• The Korean Journal of Applied Statistics
• /
• v.17 no.3
• /
• pp.499-505
• /
• 2004

The Pareto diagram analysis of the experimental data by the two level orthogonal arrays has been used widely in practice since it is a graphical, quick and easy method to analyze experimental results, which does not use the analysis of variance to screen significant effects. For the analysis of the experimental data by $L_{18}(2 \times 3^7)$ orthogonal array, Park(1996) proposed Pareto ANOVA in which the size of effects is defined by the mean squares of effects and the Pareto principle is used. In this paper, a new approach of the Pareto diagram analysis of the experimental data by $L_{18}(2 \times 3^7)$ orthogonal array is proposed. The main idea is to partition the size of three level effects by that of linear and quadratic orthogonal contrasts of those effects.

• Korean Journal of Materials Research
• /
• v.3 no.5
• /
• pp.514-520
• /
• 1993

In this paper the cure cycle of carbon fiber/phenolic resin was investigated by the Taguchi Method in an experimental design. Experiments were systematically performed using $L_{18}(2^1 \times 3_7)$ orthorgonal array table of the experimental design. In the experimental design, eight compression molding parameters (heating rate, pressing temperature, pressing rate, molding pressure, curing temperature, dwell time at curing temperature, cooling rate and degassing) were considered and the effects of the parameters on the flexural strength and the apparent porosity of carbon fiber/phenolic composites were investigated. The analysis of variance for the experimental results indicated that molding pressure and curing temperature are the most significant parmeters in the flexural strength and the apparent porosity of carbon fiber/phenolic resin composites, respectively.

• Journal of the Korean Ceramic Society
• /
• v.39 no.10
• /
• pp.1001-1006
• /
• 2002

Bond strength of $SrZrO_3$ resistive oxide barrier on Ag sheathed Bi(2223) tapes prepared by the sol-gel and dip-coating method was evaluated with an aid of Taguchi method and $L_18(2^1{\times}3^7)$ orthogonal arrays to determine the optimal process combination of levels of factors that best satisfy the bigger is better quality characteristic. The observed optimal condition is as follows: Sr/Zr mol ratio(0.3/0.7), amount of organic vehicle(5 wt%), drying temperature and time(160${\circ}C$, 10 min), heat treatment temperature and time(500${\circ}C$, 20 min), respectively. ANOVA analysis suggested that the influence of the factors within ${\alpha}$=0.1 was significant with a 90% confidence level.

• Journal of the Korean Ceramic Society
• /
• v.39 no.6
• /
• pp.582-588
• /
• 2002

IrO$_2$-RuO$_2$ films were deposited on plasma sprayed TiO$_2$ buffer layer above Ti metal by sol-gel and dip-coating method. Organic vehicle (ethyl cellulose and $\alpha$-terpineol) and glass frit were added to improve adherence of the coatings. Taguchi method and L$_{18}$ (2$^1$$\times$3$^{7}$ ) orthogonal arrays were evalvated in terms of current density to determine the optimal combination of levels of factors that best satisfy the bigger is better quality characteristic. The observed conditions were as fellows: ethyl cellulose (100 cp), drying temperature and time (17$0^{\circ}C$,20 min), heat treatment temperature and time (75$0^{\circ}C$,10 min), the weight ratio of IrO$_2$-RuO/powders to glass frit (99:5), final heat treatment time (120 min) and flow rate of air (5 sccm), respectively. ANOVA analysis suggested that the influence of the factors within $\alpha$= 0.1 was significant with a 90% confidence level.