• Journal of Magnetics
• /
• 제11권1호
• /
• pp.36-42
• /
• 2006

In this report, we demonstrate a comprehensive analysis of the effects of Au addition on the microstructure and magnetic properties of $Fe_{73.5}Si_{13.5}B_{9}Nb_{3}Au_1$ Finemet-type alloy. It was found that the as-quenched alloys were the amorphous state and turned into nanocrystalline state under heat treatments. The DSC analysis indicates that the sharply exothermal peak corresponding to the crystallization of the $\alpha-Fe(Si)$ was observed at $547-579^{\circ}C$ depending on the heating rates, which is little higher than that of original Finemet (542-$570{^{\circ}C}$, respectively). Besides, the thermomagnetic result confirmed that the full substitution of Cu by Au with the single phase structure in the M(T) curve along cooling cycle. Ultrasoft magnetic properties of the nanocrystallized samples were significantly enhanced by the proper annealing such as the increase of permeability and the decrease of the coercivity. The optimum annealing condition was found at the annealing temperature of $540^{\circ}C$ and the increase of the annealing time up to 90 min.

• 한국자기학회지
• /
• 제25권3호
• /
• pp.67-73
• /
• 2015

본 연구는 철기(Fe based) $Fe_{73.5}Si_{13.5}B_9Nb_3Cu_1$ 나노결정 합금의 분말코어(powder core)의 연자기적 특성 향상을 위한 기초연구로서, 절연 코팅제의 첨가량 및 분말입도에 따른 투자율, 코어손실 및 DC 바이어스 특성을 주로 조사하였다. 우선 합금조성을 PFC 장치를 이용하여 비정질 합금리본을 제조한 후, 열처리, 미분쇄 및 분급하여 얻어진 합금분말에 절연 코팅제(PEI)의 첨가량을 0.5, 1.0, 2.0, 2.5 wt%로 변화시켜 $16ton/cm^2$으로 압축성형 및 결정화 열처리하여 제조한 토로이달 나노결정 분말코어($OD12.7mm{\times}ID7.62mm{\times}H4.75mm$)는 절연 코팅제 함량이 증가할수록 투자율은 감소하였지만, 코어손실 및 DC 바이어스 특성은 향상됨을 확인하였다. 이러한 이유는 합금분말 절연 코팅제 첨가량이 증가할수록 비정질 합금분말 입자가 적어져 분말코어의 성형밀도가 낮아지기 때문으로 추정되었으며, 절연 코팅제의 함량은 1 wt%가 가장 적합한 것으로 판단되었다. 또한 절연 코팅제 함량을 1 wt%로 고정하고, 합금분말의 입도에 따라 제조한 분말코어의 경우, 실효투자율 및 코어손실은 입도가 클수록 우수하였지만, DC 바이어스 특성은 인가자장이 증가함에 따라 더욱 나빠짐을 확인하였다. 그 이유는 합금분말 표면의 코팅층 두께 차이에 의한 절연효과, 잔류기공 혹은 분말코어의 성형밀도 차이 등에 기인하는 것으로 추정되었다.