• 한국세라믹학회지
• /
• 제31권6호
• /
• pp.629-636
• /
• 1994

The ferrimagnetic glass-ceramics in the system Fe2O3-CaO-SiO2 for hyperthermia were investigated. Glasses could be prepared up to the content of 40 wt% of Fe2O3 and below the weight ratio of 1.0 of CaO/SiO2. The maximum saturation magnetization and the maximum coercive force were 29.85 emu/g and 340.1 Oe respectively, for a glass 40Fe2O3.20CaO.40SiO2 composition heat-treated at 95$0^{\circ}C$ for 8 hours. And for a glass 40Fe2O3.30CaO.30SiO2 composition the maximum saturation magnetization and the maximum coercive force were 18.47 emu/g and 374.4 Oe heat-treated at 1,00$0^{\circ}C$ and 90$0^{\circ}C$ for 8 hours respectively. The maximum hysteresis loss was 1,726.3 cal/g for a glass 40Fe2O3.20CaO.40SiO2 composition heat-treated at 95$0^{\circ}C$ for 8 hours. It was found that the ferrimagnetic Fe2O3.CaO.SiO2 glass-ceramics was little injurious to human body as results of biocompatibility test and biotoxicity test.

• 한국표면공학회지
• /
• 제36권5호
• /
• pp.406-412
• /
• 2003

FT-IR and thermography were used to investigate the infrared radiation characteristic of SiO$_2$ film and SiO$_2$/Fe$_2$O$_3$film coated on aluminum. Through FT-TR spectrum, SiO$_2$film showed high infrared absorption in accordance with the stretching vibration of Si-O-Si, and as$ Fe_2$$O_3$was mixed additional absorption band appeared resulting from the stretching vibration of Fe-O at $590cm^{-1}$ and the bond of Si-O-Fe at $900 cm^{-1}$ The two kinds of film measured by the integration method and the reflective method coincided with each other in the wavelength area of infrared absorption and radiation, and corresponded well with Kirchhoff's law as the infrared emissivity is high in wavelength where infrared absorption rate is high. The emissivity of $SiO_2$ film was 0.65 and that of $SiO_2$/Fe$_2$$O_3$film was 0.77, so the addition of$ Fe_2$$O_3$ raised the infrared emissivity by approximately 13%.$ SiO_2$$Fe_2$$O_3$ film is efficient as an infrared radiator at below $100^{\circ}C$. The temperature of heat radiation after 7 minutes was 117$^{\circ}C$ in aluminum plate and $155^{\circ}C$ in $SiO_2$$Fe_2$$O_3$ film, $38^{\circ}C$ higher than the former.

• 산업기술연구
• /
• 제36권
• /
• pp.77-81
• /
• 2016

Superparamagnetic $Fe_3O_4$ nanoparticles with particle size from 10 to 20 nm were synthesized by coprecipitation method. Subsequently, the $Fe_3O_4$ nanoparticles were used to fabricate $Fe_3O_4/SiO_2$ core-shell nanoparticles by sol-gel method. The $Fe_3O_4/SiO_2$ nanoparticles synthesized by sol-gel method exhibit the high uniformities of particle size and shape. We also investigated the heating characteristics of $Fe_3O_4$ and $Fe_3O_4/SiO_2$ nanoparticles for biomedical applications. The $Fe_3O_4$ nanoparticles show the faster temperature increase and the higher specific loss power(SLP) value than the $Fe_3O_4/SiO_2$ nanoparticles.

• 한국자기학회지
• /
• 제5권4호
• /
• pp.281-286
• /
• 1995

Hexaferrite $Ba_{0.25}Sr_{0.75}Fe_{12}O_{19}$에 $SiO_{2}$를 첨가한 쉬트자석의 자기적 성질의 변화를 연구하기 위해 X-선 회절 실험, 뫼스바우어 분광실험, 자기모멘트 측정실험 등을 하였다. 쉬트자석은 Dr. Blade 방법에 의해 제조되었고, 결정구조는 마그네토플럼바이트 M-type 육방결정구조이다. 첨가제 농도에 따른 격자상수의 변화는 거의 없으나, $SiO_{2}$가 2.0 wt.% 이상부터 ${\alpha}-Fe_{2}O_{3}$ 의 상이 나타나기 시작했다. 이성질체 이동값은 Fe이온들이 3가 임을 나타낸다. $SiO_{2}$의 증가에 따라 Curie 온도는 감소함을 보였다. 이것은 $Si^{4+}$가 12k-site $Fe^{3+}$의 자리를 차지함으로써 Fe-O-Fe의 초교환상호작용에 의한 원자간 거리와 양이온 사이의 각이 변함에 따른 것이다. ${\alpha}-Fe_{2}O_{3}$의 상은 $Si^{4+}$가 12k-site $Fe^{3+}$의 자리를 차지함으로 치환된 $Fe^{3+}$에 의해 나타난 것이다. 자기모멘트측정으로 부터 $SiO_{2}$를 첨가한 $Ba_{0.25}Sr_{0.75}Fe_{12}O_{19}$ 쉬트자석은 보자력 $H_{c}$, 포화자화 $M_{s}$, 잔류자화 $M_{r}$이 양이온 치환보다는 미세구조변화에 더 의존함을 알았다.

• Bulletin of the Korean Chemical Society
• /
• 제33권8호
• /
• pp.2567-2573
• /
• 2012

We successfully synthesized $Fe_3O_4@SiO_2$ nanoparticles with ultrathin silica layer of $1.0{\pm}0.5$ nm that polyethyleneimine (PEI) with low molecular weight of 2.0-4.0 kDa was covalently conjugated with the resulting $Fe_3O_4@SiO_2$ nanoparticles by silane coupling reaction. The PEI-$Fe_3O_4@SiO_2$ nanoparticles were further used as gene delivery vector for a human fibroblast cell (IMR-90) line. Gene transfection efficiency of the PEI-$Fe_3O_4@SiO_2$ complexes did not increase remarkably after magnetofection; however, the addition of Lipofectamine 2000 significantly increased the transfection efficiency of the PEI-$Fe_3O_4@SiO_2$ complexes. We believe that the present approach could be utilized for magnetofection as alternative to $Fe_3O_4$ nanoparticles conjugated with the PEI of high molecular weight thanks to its relatively low cytotoxicity and high transfection efficiency.

• 공업화학
• /
• 제8권2호
• /
• pp.179-190
• /
• 1997

준역청탄, 유연탄, 무연탄 및 국내 무연탄을 포함하는 54종의 석탄회분을 대상으로 화학조성 및 광물분석 그리고 용융온도를 측정하여 화학조성이 용융온도에 미치는 영향을 고찰하였다. 석탄회의 구성 산화물중 CaO와 MgO, 그리고 $Fe_2O_3$가 용융온도를 낮추는 산화물임을 알 수 있었다. $Fe_2O_3$에 의한 용융온도 감소 효과는 환원성분위기에서 증가되었다. 산-염기도에서 염기성분의 함량이 증가할수록 용융온도는 감소하였다. 그러나 산-염기도와 용융온도와의 상관관계는 $Fe_2O_3$/CaO비가 증가함에 따라 낮아졌다. 산화성분위기보다는 환원성분위기에서 용융온도가 낮았으며 이때 분위기 변화에 따른 용융온도차는 $Fe_2O_3$의 함량보다는 $SiO_2/Al_2O_3$비와 밀접한 상관성을 보여주었다. 석탄회의 용융온도(연화)를 예측하기 위한 다중회귀분석결과 산화성분위기에서는 Base/Acid, $Fe_2O_3$/CaO, $SiO_2/Al_2O_3$, $(SiO_2/Al_2O_3){\cdot}(Base/Acid)$ 그리고 환원성분위기에서는 Base/Acid, $Fe_2O_3$/CaO, $SiO_2$, $TiO_2$등을 독립변수로 사용함으로써 비교적 상관성이 높은 관계식을 얻을 수 있었다.

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2001년도 추계연구발표회 논문개요집
• /
• pp.48-49
• /
• 2001

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2012년도 춘계학술발표회 논문집
• /
• pp.170-171
• /
• 2012

$Fe_2O_3$, Al, Cr과 Si 분말을 고 에너지 볼 밀링해서 나노분말을 제조한 후 고주파유도 가열 활성 연소합성 장치로 1분 이내의 짧은 시간에 합성 및 소결한 $Al_2O_3+4.65(Fe_{0.43}Cr_{0.17}Al_{0.323}Si_{0.077})$, $Al_2O_3$ + 5.33 ($Fe_{0.375}Cr_{0.11}Al_{0.3}Si_{0.075}$), $Al_2O_3$ + 6.15 ($Fe_{0.325}Cr_{0.155}Al_{0.448}Si_{0.072}$), $Al_2O_3$ + 3.3 ($Fe_{0.6}Cr_{0.3}Al_{0.6}$) 소결체 시편을 $700^{\circ}C$의 온도에서 100시간 동안 공기 중에서 산화 및 $N_2-H_20-H_2S$ 혼합 가스 내에서 황화 부식을 실시하였다. 그 결과 산화 및 황화 부식 후에 ${\alpha}-Al_2O_3$가 표면에 생성되어 보호 피막으로 작용하여 우수한 내식성을 보였다.

• Corrosion Science and Technology
• /
• 제16권1호
• /
• pp.15-22
• /
• 2017

An oxidation-reduction scheme is an alternative approach for improving the galvanizability of advanced high-strength steel in the continuous hot-dip galvanizing process. Here, we investigated the effect of oxygen partial pressure ($P_{O_2}$) on the oxidation behavior of a transformation-induced plasticity steel containing 1.5 wt% Si and 1.6 wt% Mn during heating to and holding for 60 s at $700^{\circ}C$ under atmospheres with various $P_{O_2}$ values. Irrespective of $P_{O_2}$, a thin amorphous Si-rich layer of Si-Mn-O was formed underneath the Fe oxide scale (a $Fe_2O_3/Fe_3O_4$ bilayer) in the heating stage. In contrast to Si, Mn tended to segregate at the scale surface as $(Fe,Mn)_2O_3$. The multilayered structure of $(Fe,Mn)_2O_3/Fe_2O_3/Fe_3O_4$/amorphous Si-Mn-O remained even after extended oxidizing at $700^{\circ}C$ for 60 s. $Fe_2O_3$ was the dominantly growing oxide phase in the scale. The enhanced growth rate of $Fe_2O_3$ with increasing $P_{O_2}$ resulted in the formation of more Kirkendall voids in the amorphous Si-rich layer and a less Mn segregation at the scale surface. The mechanisms underlying the absence of FeO and the formation of Kirkendall voids are discussed.

• 대한화학회지
• /
• 제54권5호
• /
• pp.579-581
• /
• 2010

Solid silica supported ferric chloride ($SiO_2-FeCl_3$) 촉매를 이용하여 다양한 benzimidazoles의 one-step 합성을 수행하였으며, 합성 방법이 간단하며, 화합물의 분리가 용이하며, 반응시간이 짧다.