• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.7 no.5
• /
• pp.801-804
• /
• 2006

[ $GdAlO_3(GAO)$ ] buffer layer for $YBa_2Cu_3O_{7-{\delta}}(YBCO)$ coated superconductor wire was fabricated by sol-gel processing. Precursor solution was prepared by dissolving 1:1 stoichiometric quantaties of gadolinium nitrate hexahydrate and aluminum nitrate nonahydrate in methanol. The solution was spin-coated on $SrTiO_3(STO)$(100) single crystal substrates and heated at $1000^{\circ}C$ for 2h in wet $N_2-5%\; H_2$, atmosphere. A SEM(scanning electron microscopy) observation of the surface morphology of the GAO layer has shown that it has a faceted morphology indicating epitaxy. It was shown from x-ray diffraction(XRB) that GAO buffer layer was highly c-axis oriented epitaxial thin film with both good out-of-plane($FWHM=0.29^{\circ}$ for the (002) reflection) and in-plane ($FWHM=1.10^{\circ}$ for the {112} reflection) alignment.

• Journal of the Korean Ceramic Society
• /
• v.43 no.6 s.289
• /
• pp.369-375
• /
• 2006

[ $(Ba_{0.5}Sr_{0.5})_{0.99}Co_{x}Fe_{1-x}O_{3-{\delta}}$ ] [x=0.8, 0.2](BSCF) powders were synthesized by a Glycine-Nitrate Process (GNP) and the electrochemical performance of the BSCF cathode on a scandia stabilized zirconia, $[(Sc_{2}O_3)_{0.11}(ZrO_2)_{0.89}]-1Al_{2}O_3$ was investigated. In order to prevent unfavorable solid-state reactions between the cathode and zirconia electrolyte, a GDC ($Gd_{0.1}Ce_{0.9}O_{2-{delta}}$) buffer layer was applied on ScSZ. The BSCF (x = 0.8) cathode formed on GDC(Buffer)/ScSZ(Disk) showed poor electrochemical property, because the BSCF cathode layer peeled off after the heat-treatment. On the other hand, there were no delamination or peel off between the BSCF and GDC buffer layer, and the BSCF (x = 0.2) cathode exhibited fairly good electrochemical performances. It was considered that the observed phenomenon was associated with the thermal expansion mismatch between the cathode and buffer layer. The ohmic resistance of the double layer cathode was slightly lower than that of the single layer BSCF cathode due to the incorporation of platinum particle into the BSCF second layer.