C$ was used to synthesize the red phosphor $(Y,Gd)_2O_3$: Eu for plasma display panel. Rounded and ~l $\mu\textrm{m}$ diameter phosphor $(Y,Gd)_2O_3$: Eu can be obtained by the reaction of aformentioned powder with a small amount addition of flux at $1350^{\circ}C$ for 2 hours. Emission spectra of these phosphors were measured under excitation wavelength at 254 nm and 147 nm and the optimum concentrations of activator ion were determined at around 15 mo1e % and 10 mole % under these conditions, respectively. $BaCO_3$flux had the best property in emission intensity among the prepared $BaCO_3AlF_3$and $Li_3PO_4$phosphors. The properties of optimized sample were improved in terms of relative luminance and color coordinate comparing with commercial phosphor such as $Y_2O_3$: Eu.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2007.11a
• /
• pp.91.1-91.1
• /
• 2007